Related papers: Titanium additions to MgB2 conductors
A series of MgB2 thin films were fabricated by pulsed laser deposition (PLD), doped with various amounts of Si up to a level of 18wt%. Si was introduced into the PLD MgB2 films by sequential ablation of a stoichiometric MgB2 target and a Si…
Two sets of MgB2 samples doped with up to 5 at. % of Al were prepared in different laboratories using different procedures. Decreases in the a and c lattice parameters were observed with Al doping confirming Al substitution onto the Mg…
A relatively high critical temperature, Tc, approaching 40 K, places the recently-discovered superconductor magnesium diboride (MgB2) intermediate between the families of low- and copper-oxide-based high-temperature superconductors (HTS).…
Fe-sheathed MgB2 tapes were prepared through the in situ powder-in-tube technique by 5 at.% ZrSi2, ZrB2 and WSi2 doping, respectively. The doping effect of these compounds on the microstructure and superconducting properties of MgB2 tapes…
Transport measurements of critical current density, Jct, in monocore powder-in-tube MgB2 strands have been carried out at temperatures, T, of from 4.2 K to 40 K, and in transverse fields, B, of up to 14 T. Processing methods used were…
Here we report a systematic study of superconductive properties of mono-filamentary MgB2-based wires, manufactured with different filling technique. A detailed comparison of the influence of filling technique and final heat treatment on…
Fe-sheathed MgB2 tapes with cheap stearic acid, Mg stearate and Zn stearate doping were prepared through the in situ powder-in-tube method. It is found that Jc, Hirr, and Hc2 were significantly enhanced by doping. Compared to the pure…
We present details of synthesis optimization and physical properties of nearly single phase carbon doped MgB2 with a nominal stoichiometry of Mg(B{0.8}C{0.2})2 synthesized from magnesium and boron carbide (B4C) as starting materials. The…
We report on the superconducting performance of the ex-situ SiC doped MgB2 monofilamentary tapes. Polycrystalline powders of MgB2 doped with 5 and 10 wt% SiC were synthesized by conventional solid-state reaction route and characterized for…
We present electrical transport, magnetization, and specific heat measurements on bulk MgB2 samples (T_{c} = 38.5 K) synthesized under 200 MPa pressure using a process based on hot isostatic pressing with cooling under pressure. The samples…
The use of MgB2 in superconducting applications still awaits for the development of a MgB2-based material where both current-carrying performance and critical magnetic field are optimized simultaneously. We achieved this by doping MgB2 with…
Bulk superconducting samples of MgB2 were prepared by solid state reaction of stoichiometric quantities of Mg turnings and B in a sealed Ta cylinder at 890 C for 2 hours. The as-synthesized MgB2 samples had a Tc of 39 K, as defined as the…
In high-quality c-axis-oriented MgB2 thin films, we observed high critical current densities (Jc) of 16 MA/cm^2 at 15 K under self fields comparable to those of cuprate high-temperature superconductors. The extrapolated value of Jc at 5 K…
Superconducting MgB2 thin films were fabricated on Al2O3(0001) substrates under an ex-situ processing conditions. Boron thin films were deposited by pulsed laser deposition followed by a post-annealing process. Resistance measurements of…
We have studied structural and superconducting properties of MgB2 thin films doped with carbon during the hybrid physical-chemical vapor deposition process. A carbon-containing metalorganic precursor bis(cyclopentadienyl)magnesium was added…
Bulk samples of MgB2 were prepared with 5, 10, and 15% wt.% Y2O3 nanoparticles added using a simple solid-state reaction route. Transmission electron microscopy (TEM) showed a fine nanostructure consisting of ~3-5 nm YB4 nanoparticles…
Transport current values of 7.5 x 104 A/cm2 at 4.2 K and self-field are reported for MbB2-based tapes. MgB2 strands were formed by directly filling commercially available MgB2 powder into Nb-lined, monel tubes and wire drawing. The wires…
Superconducting MgB(2) films with Tc = 38.6 K were prepared using a precursor-deposition, ex-situ post-processing approach. Precursor films of boron, ~0.5 micrometer thick, were deposited onto Al(2)O(3) (102) substrates by e-beam…
The effect of the quality of starting powders on the microstructure and superconducting properties of in-situ processed Fe-sheathed MgB2 tapes has been investigated. Three different types of commercial atomized spherical magnesium powder…
The paper reports the first successful fabrication of MgB2 superconducting tape using a flexible metallic substrate as well as its strong pinning force, which was verified by direct measurement of transport critical current density. The…