Related papers: Titanium additions to MgB2 conductors
The superconducting properties of copper-sheathed MgB2 wires fabricated by conventional powder-in-tube techniques and the in-situ reaction procedure are analysed. The influence of the processing conditions and initial (1+x)Mg + 2B (x = 0,…
The review considers bulk MgB2-based materials in terms of their structure, superconducting and mechanical properties. Superconducting transition temperatures of 34.5-39.4 K, critical current densities of 1.8-1.0 x E6 A/sq.cm in self field…
Thin superconducting films of magnesium diboride (MgB2) with Tc \approx 24K were prepared on various oxide substrates by pulsed laser deposition (PLD) followed by an in-situ anneal. A systematic study of the influence of various in-situ…
Monocore powder-in-tube MgB2 strands were cold-drawn and heat-treated at 600C and 700C for times of up to 71 hours and structure-property relationships examined. Drawing-induced elongation of the Mg particles led, after HT, to a textured…
The Tb-123 phase has been synthesized in single-phase form with the composition TbSr2Cu2.7Mo0.3O7 by solid-state reaction route and its phase purity is confirmed by neutron powder diffraction experiments. As-synthesized sample does not show…
MoSi2 doped MgB2 tapes with different doping levels were prepared through the in-situ powder-in-tube method using Fe as the sheath material. Effect of MoSi2 doping on the MgB2/Fe tapes was investigated. It is found that the highest JC value…
We report synthesis, structure/micro-structure, resistivity under magnetic field [R(T)H], Raman spectra, thermoelectric power S(T), thermal conductivity K(T), and magnetization of ambient pressure argon annealed polycrystalline bulk samples…
Superconductivity was discovered in heavily boron-doped diamond thin films deposited by the microwave plasma assisted chemical vapor deposition (MPCVD) method. Advantages of the MPCVD deposited diamond are the controllability of boron…
Superconducting thin films of MgB2 were deposited by Pulsed Laser Deposition on magnesium oxide and sapphire substrates. Samples grown at 450C in an argon buffer pressure of about 10-2 mbar by using a magnesium enriched target resulted to…
We have discovered that samples of a new material produced by special processing of crystals of Sr2RuO4 (which is known to be a triplet superconductor with Tc values ~1.0-1.5K) exhibit signatures of superconductivity (zero DC resistance and…
Superconducting MgB2 strands with nanometer-scale SiC additions have been investigated systematically using transport and magnetic measurements. A comparative study of MgB2 strands with different nano-SiC addition levels has shown…
We found that transport critical current density (Jc) of the Ba1-xKxFe2As2/Ag tapes is significantly enhanced by the combination process of cold flat rolling and uniaxial pressing. At 4.2 K, the Jc reaches a high value of 9.1x104 A/cm2 in 4…
Superconductivity is observed with critical temperatures near 9K in the tetragonal compound Mo5PB2. This material adopts the Cr5B3 structure type common to supercondcuting Nb5Si3-xBx, Mo5SiB2, and W5SiB2, which have critical temperatures of…
We report the growth of high-quality c-axis-oriented epitaxial MgB2 thin films by using a pulsed laser deposition technique. The thin films grown on (1`1 0 2) Al2O3 substrates show a Tc of 39 K. The critical current density in zero field is…
The high resistivity of many bulk and film samples of MgB2 is most readily explained by the suggestion that only a fraction of the cross-sectional area of the samples is effectively carrying current. Hence the supercurrent (Jc) in such…
We report on significant flux pinning enhancement in MgB2/Fe tapes that has been easily obtained by a simple and cheap route using acetone as both an efficient ball-milling medium and liquid additive through the in situ method. Results…
The recent discovery of superconductivity at ~39 K in MgB2, by Nagamatsu et al. establishes this simple binary compound as having the highest bulk superconducting transition temperature, Tc, of any non-copper-oxide material. Much of the…
The pair-breaking critical current density j_{d} of magnesium diboride was determined over its entire temperature range by a pulsed dc transport measurement. At fixed low values of current density j, the resistive transition temperature Tc…
Fe-clad MgB2 long tapes have been fabricated using a powder-in-tube technique. An Mg + 2B mixture was used as the central conductor core and reacted in-situ to form MgB2. The tapes were sintered in pure Ar at 800 ^(o) C for 1 h at ambient…
The discovery of the first high critical temperature (Tc) transition metal diboride superconductor, MgB2 structure alpha-MoB2 under pressure with Tc up to 32 K at 100 GPa, provides new input into some unexplained aspects of electron-phonon…