Related papers: The Effect of Temperature on Cu-K-In-Se Thin Films
The Cu-deficient CuxInSe2 (x larger than 0.3) phase can be stabilized as a thin film. A uniform Cu-deficient composition with a chalcopyrite structure was obtained by the precision engineering of a two-step synthesis process involving…
In this paper, we report the high temperature mediated structural phase transformation from B1 to B2 phase in solgel derived Cd0.2Zn0.8O nanocomposite thin film for the temperature range of 700 to 900 degree centigrade. Xray diffraction…
V$_3$Si thin films are known to be superconducting with transition temperatures up to 15 K, depending on the annealing temperature and the properties of the substrate underneath. Here we investigate the film structural properties with the…
Copper-doped zinc sulphide (ZnS:Cu) thin films were synthesized through pulsed laser ablation in an inert background gas on stationary and rotating substrates, and a comprehensive opto-electrical characterisation is presented. The…
We report the effect of annealing on the superconductivity of MgB2 thin films as functions of the postannealing temperature in the range from 700 C to 950 C and of the postannealing time in the range from 30 min to 120 min. On annealing at…
Low-temperature scanning tunneling spectroscopy reveals that the Kondo temperature T_K of Co atoms adsorbed on Cu/Co/Cu(100) multilayers varies between 60 K and 134 K as the Cu film thickness decreases from 20 to 5 atomic layers. The…
A Mn valence instability on La2/3Ca1/3MnO3 thin films, grown on LaAlO3 (001)substrates is observed by x-ray absorption spectroscopy at the Mn L-edge and O K-edge. As-grown samples, in situ annealed at 800 C in oxygen, exhibit a Curie…
Thin films of superconducting V$_3$Si were prepared by means of RF sputtering from a compound V$_3$Si target at room temperature onto sapphire and oxide-coated silicon wafers, followed by rapid thermal processing under secondary vacuum. The…
Highly textured chalcogenide films have recently gained significant interest for phase-change memory applications. Several reports have highlighted that programming efficiency improves in devices featuring superlattice stacks, such as…
Tin Selenide (SnSe) thin films were grown onto glass and alumina substrates by Chemical Vapor Deposition (CVD) method. The structural, micro-structural and morphological characterizations of the as grown thin films were investigated using…
We report on the chemical stability of La2/3Ca1/3MnO3 thin films. X-ray absorption spectroscopy at the Mn L-edge and O K-edge makes evident deviations from the nominally expected (2/3-1/3) Mn3+/Mn4+ ratio after the growth of thin films on…
Cuprous oxide (Cu2O) films from 25 nm to 1500 nm were electrodeposited on n-Si(100) and Ni/n-Si(100) substrates from aqueous solution at room temperature. X-ray diffraction and transmission electron microscopy imaging show that the Cu2O…
Chromium thin films deposited on silicon substrates by DC magnetron sputtering were systematically investigated as a function of film thickness, using a DC power of 50 W and a post-deposition annealing temperature of 200 C. Two types of…
We report on an enhancement of the Curie temperature in GaMnAs/InGaMnAs superlattices grown by low-temperature molecular beam epitaxy, which is due to thin InGaMnAs or InGaAs films embedded into the GaMnAs layers. The pronounced increase of…
We investigate sputtering of a Ti3SiC2 compound target at temperatures ranging from RT (no applied external heating) to 970 oC as well as the influence of the sputtering power at 850 oC for the deposition of Ti3SiC2 films on Al2O3(0001)…
Thin films of TiN were sputter-deposited onto Si and sapphire wafers with and without SiN buffer layers. The films were fabricated into RF coplanar waveguide resonators, and internal quality factor measurements were taken at millikelvin…
Sol-gel spin coating technique was employed to synthesize CuO thin films at 1500 rpm, 2200 rpm and 2400 rpm for 30 seconds, and subsequently annealed at 150-550{\deg}C for 1 hour. Multi-layered CuO thin films with 3 and 5 layers were…
Copper oxide thin films are deposited on quartz substrates by DC magnetron sputtering and the effect of deposition temperature on their optoelectronic properties is examined in detail. Scanning Electron Microscopy (SEM), X-ray diffraction…
High quality vanadium sesquioxide V2O3 films (170-1100 {\AA}) were grown using the pulsed laser deposition technique on (0001)-oriented sapphire substrates, and the effects of film thickness on the lattice strain and electronic properties…
CdS samples were synthesized on amorphous glass and conductive glass substrates at room temperature using spin coating technique and subsequently annealed at five different temperatures in air for one hour. The speed and time of spin…