This work explores the possibility of increasing the density of negatively charged nitrogen-vacancy centers [NV-] in nanodiamonds using nitrogen-rich type Ib diamond powders as the starting materials. The nanodiamonds (10 - 100 nm in diameters) were prepared by ball-milling of microdiamonds, in which the density of neutral and automatically dispersed nitrogen atoms [N0] was measured by diffuse reflectance infrared Fourier transform spectroscopy (DRIFT). A systematic measurement for the fluorescence intensities and lifetimes of the crushed monocrystalline diamonds as a function of [N0] indicated that the [NV-] increases nearly linearly with [N0] at 100 - 200 ppm. The trend, however, failed to continue for nanodiamonds with higher [N0] (up to 390 ppm) but poorer crystallinity. We attribute the result to a combined effect of fluorescence quenching as well as the lower conversion efficiency of vacancies to NV- due to the presence of more impurities and defects in these as-grown diamond crystallites. The principles and practice of fabricating brighter and smaller fluorescent nanodiamonds (FNDs) are discussed.
@article{arxiv.1306.1594,
title = {Creating high density ensembles of nitrogen-vacancy centers in nitrogen-rich type Ib nanodiamonds},
author = {Long-Jyun Su and Chia-Yi Fang and Yu-Tang Chang and Kuan-Ming Chen and Yueh-Chung Yu and Jui-Hung Hsu and Huan-Cheng Chang},
journal= {arXiv preprint arXiv:1306.1594},
year = {2013}
}