Related papers: Absence of Superconductivity in BeB2
Here, we report that K-doped BaMn2Bi2 shows no experimental evidence of superconductivity down to 1.5 K under pressures up to 35.6 GPa, however, a tetragonal to an orthorhombic phase transition is observed at pressure of 20 GPa. Theoretical…
2H-NbSe2 is the prototype and most frequently studied of the well-known transition metal dichalcogenide (TMDC) superconductors. Widely acknowledged to be a conventional superconductor, its transition temperature to the superconducting state…
We report phase formation, and detailed study of magnetization and resistivity under magnetic field of MgB2 polycrystalline bulk samples prepared by Fe-tube encapsulated and vacuum (10-5 torr) annealed (750 0C) route. Zero-field-cooled…
Superconducting Ag or Cu sheathed MgB2 wires have been fabricated by conventional powder-in-tube techniques. The in-situ reaction of Mg and B powders with atomic proportions of 1:2 and 1.33:2 inside Ag or Cu tubes at low temperatures have…
The microstructure of the MgB2 superconductor sintered at high temperature under a high pressure of about 3 GPa was investigated by using a high-resolution transmission electron microscope (HRTEM). The TEM images did not show any pores in…
Effects of magnetic impurity on the superconductivity has been investigated in Mg1-xMnB2. With increase of Mn concentration x, the lattice constant c (perpendicular to the boron sheet) decreases at a rate of -1.4 % (= dlnc/dx), while a…
We report superconductivity in single crystals of the new iron-pnictide system BaFe1.9Pt0.1As2 grown by a self-flux solution method and characterized via x-ray, transport, magnetic and thermodynamic measurements. The magnetic ordering…
We present electronic structure calculations together with resistivity, susceptibility, and specific heat measurements for TaB$_2$ to search for the recently contradictorily reported superconductivity and to study related normal state…
We report measurements of the transport and the magnetic properties of high-quality, sub-millimeter-sized MgB2 single crystals with clear hexagonal-plate shapes. The low-field magnetization and the magnetic hysteresis curves show the vortex…
Single crystals of MgB2 have been grown at high pressure via the peritectic decomposition of MgNB9. The crystals are of a size up to 1.5x0.9x0.2 mm3 with a weight up to 0.23 mg, and typically have transition temperatures between 37 and 39…
Electrolysis was carried out on fused mixtures of MgCl2, NaCl, KCl and MgB2O4 under an Ar flow at 600C. Electrical resistivity measurements for the grown deposits show an onset of superconducting transition at 37 K in the absence of applied…
Carbon-substituted MgB2 single crystals, Mg(B_1-xC_x)_2 of 0.3-1.0 mm size were grown for x=0.02-0.15 by a high-pressure technique. The doping dependence of lattice constants studied in a range of x=0.0-0.2 shows a monotonic decrease in a,…
We present electrical transport, magnetization, and specific heat measurements on bulk MgB2 samples (T_{c} = 38.5 K) synthesized under 200 MPa pressure using a process based on hot isostatic pressing with cooling under pressure. The samples…
Inspired by recent predictions of superconductivity in B-C framework clathrates, we employ density functional theory to explore potential superconductors among hexagonal hydride-substituted compounds with compositions XB$_8$C, XB$_7$C$_2$,…
$MgB_2$ becomes superconducting just below 40 K. Whereas porous polycrystalline samples of $MgB_2$ can be synthesized from boron powders, in this letter we demonstrate that dense wires of $MgB_2$ can be prepared by exposing boron filaments…
In the present work, we report the synthesis of Pb-Bi alloy with enhanced Tc of up to 9K, which is higher than that of Pb. The alloy is synthesized via a solid-state reaction route in the vacuum-encapsulated quartz tube at 7000C in an…
We report on the synthesis and on basic superconducting properties of a completely new Mo_2Re_3B ternary boride. The crystal structure of the Mo_2Re_3B compound is characterised by Pmmm space group and the cell parameters: a=11.626 A,…
The dependence of Tc on nearly hydrostatic pressure has been measured for an isotopically pure (11B) MgB2 sample in a helium-loaded diamond-anvil-cell to nearly 20 GPa. Tc decreases monotonically with pressure from 39.1 K at ambient…
OsB_2 crystallizes in an orthorhombic structure (Pmmn) which contains alternate boron and osmium layers stacked along the c-axis. The boron layers consist of puckered hexagons as opposed to the flat graphite-like boron layers in MgB_2.…
Point-contact spectroscopy measurements on magnesium diboride reveal the existence of two superconducting energy gaps closing at the same transition temperature in line with the multiband model of superconductivity. The sizes of the two…