Related papers: Microwave performance of high-density bulk MgB2
Microwave-field distribution, dissipation, and surface impedance are theoretically investigated for superconductors with laminar grain boundaries (GBs). In the present theory we adopt the two-fluid model for intragrain transport current in…
Superconducting $MgB_2$ wires in Cu, GlidCop or Monel sheath with Nb or Fe barrier are prepared. Wires vary by sheath material, number of superconducting cores and their chemical composition. Wires are HIP-ed (Hot Isostatic Pressing) at…
We report measurements of the complex resistivity in $YBCO$ and $MgB_2$ thin films over a continuous frequency spectrum in the microwave range, making use of a Corbino disk geometry. The paper mainly focuses on the extraction of the…
Two different hot isostatic pressing cycles (HIPing) were investigated to synthesize bulk MgB2 samples: a "standard" cycle where a low vessel pressure is maintained while heating to the process temperature with a subsequent simultaneous…
Bulk samples of MgB2 have been formed by hot isostatic pressing (HIPping) of commercial powder at 100MPa and 950=B0C. The resulting material is 100% dense with a sharp superconducting transition at 37.5K. Microstructural studies have…
We report on the microwave surface resistance of two polycrystalline Mg11B2 samples; one consists of pristine material, the other has been irradiated at very high neutron fluence. It has already been reported that in the strongly irradiated…
We evaluate the performance of hybrid microwave resonators made by combining sputtered Nb thin films with Tungsten nanowires grown with a He-beam induced deposition technique. Depending on growth conditions the nanowires have a typical…
We report magnetic field dependent magnetization and microwave impedance measurements on a MgB2 superconductor prepared by high pressure synthesis. We find that the upper critical field is linearly dependent on temperature near Tc and the…
Surface properties are critical to the capabilities of superconducting microwave devices. The native oxide of niobium-based devices is thought to consist of a thin normal conducting layer. To improve understanding on the importance of this…
The new superconductor MgB2 may prove useful for microwave applications at intermediate temperatures. MgB2 films with the thickness of 300 - 400 nm have surface resistance Rs less than 0.01 mOhms at a frequency (f) of 8.5 GHz and 7 K,and ~…
The surface impedance of Nb/CuMn (superconducting/spin-glass) bilayers has been measured at 10 GHz with the parallel plate resonator technique to obtain information about the exotic behavior of the order parameter in…
The MgB2 bulks were prepared by high energy milling of Mg and B powder. The correlations among milling times, microstructure and superconducting properties were investigated in MgB2 bulks. Samples were characterized by x-ray diffraction…
We have grown superconducting TiN films by atomic layer deposition with thicknesses ranging from 6 to 89 nm. This deposition method allows us to tune the resistivity and critical temperature by controlling the film thickness. The microwave…
The microwave response of ceramic MgB2 has been investigated as a function of temperature and external magnetic field by two different techniques: microwave surface impedance and second-harmonic emission measurements. The measurements of…
The microstructure of the MgB2 superconductor sintered at high temperature under a high pressure of about 3 GPa was investigated by using a high-resolution transmission electron microscope (HRTEM). The TEM images did not show any pores in…
The magnetic-field-induced variations of the microwave surface resistance have been investigated in a heavily neutron-irradiated MgB2 sample, in which the irradiation has caused the merging of the two gaps into a single value. The…
We have studied an anomalous microwave (mw) response of superconducting YBa_{2}Cu_{3}O_{7-delta} (YBCO) microstrip resonators in the presence of a weak dc magnetic field, H_{dc}. The surface resistance (R_{s}) and reactance (X_{s}) show a…
The microwave power, dc magnetic field, frequency and temperature dependence of the surface resistance of MgB2 films and powder samples were studied. Sample quality is relatively easy to identify by a number of characteristics, the most…
In this paper we present the results of measurements of the microwave surface impedance of a powder sample and two films of MgB$_2$. One film has $T_c=30$ K and is not textured, the other is partially c-axis orientated with $T_c=38$ K.…
We have carried out non-linear microwave (8 GHz) surface impedance measurements of three YBaCuO thin films in dc magnetic fields $H_{dc}$ (parallel to c axis) up to 12 mT using a coplanar resonator technique. In zero dc field the three…