Related papers: Reactive magnetron sputtering of tungsten target i…
Ga2O3 thin films were deposited by reactive magnetron sputtering from a liquid gallium target. The influence of deposition temperature, substrate type, and discharge parameters on the structural and electrical properties was systematically…
5$\mu$m thick NdFeB films have been sputtered onto 100 mm Si substrates using high rate sputtering (18 $\mu$m/h). Films were deposited at ≤ 500 C and then annealed at 750 C for 10 minutes. While films deposited at temperatures up to…
Al-doped ZnO thin films were deposited using reactive high power impulse magnetron sputtering at substrate temperatures between room temperature and 600 $\bullet$ C. Two sample series with different oxygen partial pressures were studied.…
We investigate sputtering of a Ti3SiC2 compound target at temperatures ranging from RT (no applied external heating) to 970 oC as well as the influence of the sputtering power at 850 oC for the deposition of Ti3SiC2 films on Al2O3(0001)…
We report on magnetron deposition of thin superconducting rhenium films on sapphire substrates. During the deposition, substrates were held at ambient temperature. Critical temperature of the films is Tc~3.6 K. Films have polycrystalline…
Here, we report the full-fledged journey towards the material synthesis and characterization of few-layered/thin WSe$_2$ using sputtered W-films on SiO$_2$/Si substrates followed by electrical studies under dark and illumination conditions.…
5$\mu$m thick SmCo films were deposited onto Si substrates using triode sputtering. A study of the influence of deposition temperature (Tdep <= 600 degrees C) on the structural, magnetic and mechanical properties has shown that optimum…
Thin films of the recently discovered magnesium diboride (MgB2) intermetalic superconducting compound have been grown using a magnetron sputtering deposition technique followed by in-situ annealing at 830 C. High quality films were obtained…
The superconducting critical temperature (Tc > 15K) of niobium titanium nitride (NbTiN) thin films allows for low-loss circuits up to 1.1 THz, enabling on-chip spectroscopy and multi-pixel imaging with advanced detectors. The drive for…
50nm thick nanogranular polycrystalline dysprosium thin films have been prepared via ultra-high vacuum DC sputtering on SiO2 and Si wafers. The maximum in-plane spontaneous magnetization at T = 4K was found to be MS4K = 3.28T for samples…
In this work, amorphous thin films in Mg-Si-O-N system were prepared in order to investigate the dependence of optical and mechanical properties on Mg composition. Reactive RF magnetron co-sputtering from magnesium and silicon targets were…
Thin films of Co2MnSi have been grown on a-plane sapphire substrates from three elemental targets by dc magnetron co-sputtering. These films are single phase, have a strong (110) texture and a saturation magnetization of 4.95 uB/formula…
Al2O3 thin films have been deposited at substrate temperatures between 500{\deg}C to 600{\deg}C by reactive magnetron sputtering using an additional arbitrary substrate bias to tailor the energy distribution of the incident ions. The films…
Aluminosilicate (Al-Si-O) thin films containing up to 31 at. % Al and 23 at. % Si were prepared by reactive RF magnetron co-sputtering. Mechanical and structural properties were measured by indentation and specular reflectance infrared…
Epitaxially grown full Heusler alloy of Rh2MnSb thin films were prepared for the first time using DC magnetron sputtering. The films were deposited on MgO [001] substrates with a deposition temperature of 600{\deg}C, 700{\deg}C, and…
We report on the structural and superconducting properties of nanocrystalline tungsten thin films growth by sputtering at room temperature with an N2:Ar mixture (N2 from 3% to 50%). The crystalline phases were identified by comparing…
We report the reduction in residual stress of AlN thin films and also the crystal structure, surface morphology and nanomechanical properties of magnetron sputtered as a function of substrate temperature (Ts, 35 - 600 ?C). The residual…
This paper presents progress towards the large-scale manufacturability of piezo- and ferroelectric Al$_{1-x}$Sc$_x$N thin films with very high Sc content. Al$_{0.6}$Sc$_{0.4}$N layers were deposited by reactive sputtering from a 300 mm…
Superconducting properties of three series of amorphous WxSi1-x films with different thickness and stoichiometry were investigated by dc transport measurements in a magnetic field up to 9 T. These amorphous WxSi1-x films were deposited by…
This paper reports on the deposition of amorphous and crystalline thin films of Ga2O3 by reactive pulsed direct current magnetron sputtering from a liquid gallium target onto fused (f-) quartz and c plane (c-) sapphire substrates, where the…