We report the lithium plating associated capacity loss during fast charging of compressively loaded lithium-ion batteries (LIBs). The charging and discharging of LIB under compressive loading during service may affect the cell performance…
In this work, we adopt first-principle calculations based on density functional theory and Kinetic Monte Carlo simulations to investigate the adsorption and diffusion of lithium in bilayer graphene (BLG) as anodes in lithium-ion batteries.…
Fracture of lithium-ion battery electrodes is found to contribute to capacity fade and reduce the lifespan of a battery. Traditional fracture models for batteries are restricted to consideration of a single, idealised particle; here,…
Some rate of oxidation and reduction side-reactions will inevitably coexist in most rechargeable batteries, contributing to reversible and irreversible self-discharge. While parasitic reduction traps electrons, parasitic oxidation donates…
Next-generation high-energy-density batteries require ideally stable metal anodes, for which smooth metal deposits during battery recharging are considered a sign of interfacial stability that can ensure high efficiency and long cycle life.…
This work presents a comprehensive study on the aging behavior of 18650-type lithium-ion batteries, focusing on the uneven intercalation of lithium ions during fast charging processes. It introduces a novel approach using color visual…
A combination of Scanning Tunneling Microscopy/Spectroscopy and Density Functional Theory (DFT+U) is used to characterize excess electrons in TiO$_2$ rutile and anatase, two prototypical materials with identical chemical composition but…
The solvation environments of Li$^+$ in conventional non-aqueous battery electrolytes, such as LiPF$_6$ in mixtures of ethylene carbaronate (EC) and ethyl methyl carbonate (EMC), are often used to rationalize the transport properties of…
The improvement of Li-ion battery performance requires development of models that capture the essential physics and chemistry in Li-ion battery electrode materials. In this paper a novel electrochemical phase-field model is presented that…
We have studied lithiation of graphene oxide (GO) as a function of oxygen coverage using first principles calculations. Our results show that the lithiation potentials and capacities in GO can be tuned by controlling the oxygen coverage, or…
Based on ab initio calculations, we examine the incorporation of Li atoms in the MoS2/graphene interface. We find that the intercalated Li atoms are energetically more stable than Li atoms adsorbed on the MoS2 surface. The intercalated…
Lithium metal batteries (LMB) are vital devices for high-energy-density energy storage, but Li metal anode is highly reactive with electrolyte and forms uncontrolled dendrite that can cause undesirable parasitic reactions thus poor cycling…
Black phosphorous is a layered material having a high capacity of 2596 mAh/g as a battery electrode, however it suffers from cracking due to high volume expansion during lithiation. These cracks causes loss of electrical contact in the…
Li ion diffusion is fundamentally a thermally activated ion hopping process. Recently, soft lattice, anharmonic phonon and paddlewheel mechanism have been proposed to potentially benefit the ion transport, while the understanding of…
The participation of oxygen or other anionic species in redox activities in cathode materials for lithium and sodium-ion battery systems is known to play a role in governing the useful capacity of these batteries. Directly probing anionic…
We present a comparative ab initio computational study of sodium and lithium storage in amorphous (glassy) carbon (a-C) vs. graphite. Amorphous structures are obtained by fitting stochastically generated structures to a reference radial…
Developing sustainable battery electrode manufacturing methods is particularly pressing for alloying-type active materials, such as silicon, which often require additional energy-intensive and solvent-based processing to reinforce them with…
Sodium-ion batteries (SIBs) are cost-effective alternatives to lithium-ion batteries (LIBs), but their low energy density remains a challenge. Current electrode designs fail to simultaneously achieve high areal loading, high active content,…
Solid electrolyte interphase (SEI), a thin layer that dynamically forms between active electrode and electrolyte during battery operation, critically governs the performance of rechargeable batteries1-5. An ideal SEI is expected to be…
Ceramic solid-state batteries with sodium (Na) metal electrodes promise enhanced safety and energy density compared to contemporary secondary batteries. However, the critical delamination of the Na metal electrode during discharge - when…