The Hall effect is investigated in thin-film samples of iron-chalcogenide superconductors in detail. The Hall coefficient (RH) of FeTe and Fe(Se1-xTex) exhibits a similar positive value around 300 K, indicating that the high-temperature…
The Hall effect is investigated in detail for nonsuperconducting and superconducting FeTe thin films. The Hall coefficient commonly exhibits a sign reversal from positive in a high-temperature paramagnetic state to negative in a…
We have investigated the temperature and magnetic field dependence of the Hall coefficient of two well-characterized superconducting MgB$_2$ films (T$_{c0}$=38.0 K) in both the normal and superconducting states. Our results show that the…
We report the temperature dependence of resistivity (rho) and Hall coefficient (R_H) in the normal state of homogeneously disordered epitaxial NbN thin films with kFl~3.27-10.12. The superconducting transition temperature (Tc) of these…
Superconducting compounds of the family Hg-Ba-Ca-Cu-O have been the subject of intense study since the current record-holder for the highest critical temperature of a superconductor belongs to this class of materials. Thin films of the…
Magnetite epitaxial thin films have been prepared by pulsed laser deposition at 340 C on MgO and Si substrates. One key result is that the thin film properties are almost identical to the properties of bulk material. For 40 - 50 nm thick…
We investigated the transport properties under magnetic fields of up to 9 T for FeSe$_{1-x}$Te$_x$ thin films on CaF$_2$. Measurements of the temperature dependence of the electrical resistivity revealed that for $x = 0.2 - 0.4$, where…
The Hall conductivities of HgBa_{2}CaCu_{2}O_{6+\delta}and HgBa_{2}Ca_{2}Cu_{3}O_{8+\delta} thin films are investigated for a magnetic field parallel to the c axis. The mixed-state Hall conductivity for these compounds is well described by…
The Hall coefficient (R_H) is investigated along the in-plane direction for carefully prepared La_2-x_Sr_x_CuO_4_ thin films from x=0.08 to x=0.40. It is found that R_H becomes almost temperature independent around room temperature for x >=…
Thin films of the high-temperature superconductor HgBa$_2$CaCu$_2$O$_{6+\delta}$ have been prepared on SrTiO$_3$ substrates by pulsed-laser deposition of precursor films and subsequent annealing in mercury-vapor atmosphere. The…
Measurements of the Hall effect and the resistivity on precisely-patterned YBCO thin films in magnetic fields B from 0.5 to 6 T oriented parallel to the sample crystallographic c axis reveal a sign reversal of the Hall coefficient for B <=…
We prepared high epitaxial thin films of the compound Sr_2FeMoO_6 with narrow rocking curves by pulsed laser deposition. The diagonal and nondiagonal elements of the resistivity tensor were investigated at temperatures from 4 K up to room…
The anomalous Hall effect (AHE) of ferromagnetic thin films of Sr$_{1-x}$Ca$_{x}$RuO$_3$ (0 $\leq x \leq$ 0.4) is studied as a function of $x$ and temperature $T$. As $x$ increases, both the transition temperature $T_c$ and the…
The normal-state Hall coefficient R_H and the in-plane resistivity \rho_{ab} are measured in La-doped Bi_{2}Sr_{2}CuO_{y} (T_c \simeq 13 K) single crystals and La_{2-x}Sr_{x}CuO_{4} thin films by suppressing superconductivity with 61-T…
The sign change in the Hall conductivity has been studied in thin amorphous Nb$_{1-x}$Ge$_x (x\approx$0.3) films. By changing the film thickness it is shown that the field at which the sign reversal occurs shifts to lower values (from above…
We have measured the longitudinal resistivity and the Hall resistivity in the ab-plane of highly c-axis-oriented MgB2 thin films. In the normal state, the Hall coefficient (R_H) behaves as R_H ~ T with increasing temperature (T) up to 130 K…
Superconducting FeSe0.8Te0.2 thin films on SrTiO3, LaAlO3 and CaF2 substrates were electrochemically etched in an ionic liquid DEME-TFSI electrolyte with a gate bias of 5 V. Superconductivity at 38 K was commonly observed on all substrates…
We report the high-field superconducting properties of thin, disordered Re films via magneto-transport and tunneling density of states measurements. Films with thicknesses in the range of 9 nm to 3 nm had normal state sheet resistances of…
The electrical resistivity and Hall coefficient of LaFeAsO0.95F0.05 polycrystalline samples were measured in pulsed magnetic fields up to m0H = 60 T from room temperature to 1.5 K. The resistance of the normal state shows a negative…
Transport properties of the good thermoelectric misfit oxide Ca$_3$Co$_4$O$_9$ are examined. In-plane resistivity and Hall resistance measurements were made on epitaxial thin films which were grown on {\it c}-cut sapphire substrates using…