Related papers: Improved critical current densities in MgB2 tapes …
We have previously shown for powders that Mo substitution into the CuO chains of YBa2Cu3O7 can create effective pinning centres which significantly increase the critical current density (j_c) in 7 T field by a factor of 4 and 10 at 50 and…
Polycrystalline MgB2 samples with 0, 2, 4 and 6 percent added nano-Co3O4 being synthesized by vacuum (10-5 Torr) annealing at 750 0C for three hours each are found to be nearly single phase with presence of only a small quantity of Mg/MgO…
Low resistivity ("clean") MgB2 bulk samples annealed in Mg vapor show an increase in upper critical field Hc2(T) and irreversibility field Hirr(T) by a factor of 2 in both transport and magnetic measurements. The best sample displayed Hirr…
By doping MgB_2 superconductor with SiC nano-particles, we have successfully introduced pinning sites directly into the crystal lattice of MgB_2 grains (intra-grain pinning). It became possible due to the combination of counter-balanced Si…
We report the influence of 6 MeV Zr$^{4+}$ irradiation and post-irradiation annealing (200 {\deg}C) in the in-field dependences of the critical current densities J$_c$ of 1.3 $\mu$m thick GdBa$_2$Cu$_3$O$_{7-d}$ coated conductors grown by…
In order to establish the doping dependence of the critical current properties in the iron-based superconductors, the in-plane critical current density (Jc) of BaFe2As2-based superconductors, Ba1-xKxFe2As2 (K-Ba122), Ba(Fe1-xCox)2As2…
Nb3Sn conductors are important candidates for high-field magnets for particle accelerators, and they continue to be widely used for many laboratory and NMR magnets. However, the critical current density, Jc, of present Nb3Sn conductors…
Magneto-optical current reconstruction has been used for detailed analysis of the local critical current density (Jc) variation in monocore Bi-2223 tapes. We find, even in high quality tapes with bulk transport Jc ~ 40 kA/cm^2 (77K, 0T),…
We investigated the doping effects of SWCNTs and MWCNTs on the Tc, lattice parameters, Jc(B), microstructure, and Hc2 of MgB2/Fe wire. These effects systematically showed the following sequence for Tc and the a-axis: the SWCNT doped wire <…
We have fabricated (Ba,K)Fe2As2 superconducting wires through ex-situ powder-in-tube method. Silver was used as a chemical addition to improve the performance of these superconducting wires. The transport critical current densities (Jc)…
By doing magnetization measurements during magnetic field sweeps on thin films of the new superconductor $MgB_2$, it is found that in a low temperature and low field region small flux jumps are taking place. This effect strongly suppresses…
Monocore powder-in-tube MgB2 strands were cold-drawn and heat-treated at 600C and 700C for times of up to 71 hours and structure-property relationships examined. Drawing-induced elongation of the Mg particles led, after HT, to a textured…
In this letter, we report the first successful fabrication of dense, metal-clad MgB2 superconductor wires as well as the first demonstration of high transport Jc of greater than 36,000 A/cm2 in MgB2. The fabrication technique that we…
This work studies the influence of microstructures and crystalline defects on the superconductivity of MgB2, with the objective to improve its flux pinning. A MgB2 sample pellet that was hot isostatic pressed (HIPed) was found to have…
Strong pinning depends on the pinning force strength and number density of effective defects. Using hydrostatic pressure method, we demonstrate that hydrostatic pressure up to 1.2 GPa can significantly enhance flux pinning or Jc by a factor…
Tremendous efforts towards improvement in the critical current density (Jc) of iron based superconductors (FeSCs), especially at relatively low temperatures and magnetic fields, have been made so far through different methods, resulting in…
Improving the critical temperature (TC), critical magnetic field (HC), and critical current (JC) of superconducting materials has always been one of the most significant challenges in the field of superconductivity, but progress has been…
Polycrystalline Sr0.6K0.4Fe2As2 samples with various Pb additions (0-20 wt%) were prepared using a one-step solid state reaction. X-ray diffraction analysis shows no evidence for chemical reaction between the Pb and the FeAs-based…
Iron is an important sheath material for fabrication of MgB2 wires. However, the effect of Fe doping on the superconducting properties of MgB2 remains controversial. In this work, we present results of nano-scale Fe particle doping in to…
We report large transport critical current densities observed in Ag-added (Ba,K)Fe2As2 superconducting wires prepared by an ex-situ powder-in-tube (PIT) process. The wire has a simple composite structure sheathed only by Ag. A precursor…