The magnetic properties of Fe$_3$O$_4$ nanoparticle assemblies have been investigated in detail through a combination of vibrating sample magnetometry and muon spin relaxation ($\mu$SR) techniques. Two samples with average particle sizes of…
Magnetic nanoparticles of La0.67Sr0.33MnO3 (LSMO) manganite with mean particle sizes of 13, 16, 18 and 21 nm were prepared by the sol-gel method. The crystal structure and mean particle size of the synthesized powders were estimated by…
We have studied the magnetic behavior of dextran-coated magnetite (Fe$_3$O$_4$) nanoparticles with median particle size $\left<d\right>=8$ $nm$. Magnetization curves and in-field M\"ossbauer spectroscopy measurements showed that the…
In this paper we investigate the superspin glass behavior of a concentrated assembly of interacting maghemite nanoparticles and compare it to that of canonical atomic spin glass systems. ac versus temperature and frequency measurements show…
The structural and magnetic properties of ZnFe2O4 nanoparticles embedded in a non-magnetic ZnO matrix are presented. X-ray diffractograms and Transmission Electron Microscopy (TEM) images showed that the resulting samples are composed of…
Earlier investigation of Co_{0.2}Zn_{0.8}Fe_{1.95}Ho_{0.05}O_{4} spinel has shown the existence of "super-ferromagnetic " clusters containing Fe^{3+} and Ho^{3+} ions along with small size clusters of Fe^{3+} ions (Bhowmik et al, J. Magn.…
We report the particle size dependent magnetic behaviour in the antiferromagnetic spinel CoRh2O4. The nanoparticles were obtained by mechanical milling of bulk material, prepared under sintering method. The XRD spectra show that the samples…
We present X-ray diffraction (XRD), M\"ossbauer spectroscopy (MS) and d.c. magnetization measurements performed on ball-milled CuFe2O4 samples. The average particle size <d> was found to decrease to the nanometer range after t=15 min of…
We present the low temperature magnetic properties in Ni1.5Fe1.5O4 ferrite as the function of pH at which the material was prepared by chemical route and post annealing temperature. The material is a ferri or ferromagnet, but showed…
This paper presents the results of simulations of the magnetization field {\it ac} response (at $2$ to $12$ GHz) of various submicron ferrite particles (cylindrical dots). The ferrites in the present simulations have the spinel structure,…
Spherical magnetite nanoparticles having average particle size <d> = 5 nm have been synthesized by coprecipitation of Fe(II) and Fe(III) salts in KOH with Polyvinylalcohol (PVA). The resulting dry powder displayed superparamgnetic (SPM)…
In this report, the magnetic behaviour of $NiCr_{2}O_{4}$ bulk and nanoparticle samples under different applied magnetic field has been investigated extensively. Nanoparticles of $NiCr_{2}O_{4}$ were obtained by mechanical milling of…
Single-phase Mg-doped ZnFe$_2$O$_4$ nanoparticles with x= 0, 0.3, 0.5, 0.7 have been prepared by the glycol-thermal method without any subsequent calcination. The crystallite size, microstructure and magnetic properties of the prepared…
We present a detailed study of the magnetic behavior of iron-oxide (gamma-Fe2O3 and Fe3O4) nanoparticles constituents of ferrofluids (FF's) with average particle sizes <d> = 2.5 and 10 nm. The particles were dispersed in the frozen liquid…
Pure ultrafine ZnFe2O4 particles have been obtained from mechanosynthesis of the ZnO and Fe2O3 oxides. The average grain diameter was estimated from x-ray diffraction to be <d> = 36(6) nm. Refinement of neutron diffraction (ND) data showed…
We report the synthesis, structure, and magnetic and transport properties of a new ternary intermetallic compound PrRhSn3 which crystallizes in LaRuSn3-type cubic structure (space group Pm-3n). At low applied fields the dc magnetic…
Controlled assembly of single-crystal, colloidal maghemite nanoparticles is facilitated via a high-temperature polyol-based pathway. Structural characterization shows that size-tunable nanoclusters of 50 and 86 nm diameters (D), with high…
Spin wave resonances with enormously large wave numbers corresponding to wave vectors 10^5-10^6 cm^{-1} are observed in thin plates of FeBO3. The study of spin wave resonances allows one to obtain information about the spin wave spectrum.…
Ni3C nanoparticles of about 40 nm have been studied experimentally to exhibit weak ferromagnetic (FM), spin-glass (SG) and paramagnetic (PM) properties. The freezing temperature of the SG phase at zero applied field is determined as, TF0 ~…
Detailed dc and ac magnetic properties of chemically synthesized Nd0.4Sr0.6MnO3 with different particle size (down to 27 nm) have been studied in details. We have found ferromagnetic state in the nanoparticles, whereas, the bulk…