Related papers: Comparative Study of Dense Bulk MgB$_2$ Materials …
Despite the intense activity in the year since the discovery of superconductivity in MgB2, key parameters, in particular the upper and lower critical fields Hc2 and Hc1 and their anisotropies, are not well-established, largely because of…
We address the effect of MgO impurity on the superconducting properties of MgB2. The synthesis of MgB2 is very crucial because of sensitivity of Mg to oxidation which may lead to MgO as a secondary phase. Rietveld refinement was performed…
Electrolysis was carried out on fused mixtures of MgCl2, NaCl, KCl and MgB2O4 under an Ar flow at 600C. Electrical resistivity measurements for the grown deposits show an onset of superconducting transition at 37 K in the absence of applied…
A trapped field of over 3 T has been measured at 17.5 K in a magnetised stack of two disc-shaped bulk MgB2 superconductors of diameter 25 mm and thickness 5.4 mm. The bulk MgB2 samples were fabricated by uniaxial hot pressing, which is a…
In this paper we report a new sol-gel method for the fabrication of MgB2 films. Polycrystalline MgB2 films were prepared by spin-coating a precursor solution of Mg(BH_4)_2 diethyl ether on (001)Al2O3 substrates followed with annealing in Mg…
Here we report a systematic study of superconductive properties of mono-filamentary MgB2-based wires, manufactured with different filling technique. A detailed comparison of the influence of filling technique and final heat treatment on…
We review recent measurements of upper (Hc2) and lower (Hc1) critical fields in clean single crystals of MgB2, and their anisotropies between the two principal crystallographic directions. Such crystals are far into the "clean limit" of…
We have developed disk-shaped MgB2 bulk superconducting magnets (20, 30 mm in diameter, 10 mm in thickness) using the in-situ process from Mg and B powders and evaluated the temperature dependence of trapped magnetic field. A pair of two…
Measurements of the critical current density (Jc) by magnetization and the upper critical field (Hc2) by magnetoresistance have been performed for hafnium-doped MgB2. There has been a remarkable enhancement of Jc as compared to that by ion…
The paper reports the first successful fabrication of MgB2 superconducting tape using a flexible metallic substrate as well as its strong pinning force, which was verified by direct measurement of transport critical current density. The…
It has recently been observed that MgB_2 is a superconductor with a high transition temperature. Here we propose a model of anisotropic s-wave superconductivity which consistently describes the observed properties of this compound,…
MgB2 thick film was synthesized on the stainless steel substrate by the technique of hybrid physical-chemical vapor deposition (HPCVD), using Mg ingot and B2H6 as the raw materials. The film thickness is about 10 microns. The scanning…
The microwave response of three high-density bulk MgB2 samples has been investigated in the linear and nonlinear regimes. The three samples, characterized by different mean size of grains, have been obtained by reactive infiltration of…
The upper critical field, $H_{c2}$, of Mg(B$_{1-x}$C$_x$)$_2$ has been measured in order to probe the maximum magnetic field range for superconductivity that can be attained by C doping. Carbon doped boron filaments are prepared by CVD…
We have performed a comparative study of two thin films of magnesium diboride (MgB2) grown by different techniques. The critical current density at different temperatures and magnetic fields was evaluated from magnetisation curves, the…
Bulk samples of MgB2 were prepared with 5, 10, and 15% wt.% Y2O3 nanoparticles added using a simple solid-state reaction route. Transmission electron microscopy (TEM) showed a fine nanostructure consisting of ~3-5 nm YB4 nanoparticles…
Thin films of the high-temperature superconductor HgBa$_2$CaCu$_2$O$_{6+\delta}$ have been prepared on SrTiO$_3$ substrates by pulsed-laser deposition of precursor films and subsequent annealing in mercury-vapor atmosphere. The…
Superconducting $MgB_2$ wires in Cu, GlidCop or Monel sheath with Nb or Fe barrier are prepared. Wires vary by sheath material, number of superconducting cores and their chemical composition. Wires are HIP-ed (Hot Isostatic Pressing) at…
Bulk metallic samples were synthesized from different binary powder mixtures consisting of elemental Cu, Co, and Fe using severe plastic deformation. Small particles of the ferromagnetic phase originate in the conductive Cu phase, either by…
We report magnetic field dependent magnetization and microwave impedance measurements on a MgB2 superconductor prepared by high pressure synthesis. We find that the upper critical field is linearly dependent on temperature near Tc and the…