Doping in the chalcopyrite Cu(In,Ga)Se2 is determined by intrinsic point defects. In the ternary CuInSe2, both N-type and P-type conductivity can be obtained depending on the growth conditions and stoichiometry: N-type is obtained when grown Cu-poor, Se-poor and alkali-free. CuGaSe2, on the other hand, is found to be always a P-type semiconductor that seems to resist all kinds of N-type doping no matter whether it comes from native defects or extrinsic impurities. In this contribution, we study the N-to-P transition in Cu-poor Cu(In,Ga)Se2 single crystals in dependence of the gallium content. Our results show that Cu(In,Ga)Se2 can still be grown as an N-type semiconductor until the gallium content reaches the critical concentration of 15-19%, where the N-to-P transition occurs. Furthermore, trends in the Seebeck coefficient and activation energies extracted from temperature-dependent conductivity measurements, demonstrate that the carrier concentration drops by around two orders of magnitude near the transition concentration. Our proposed model explains the N-to-P transition based on the differences in formation energies of donor and acceptor defects caused by the addition of gallium.
@article{arxiv.2204.12973,
title = {How much gallium do we need for a p-type Cu(In,Ga)Se2?},
author = {Omar Ramírez and Evandro Martin Lanzoni and Ricardo G. Poeira and Thomas P. Weiss and Renaud Leturcq and Alex Redinger and Susanne Siebentritt},
journal= {arXiv preprint arXiv:2204.12973},
year = {2025}
}