Superconducting properties of bulk, dense, pure MgB2 and doped (Mg1-xAx)B2 samples with A = Na, Ca, Cu, Ag, Zn and Al were studied for compositional ranges 0 < x < 0.20. The effect on pinning properties and critical current were…
We present electrical transport, magnetization, and specific heat measurements on bulk MgB2 samples (T_{c} = 38.5 K) synthesized under 200 MPa pressure using a process based on hot isostatic pressing with cooling under pressure. The samples…
Bulk samples of MgB2 have been formed by hot isostatic pressing (HIPping) of commercial powder at 100MPa and 950=B0C. The resulting material is 100% dense with a sharp superconducting transition at 37.5K. Microstructural studies have…
Superconductivity with Tc above 9 K was found in metal-deficient NbB2 prepared under 5 GPa, while no clear superconductivity was observed down to 3 K in stoichiometric NbB2. The superconductivity was observed above x = 0.04 in Nb1-xB2. and…
We have successfully prepared the MgB2 superconducting bulk and powdered materials by the method of combustion synthesis. The starting materials used in this study were powders of Mg and B. X-ray powder diffraction pattern was well assigned…
The high-pressure synthesis is one of the most promising methods to produce MgB2 superconductive (SC) material. The available high-pressure apparatuses have working volume up to 100 cm3 which allows samples up to 60 mm in diameter to be…
High-density bulk materials of a newly discovered 40K intermetallic MgB2 superconductor were prepared by high pressure sintering. Superconducting transition with the onset temperature of 39K was confirmed by both magnetic and resistive…
The synthesis of MgB2-based materials under high pressure gave the possibility to suppress the evaporation of magnesium and to obtain near theoretically dense nanograined structures with high superconducting, thermal conducting, and…
The normal state and superconducting properties of MgB2 and Mg1-xAlxB2 are discussed based on structural, transport, and high pressure experiments. The positive Seebeck coefficient and its linear temperature dependence for Tc<T<160 K…
High-pressure superconductivity in a rare-earth doped Ca0.86Pr0.14Fe2As2 single crystalline sample has been studied up to 12 GPa and temperatures down to 11 K using designer diamond anvil cell under a quasi-hydrostatic pressure medium. The…
The MgB2 bulks were prepared by high energy milling of Mg and B powder. The correlations among milling times, microstructure and superconducting properties were investigated in MgB2 bulks. Samples were characterized by x-ray diffraction…
In this letter, we report the first successful fabrication of dense, metal-clad MgB2 superconductor wires as well as the first demonstration of high transport Jc of greater than 36,000 A/cm2 in MgB2. The fabrication technique that we…
We report on the results of a comparative investigation of highly dense bulk MgB$_2$ samples prepared by three methods: (i) hot deformation; (ii) high pressure sintering; and (iii) mechanical alloying of Mg and B powders with subsequent hot…
Measurements of the superconducting upper critical field, H_{c2}, and critical current density, J_c, have been carried out for MgB_2 doped with Ti and/or C in order to explore the problems encountered if these dopants are used to enhance…
The review considers bulk MgB2-based materials in terms of their structure, superconducting and mechanical properties. Superconducting transition temperatures of 34.5-39.4 K, critical current densities of 1.8-1.0 x E6 A/sq.cm in self field…
We employ ab initio modeling to investigate the possibility of attaining high-temperature conventional superconductivity in ambient-pressure materials based on the known MgB$_2$C$_2$ and recently proposed thermodynamically stable NaBC…
Two single crystalline samples with the same nominal composition of Rb0.8Fe2Se2 prepared via slightly different precursor routes under the same thermal processing conditions were investigated at ambient and high pressures. One sample was…
NaCl-type metal tellurides (MTe) have been widely studied due to unique physical properties. We investigated the In-doping effects on structural and physical properties of Na-Cl type (AgPbBi)(1-x)/3InxTe and the superconducting properties…
Superconductivity is an important area of modern research which has benefited enormously from experiments under high pressure conditions. The focus of this paper will be on three classes of high-temperature superconductors: (1) the new…
Single crystals of Mg1-xAlxB2 have been grown at a pressure of 30 kbar using the cubic anvil technique. Precipitation free crystals with x < 0.1 were obtained as a result of optimization of already developed MgB2 crystal growth procedure.…