Related papers: Bulk Magnesium Diboride, Mechanical and Supercondu…
This work studies the influence of microstructures and crystalline defects on the superconductivity of MgB2, with the objective to improve its flux pinning. A MgB2 sample pellet that was hot isostatic pressed (HIPed) was found to have…
The synthesis of MgB2-based materials under high pressure gave the possibility to suppress the evaporation of magnesium and to obtain near theoretically dense nanograined structures with high superconducting, thermal conducting, and…
Carbon-doped magnesium diboride was fabricated from pre-reacted pure MgB2 by mechanical alloying. The sample set had excellent critical current densities Jc(8T,4.2K) ranging from 15-60 kA/cm2, depending on composition. Magneto-optical…
We succeeded in the synthesis of high-Jc MgB2 bulks via high energy ball-milling of elemental Mg and B powder at ambient temperatures. Alternatively to longtime mechanical alloying technique, the mixed powder was ball-milled for only 1h and…
Seven years after the discovery of superconductivity in magnesium diboride, the fundamental superconducting properties of this compound are well known and the peculiar current transport in polycrystalline materials is essentially…
High-density bulk materials of a newly discovered 40K intermetallic MgB2 superconductor were prepared by high pressure sintering. Superconducting transition with the onset temperature of 39K was confirmed by both magnetic and resistive…
A trapped field of over 1 T at 5 K and 0.5 T at 20 K has been measured between a stack of magnetized cylinders of bulk polycrystalline Ba0.6K0.4Fe2As2 superconductors 10 mm in diameter and 18 mm in combined thickness. The trapped field…
The study of high pressure (2 GPa) synthesized MgB2-based materials allows us to conclude that higher borides (with near MgB12 stoichiometry) and oxygen-enriched Mg-B-O inclusions can be pinning centers in nanostructural magnesium diboride…
Superconducting thin films of MgB2 were deposited by Pulsed Laser Deposition on magnesium oxide and sapphire substrates. Samples grown at 450C in an argon buffer pressure of about 10-2 mbar by using a magnesium enriched target resulted to…
The high-pressure synthesis is one of the most promising methods to produce MgB2 superconductive (SC) material. The available high-pressure apparatuses have working volume up to 100 cm3 which allows samples up to 60 mm in diameter to be…
The study of materials behavior under extreme conditions is fundamental to science and modern technology. Fast ramp compression is a unique method for exploring materials behavior and phase transformations under extreme conditions. One…
Flake-shaped FeSi-based metallic amorphous alloy particles, having an aspect ratio as high as 175 to 1, were prepared by ball milling gas atomized amorphous powders of an effective diameter of 20 micrometers. The starting powder had a…
The microstructure of the MgB2 superconductor sintered at high temperature under a high pressure of about 3 GPa was investigated by using a high-resolution transmission electron microscope (HRTEM). The TEM images did not show any pores in…
The critical current density of four MgB2 samples was measured inductively and for one of them also by transport. Pure phased and dense bulk samples yield a critical current density which in value, as well as in its magnetic field and…
A trapped field of over 3 T has been measured at 17.5 K in a magnetised stack of two disc-shaped bulk MgB2 superconductors of diameter 25 mm and thickness 5.4 mm. The bulk MgB2 samples were fabricated by uniaxial hot pressing, which is a…
Magnesium (Mg) and its alloys have a great potential as structural materials due to their beneficial combination of high strength to weight ratio, high thermal conductivity and good machinability. However, few literatures about Mg coatings…
We tune the thermodynamics of hydrogen absorption in Mg by means of elastic clamping. The loading isotherms measured by hydrogenography show that Mg films covered with Mg-alloy-forming elements, such as Pd and Ni, have hydrogen plateau…
We report on the determination of high-pressure elasticity from thermal diffuse x-ray scattering of magnesium oxide at pressures up to 28 GPa. We find that the full elasticity tensor as a function of pressure can be extracted from x-ray…
The review considers bulk MgB2-based materials in terms of their structure, superconducting and mechanical properties. Superconducting transition temperatures of 34.5-39.4 K, critical current densities of 1.8-1.0 x E6 A/sq.cm in self field…
The MgB2 - based material high-pressure synthesized at 2 GPa and 800 C for 1 h from Mg and B (taken in the stoichiometry ratio of MgB2) with addition of 2-10 wt% of Ti demonstrated the critical current density (jc) higher than 100 kA/cm^2…