Related papers: Comparative Study of Dense Bulk MgB$_2$ Materials …
High-density bulk materials of a newly discovered 40K intermetallic MgB2 superconductor were prepared by high pressure sintering. Superconducting transition with the onset temperature of 39K was confirmed by both magnetic and resistive…
Bulk textured MgB_2 material of nearly full density showing a weak c-axis alignment of the hexagonal MgB_2 grains parallel to the pressure direction was obtained by hot deformation of a stoichiometric MgB_2 pellet prepared by a gas-solid…
The MgB2 bulks were prepared by high energy milling of Mg and B powder. The correlations among milling times, microstructure and superconducting properties were investigated in MgB2 bulks. Samples were characterized by x-ray diffraction…
We present electrical transport, magnetization, and specific heat measurements on bulk MgB2 samples (T_{c} = 38.5 K) synthesized under 200 MPa pressure using a process based on hot isostatic pressing with cooling under pressure. The samples…
High energy milling of MgB2 pre-reacted powder renders the material largely amorphous through extreme mechanical deformation and is suitable for mechanically alloying MgB2 with dopants including carbon. Bulk samples of milled C and MgB2…
Superconducting properties of bulk, dense, pure MgB2 and doped (Mg1-xAx)B2 samples with A = Na, Ca, Cu, Ag, Zn and Al were studied for compositional ranges 0 < x < 0.20. The effect on pinning properties and critical current were…
Highly dense nanocrystalline MgB_2 bulk superconductors with distinctly improved pinning were prepared by mechanical alloying of Mg and B powders and hot compaction at ambient temperatures. The nanocrystalline samples reveal high critical…
Two different hot isostatic pressing cycles (HIPing) were investigated to synthesize bulk MgB2 samples: a "standard" cycle where a low vessel pressure is maintained while heating to the process temperature with a subsequent simultaneous…
Dense pure and doped (Mg1-xAx)B2 samples with A = Na, Ca, Cu, Ag, Zn and Al were synthesized at high pressure - high temperature in a multi anvils press (3.5-6 GPa, 900-1000C) for x up to 0.20. They were studied by x-ray diffraction,…
High-pressure (HP) synthesis and sintering are promising methods for manufacturing of the bulk MgB2 superconductive material. The available high-pressure apparatuses with 100 cm3 working volume can allow us to use the bulk MgB2 for…
We succeeded in the synthesis of high-Jc MgB2 bulks via high energy ball-milling of elemental Mg and B powder at ambient temperatures. Alternatively to longtime mechanical alloying technique, the mixed powder was ball-milled for only 1h and…
Bulk samples of MgB2 have been formed by hot isostatic pressing (HIPping) of commercial powder at 100MPa and 950=B0C. The resulting material is 100% dense with a sharp superconducting transition at 37.5K. Microstructural studies have…
Powdered and sintered MgB2 samples have been characterized through magnetic measurements performed from T = 5 K up to few degrees above the transition temperature of about 39 K. We found that the sintered samples behave as well-connected…
We report a significant enhancement of the upper critical field $H_{c2}$ of different $MgB_2$ samples alloyed with nonmagnetic impurities. By studying films and bulk polycrystals with different resistivities $\rho$, we show a clear trend of…
We have successfully prepared the MgB2 superconducting bulk and powdered materials by the method of combustion synthesis. The starting materials used in this study were powders of Mg and B. X-ray powder diffraction pattern was well assigned…
The high-pressure synthesis is one of the most promising methods to produce MgB2 superconductive (SC) material. The available high-pressure apparatuses have working volume up to 100 cm3 which allows samples up to 60 mm in diameter to be…
Hot Isostatic Pressing was applied to synthesize bulk samples with diameter up to 30 mm starting with Alfa Aesar magnesium diboride powder. HIPing at 2 kbar, 1000 C with cooling under pressure (DMCUP cycle) resulted in a fully dense (or low…
Highly dense MgB2 policrystalline bulk materials, obtained by reactive liquid infiltration, have been characterized in their superconducting transport and magnetic properties in magnetic field and in a temperature range of interest for the…
The synthesis of MgB2-based materials under high pressure gave the possibility to suppress the evaporation of magnesium and to obtain near theoretically dense nanograined structures with high superconducting, thermal conducting, and…
Bulk MgB2 samples were prepared under different synthesis conditions and analyzed by scanning and transmission electron microscopy. The critical current densities were determined from the magnetization versus magnetic field curves of bulk…