We have first used the aquesous KMnO4 solutions to de-intercalate and oxideze gamma-phase of Na0.7CoO2 and successfully form the superconductive phase of cobalt oxyhydrate hydrates (Na,K)xCoO2.yH2O with Tc=3.2-4.6K based on the…
The layered sodium cobalt oxyhydrate superconductor Na0.3CoO2*1.4H2O is shown through X-ray diffraction and thermogravimetric studies to be one of a series of hydrated phases of Na0.3CoO2. Further, it is shown that the material is…
We have first succeefully synthesized the sodium cobalt oxyhydrate superconductors using KMnO4 as a de-intercalating and oxidizing agent. It is a novel route to form the superconductive phase of NaxCoO2.yH2O without resorting to the…
We report the electrical, magnetic and thermal measurements on a layered cobalt oxyhydrate Na$_{0.31}$CoO$_{2}\cdot$1.3H$_{2}$O. Bulk superconductivity at 4.3 K has been confirmed, however, the measured superconducting fraction is…
We report the synthesis and superconducting properties of a metastable form of the known superconductor NaxCoO2*yH2O (x ~ 1/3, y ~ 4x). Instead of using the conventional bromine-acetonitrile mixture for sodium deintercalation, we use an…
Muon spin relaxation ($\mu$SR) measurements on the new layered cobalt oxide superconductor Na$_{0.35}$CoO$_{2}\cdot$1.3H$_{2}$O and its parent, non-superconducting compounds, have revealed unconventional nature of superconductivity through:…
The observation of superconductivity at 4.3 K in a new crystalline form of Na0.3CoO2*1.3H2O is reported. The new superconductor has three layers of CoO6 octahedra per crystallographic unit cell, in contrast to the previously reported…
Co(II) dissolved in acetate buffer at pH 7 is found to be a good water oxidation catalyst (WOC) showing electrocatalytic water oxidation current significantly greater than Co(II) in phosphate buffer under the same conditions owing to the…
Unconventional superconductivity in bulk materials under ambient pressure is extremely rare among the 3d transition metal compounds outside the layered cuprates and iron-based family. It is predominantly linked to highly anisotropic…
The hydration phase diagram for sodium cobalt oxyhydrate, Na0.3CoO2*yH2O (y=0, 0.6, 1.3), was determined as a function of relative humidity at 298K. It is found that greater than 75% relative humidity is needed for complete hydration of…
Pure phases of a new oxyarsenide superconductor of the nominal composition CeOFe0.9Co0.1As was successfully synthesized by solid state reaction in sealed silica ampoules at 1180 C. It crystallizes in the layered tetragonal ZrCuSiAs type…
We report the evidence of proton incorporations in a newly-discovered cobalt oxyhydrate superconductor. During the hydration process for Na$_{0.32}$CoO$_{2}$ by the direct reaction with water liquid, it was shown that substantial NaOH was…
Here we present results of accurate wet-chemical redox analyses, revealing that the oxidation number of cobalt in the newly discovered CoO2-layer superconductor, NaxCoO2 yH2O (x ~ 0.36, y ~ 1.3) is ~ 3.46. This value is significantly lower…
We report a successful tuning of Co valence state in cobalt oxyhydrate superconductor via a facile post reduction using NaOH as reducing agent. The change in Co valence was precisely determined by measuring the volume of the released…
We report the in-plane resistivity and magnetic susceptibility of the layered cobalt oxide Na$_{0.35}$CoO$_{2}{\cdot}1.3$H$_{2}$O single crystal. The temperature dependence of the resistivity shows metallic behavior from room temperature to…
Alkaline water electrolysis is considered a commercially viable option for large-scale hydrogen production. However, this process still faces challenges due to the high voltage (>1.65 V at 10 mA cm$^{-2}$) and its limited stability at…
We succeeded in synthesizing the powder samples of bilayer-hydrate sodium cobalt oxide superconductors NaxCoO2-yH2O with Tc = 0 ~ 4.6 K by systematically changing the keeping duration in a 75 % relative humidity atmosphere after…
Electrocatalysts based on transition metal sulfides are drawing accelerating concerns in renewable energy research because of their intrinsically excellent activities towards both hydrogen evolution reaction and oxygen evolution reaction.…
Neutron scattering has been used to investigate the crystal structure and lattice dynamics of superconducting Na0.3CoO2 1.4(H/D)2O, and the parent Na0.3CoO2 material. The structure of Na0.3CoO2 consists of alternate layers of CoO2 and Na…
Chemical doping has recently become a very important strategy to induce superconductivity especially in complex compounds. Distinguished examples include Ba-doped La$_2$CuO$_4$ (the first high temperature superconductor), K-doped BaBiO$_3$,…