In this paper we report the growth and superconductivity of $Na_xTaS_2$ crystals. The structural data deduced from X-ray diffraction pattern shows that the sample has the same structure as $2H-TaS_2$. A series of crystals with different…
Superconducting Sm(O,F)BiS2 single crystals were successfully grown using KI-KCl flux. The obtained single crystals were flat-shaped and their size was 500um. The structure and composition of the obtained single crystals were obtained using…
We report the successful growth of high quality single crystals of LiFeAs with lateral sizes up to 5 x 5 mm2 by the Sn-flux method. Electrical resistivity studies reveal that the superconducting onset temperature is 18.2 K with a transition…
Single crystals of SrFe2-xPtxAs2 (0 < x < 0.36) were grown using the self flux solution method and characterized using x-ray crystallography, electrical transport, magnetic susceptibility, and specific heat measurements. The…
Single crystal of Cu0.03TaS2 with low copper intercalated content was successfully grown via chemical iodine-vapor transport. The structural characterization results show that the copper intercalated 2H-Cu0.03TaS2 single crystal has the…
Centimeter sized platelet single crystals of KFe2As2 were grown using a self-flux method. An encapsulation technique using commercial stainless steel container allowed the stable crystal growth lasting for more than 2 weeks. Ternary K-Fe-As…
F-substituted NdOBiS2 superconducting single crystals were grown using CsCl/KCl flux. This is the first example of the single-crystal growth of a BiS2-based superconductor. The obtained single crystals had a plate-like shape with a size of…
We report single-crystal growth of La$_{0.34}$Na$_{0.66}$Fe$_2$As$_2$ iron-based superconductor with the size of several millimeters. The samples were accidentally obtained in trying to grow LaFeAsO$_{1-y}$F$_y$ ( $y \geq$ 0.8 ) single…
Millimeter sized single crystals of CaFe$_{1-x}$Co$_x$AsF were grown using a self-flux method. It is found that high-quality single crystals can be grown from three approaches with different initial raw materials. The chemical compositions…
Single crystals of undoped CaFe2As2 were grown by a FeAs self-flux method, and the crystals were quenched in ice-water rapidly after high temperature growth. The quenched crystal undergoes a collapsed tetragonal structural phase transition…
Single crystals of SmFeAsO1-xFy of a size up to 120 micrometers have been grown from NaCl/KCl flux at a pressure of 30 kbar and temperature of 1350-1450 C using the cubic anvil high-pressure technique. The superconducting transition…
Millimeter sized single crystals of KCa_2Fe_4As_4F_2 were grown using a self-flux method. The chemical compositions and crystal structure were characterized carefully. Superconductivity with the critical transition T_c = 33.5 K was…
Cd-doped La(O,F)BiS2 single crystals were grown using a CsCl/KCl flux. The grown crystals have a plate-like shape with ~1-2 mm square size in a well-developed ab-plane. The Cd doping in the crystals was successfully characterized by single…
High-quality Bi$_{2+x}$Sr$_{2-x}$CuO$_{6+\delta}$(0$<$x$\leq$0.5) single crystals have been grown successfully using the travelling-solvent floating-zone(TSFZ) technique. The samples with $x >$ 0.05 are in the underdoped level. The…
Single crystals of Ba0.6K0.4Fe2As2 with excellent quality have been successfully grown without fluxing agent through a simple one-step method for the first time. X-ray diffraction patterns demonstrate that the samples have high crystalline…
An eutectic LiCl/KCl flux method in a horizontal configuration has been used to grow a series of homogeneous Fe$_{1+\delta}$Se$_{1-x}$Te$_x$ single crystals of high quality with 0.5 $\leq$ $x$ $\leq$ 1. Compared with previously used…
In this paper we present the single crystal growth of Fe0.95Se0.6Te0.4 high TC superconducting sample by the modified Bridgman technique. The x-ray diffraction pattern shows the single crystal nature of the sample, as only (00l) peaks are…
F-substituted LaOBiSe2 single crystals were grown using CsCl flux. The obtained single crystals showed a plate-like shape with a size of about 1.0 mm square. The c-axis lattice constant of the grown crystals was determined to be 14.114(3)…
Millimeter-sized single crystals of LaFeAsO, LaFeAsO1-xFx, and LaFe1-xCoxAsO were grown in NaAs flux at ambient pressure. The detailed growth procedure and crystal characterizations are reported. The as-grown crystals have typical…
The single crystal of ThCr2Si2-type BaPd2As2 was successfully prepared by a self-flux method, and the crystal structure was characterized by X-ray diffraction method with the lattice parameters a = 4.489(2) {\AA} and c = 10.322(3) {\AA}.…