The copper ferrite thin films have been deposited by RF sputtering at a 50W rf power. The As-deposited films are annealed in air at $800^{\circ}$C and then slow cooled. The As-deposited (AD) as well as slow cooled (SC) films are studied…
Copper ferrite thin films were rf sputtered at a power of 50W. The as deposited films were annealed in air at 800{\deg}C and slow cooled. The transmission electron microscope (TEM) studies were carried out on as deposited as well as on slow…
We report on the magnetic properties of zinc ferrite thin film deposited on SrTiO$_3$ single crystal using pulsed laser deposition. X-ray diffraction result indicates the highly oriented single phase growth of the film along with the…
5$\mu$m thick NdFeB films have been sputtered onto 100 mm Si substrates using high rate sputtering (18 $\mu$m/h). Films were deposited at ≤ 500 C and then annealed at 750 C for 10 minutes. While films deposited at temperatures up to…
Al-doped ZnO thin films were deposited using reactive high power impulse magnetron sputtering at substrate temperatures between room temperature and 600 $\bullet$ C. Two sample series with different oxygen partial pressures were studied.…
The magnetization of thin films of cobalt ferrite frequently falls far below the bulk value of 455 kAm-1, which corresponds to an inverse cation distribution in the spinel structure with a significant orbital moment of about 0.6 muB that is…
The rf sputtered copper ferrite films contain nanocrystalline grains. In these films, the magnetization does not saturate even in high magnetic fields. This phenomenon of high field susceptibility is attributed to the defects and/or…
Ta (100 nm) / NdFeB (5 $\mu$m) / Ta (100 nm) films have been deposited onto Si substrates using triode sputtering (deposition rate ~ 18 $\mu$m/h). A 2-step procedure was used : deposition at temperatures up to 400 C followed by ex-situ…
5$\mu$m thick SmCo films were deposited onto Si substrates using triode sputtering. A study of the influence of deposition temperature (Tdep <= 600 degrees C) on the structural, magnetic and mechanical properties has shown that optimum…
Chromium thin films deposited on silicon substrates by DC magnetron sputtering were systematically investigated as a function of film thickness, using a DC power of 50 W and a post-deposition annealing temperature of 200 C. Two types of…
Homogeneous freestanding films have been obtained by the direct current (DC) magnetron sputtering technique using a sacrificial layer. After annealing, the films are crystallized with a strong out-of-plane texture along the (022) direction.…
Thin films of the charge-ordered (CO) compound Pr$_{0.5}$Ca$_{0.5}$MnO$_{3}$ have been deposited onto (100)-oriented SrTiO$_{3}$ substrates using the Pulsed Laser Deposition technique. Magnetization and transport properties are measured…
We report the deposition of thin Co$_2$FeSi films by RF magnetron sputtering. Epitaxial (100)-oriented and L2$_1$ ordered growth is observed for films grown on MgO(100) substrates. (110)-oriented films on Al$_2$O$_3$(110) show several…
The effect of vacuum annealing thin films of the compensated ferrimagnetic half-metal Mn2RuxGa at temperatures from 250 to 400 degree Celsius is investigated. The 39.3 nm films deposited on (100) MgO substrates exhibit perpendicular…
Wurtzite GaN:Mn films on sapphire substrates were successfully grown by use of the molecular beam epitaxy (MBE) system. The film has an extremely high Curie temperature of around 940 K, although the Mn concentration is only about 3 ~ 5 %.…
In this work, we studied cobalt nitride (Co-N) thin films deposited using a dc magnetron sputtering method at a substrate temperature (\Ts) of 523\,K. We find that independent of the reactive gas flow (\pn) used during sputtering, the…
50nm thick nanogranular polycrystalline dysprosium thin films have been prepared via ultra-high vacuum DC sputtering on SiO2 and Si wafers. The maximum in-plane spontaneous magnetization at T = 4K was found to be MS4K = 3.28T for samples…
We investigated structural, magnetic and electrical properties of sputter deposited Mn-Fe-Ga compounds. The crystallinity of the Mn-Fe-Ga thin films was confirmed using x-ray diffraction. X-ray reflection and atomic force microscopy…
Thin films of Co2MnSi have been grown on a-plane sapphire substrates from three elemental targets by dc magnetron co-sputtering. These films are single phase, have a strong (110) texture and a saturation magnetization of 4.95 uB/formula…
The magnetization (M) as a function of temperature (T) from 2 to 300 K and in-plane field (H) up to 1 kOe, room temperature easy and hard direction in-plane field hysteresis loops for fields between -100 and +100 Oe, and 10 GHz…