Related papers: Titanium additions to MgB2 conductors
Measurements of the superconducting upper critical field, H_{c2}, and critical current density, J_c, have been carried out for MgB_2 doped with Ti and/or C in order to explore the problems encountered if these dopants are used to enhance…
Processing methods are described for the development of magnesium diboride wire using the chemical vapor deposition (CVD) to produce long lengths of suitably doped starting boron fiber. It is found that titanium can be co-deposited with the…
Superconducting MgB2 thin films were prepared on Al2O3(0001) and MgO(100) substrates. Boron thin films were deposited by the electron-beam evaporation followed by post-annealing process with magnesium. Proper post annealing conditions were…
The nano-SiC doped MgB2/Fe wires were fabricated using a powder-in-tube method and an in-situ reaction process. The depression of Tc with increasing SiC doping level remained rather small due to the counterbalanced effect of Si and C…
The upper critical field, $H_{c2}$, of Mg(B$_{1-x}$C$_x$)$_2$ has been measured in order to probe the maximum magnetic field range for superconductivity that can be attained by C doping. Carbon doped boron filaments are prepared by CVD…
The MgB2 - based material high-pressure synthesized at 2 GPa and 800 C for 1 h from Mg and B (taken in the stoichiometry ratio of MgB2) with addition of 2-10 wt% of Ti demonstrated the critical current density (jc) higher than 100 kA/cm^2…
A MgB2 superconducting tape has been successfully prepared by a new way of boron diffusion into Mg tape. This tape superconductor has a Tc of 39 K with a sharp transition width of 0.4 K, high bulk critical current density jc of 6.7*10^5…
MgB2/Fe tapes with 2.5-15 at.% ZrB2 additions were prepared through the in situ powder-in-tube method. Compared to the pure tape, a significant improvement in the in-field critical current density Jc was observed, most notably for 10 at.%…
The effect of doping MgB2 with carbon nanotubes on transition temperature, lattice parameters, critical current density and flux pinning was studied for MgB2-xCx with x = 0, 0.05, 0.1, 0.2 and 0.3. The carbon substitution for B was found to…
Doping of MgB2 by nano-SiC and its potential for improvement of flux pinning was studied for MgB2-x(SiC)x/2 with x = 0, 0.2 and 0.3 and a 10wt% nano-SiC doped MgB2 samples. Co-substitution of B by Si and C counterbalanced the effects of…
A review of current developments in the study of chemical doping effect on the superconducting properties of MgB2 wires and tapes is presented, based on the known literature data and our own results. The critical current density of MgB2 can…
An improvement of the transport critical current density, Jc, of MgB2 wires was obtained after addition of 10 wt.% B4C powders, after reaction at 800 C: Jc values of 1.10^4 A/cm2 at 4.2 K and 9T were obtained for wires of 1.11 mm diameter…
The effect of doping with Ti, Ta, SiC in complex with synthesis temperature on the amount and distribution of structural inhomogeneities in MgB2 matrix of high-pressuresynthesized-materials (2 GPa) which can influence pining: higher borides…
We prepared and characterized monofilamentary MgB2 wires with a mechanically reinforced composite sheath of Ta(Nb)/Cu/steel, which leads to dense filaments and correspondingly high transport currents up to Jc = 10^5 A/cm^2 at 4.2 K, self…
We report the effect of adipic acid (C6H10O4) doping on lattice parameters, microstructure, critical temperature (Tc), current density (Jc), and irreversibility field (Hirr) for MgB2 superconductor. Actual carbon (C) substitution level for…
We have fabricated a series of ex situ copper sheathed powder-in-tube MgB2 wires with 20% by volume Ag, Pb, In, and Ga metal added to the MgB2 powder. We find the transport critical current of these wires increases significantly with the…
MgB2 is a promising superconductor for important large-scale applications for both high field magnets and cryocooler-cooled magnet operated at temperatures around 20 K. In this work, by utilizing C60 as a viable alternative dopant, we…
Nanocarbon-doped Fe-sheathed MgB2 tapes with different doping levels were prepared by the in situ powder-in-tube method. Compared to the undoped tapes, Jc for all the C-doped samples was enhanced by more than an order of magnitude in…
With the relatively high critical temperature (Tc) of 39 K1 and the high critical current density (Jc) of > 100000 A/cm2 in moderate fields, magnesium diboride (MgB2) superconductors could offer the promise of important large-scale and…
The MgB2 coated superconducting tapes have been fabricated on textured Cu (0 0 1) and polycrystalline Hastelloy tapes using coated conductor technique, which has been developed for the second generation high temperature superconducting…