Thickness uniformity is regarded as an important parameter in designing thin film devices. However, some applications based on films with non-uniform thickness have recently emerged, such as gas sensors and optimized materials based on the…
By doing magnetization measurements during magnetic field sweeps on thin films of the new superconductor $MgB_2$, it is found that in a low temperature and low field region small flux jumps are taking place. This effect strongly suppresses…
We suggest a new theoretical approach describing the velocity of magnetic flux dendrite penetration into thin superconducting films. The key assumptions for this approach are based upon experimental observations. We treat a dendrite tip…
We report the influence of intrinsic superconducting parameters on the vortex dynamics and the critical current densities of a MgB$_2$ thin film. The small magnetic penetration depth of \lambda = 50 nm at T=4 K is related to a clean…
We present numerical and analytical studies of coupled nonlinear Maxwell and thermal diffusion equations which describe nonisothermal dendritic flux penetration in superconducting films. We show that spontaneous branching of propagating…
The critical current density of four MgB2 samples was measured inductively and for one of them also by transport. Pure phased and dense bulk samples yield a critical current density which in value, as well as in its magnetic field and…
Oxygen was systematically incorporated in MBE grown MgB2 films using in-situ post-growth anneals in an oxygen environment. Connectivity analysis in combination with measurements of the critical temperature and resistivity indicate that…
Magneto-optical imaging was used to observe dendritic flux avalanches connecting the outer and inner edges of a ring-shaped superconducting MgB2 film. Such avalanches create heated channels across the entire width of the ring, and inject…
We propose a mechanism responsible for the abrupt vanishing of the dendritic flux instability found in many superconducting films when an increasing magnetic field is applied. The onset of flux avalanches and the subsequent reentrance of…
We have successfully synthesized MgB2 thick films on 4H-SiC substrate by hybrid physical-chemical deposition (HPCVD). The films have transition temperature TC above 40 K. X-ray diffraction (XRD) shows the c-axis oriented structure of MgB2,…
The critical current density flowing across low angle grain boundaries in YBa$_2$Cu$_3$O$_{7-\delta}$ thin films has been studied magnetometrically. Films (200 nm thickness) were deposited on SrTiO$_3$ bicrystal substrates containing a…
Local magnetization measurements on 100 nm type-II superconducting Pb thin films show that flux penetration changes qualitatively with temperature. Small flux jumps at the lowest temperatures gradually increase in size, then disappear near…
In high-quality c-axis-oriented MgB2 thin films, we observed high critical current densities (Jc) of 16 MA/cm^2 at 15 K under self fields comparable to those of cuprate high-temperature superconductors. The extrapolated value of Jc at 5 K…
The complex conductivity of a MgB2 film has been investigated in the frequency range 4 cm^{-1}< nu < 30 cm^{-1} and for temperatures 2.7 K < T <300 K. The overall temperature dependence of both components of the complex conductivity is…
The thermal stability of MgB2 has been studied experimentally to determine the role of thermodynamic and kinetic barriers in the decomposition process. The MgB2 decomposition rate approaches one monolayer per second at 650 C and has an…
Critical fields of four MgB2 thin films with a normal state resistivity ranging from 5 to 50 mWcm and Tc from 29.5 to 38.8 K were measured up to 28 T. Hc2(T) curves present a linear behavior towards low temperatures. Very high critical…
We report the growth of high-quality epitaxial MgB2 thin films on (1102) Al2O3 and (001) SrTiO3 substrates by using a pulsed laser deposition technique. The thin films grown on Al2O3 substrates show a Tc of 39 K with a sharp transition…
We report on the observation of dendritic flux avalanches in a large Niobium single crystal. In contrast to avalanches observed in thin films, they appear only in a very narrow temperature interval of about a tenth of a Kelvin near the…
We have investigated the thermodynamic and kinetic barriers involved in the synthesis of MgB2 films. This work refines our initial conjectures predicting optimal MgB2 thin film growth conditions as a consequence of the unusually large…
Very thick, ~ 40 $\mu$m, clean, and highly textured MgB2 film was effectively grown on an Al2O3 substrate. The fabrication technique is by the hybrid physical-chemical vapor deposition (HPCVD) using B2H6 gas and Mg ingot as the sources. The…