Related papers: Synthesis of MgB2 from elements
A new method for preparation of single crystals of the superconducting intermetallic MgB2 compound from a Mg-Cu-B melt flux is presented. The high vapour pressure of Mg at elevated temperature is a serious challenge of the preparation…
Superconducting MgB2 was synthesized in a stainless steel tube which compressed by pulsed magnetic field. The temperature dependence of diamagnetic moment m(T) was investigated and the pinning potential was determined
We have successfully prepared the MgB2 superconducting bulk and powdered materials by the method of combustion synthesis. The starting materials used in this study were powders of Mg and B. X-ray powder diffraction pattern was well assigned…
Dense pure and doped (Mg1-xAx)B2 samples with A = Na, Ca, Cu, Ag, Zn and Al were synthesized at high pressure - high temperature in a multi anvils press (3.5-6 GPa, 900-1000C) for x up to 0.20. They were studied by x-ray diffraction,…
The high-pressure synthesis is one of the most promising methods to produce MgB2 superconductive (SC) material. The available high-pressure apparatuses have working volume up to 100 cm3 which allows samples up to 60 mm in diameter to be…
High-density bulk materials of a newly discovered 40K intermetallic MgB2 superconductor were prepared by high pressure sintering. Superconducting transition with the onset temperature of 39K was confirmed by both magnetic and resistive…
We synthesized single crystalline and policrystalline MgB_2 under ambient pressures. The single crystals of MgB_2 were of good quality, where the crystal structure refinements were successfully converged with R = 0.020. The specific heat of…
The MgB2 superconductor synthesized in a flowing argon atmosphere using nanometer magnesium powder as the raw materials, denoted as Nano-MgB2, has been studied by the technique of in-situ high temperature resistance measurement (HT-RT…
Electrolysis has been performed on a fused mixture of magnesium chloride, potassium chloride, and magnesium borate at 600 oC under an Ar atmosphere using a graphite anode and a Pt cathode. Magnetic measurements and X-ray diffractometry have…
The review considers bulk MgB2-based materials in terms of their structure, superconducting and mechanical properties. Superconducting transition temperatures of 34.5-39.4 K, critical current densities of 1.8-1.0 x E6 A/sq.cm in self field…
We fabricated superconducting MgB2 thin films on (001) MgO substrates. The samples were prepared by magnetron rf and dc co-sputtering on heated substrates. They were annealed ex-situ for one hour at temperatures between 450{\deg}C and…
Superconducting MgB2 thin films were prepared on 50-micrometer-thick, flexible polyamide Kapton-E foils by vacuum co-deposition of Mg and B precursors with nominal thickness of about 100 nm and a special ex-situ rapid annealing process in…
The basic magnetic and electronic properties of most binary compounds have been well known for decades. Therefore the recent announcement of superconductivity at 39 K in the simple binary ceramic compound MgB2 is surprising. This compound,…
This review paper illustrates the main normal and superconducting state properties of magnesium diboride, a material known since early 1950's, but recently discovered to be superconductive at a remarkably high critical temperature Tc=40K…
The results of electrical resistance (1.4 - 300 K), magnetization (2-300 K) and heat-capacity (2 - 50 K) measurements in Y$_2$PdGe$_3$, found to crystallize in a AlB$_2$-derived hexagonalstructure, are reported. The results establish that…
Thin superconducting films of magnesium diboride (MgB2) with Tc \approx 24K were prepared on various oxide substrates by pulsed laser deposition (PLD) followed by an in-situ anneal. A systematic study of the influence of various in-situ…
We succeeded in the synthesis of high-Jc MgB2 bulks via high energy ball-milling of elemental Mg and B powder at ambient temperatures. Alternatively to longtime mechanical alloying technique, the mixed powder was ball-milled for only 1h and…
We report the effect of annealing on the superconductivity of MgB2 thin films as functions of the postannealing temperature in the range from 700 C to 950 C and of the postannealing time in the range from 30 min to 120 min. On annealing at…
We present electrical transport, magnetization, and specific heat measurements on bulk MgB2 samples (T_{c} = 38.5 K) synthesized under 200 MPa pressure using a process based on hot isostatic pressing with cooling under pressure. The samples…
Following the recent theoretical prediction of superconductivity in hole doped LiBC by Rosner et al [1], we have attempted to synthesise Li deficient LixBC (x = 1, 0.8, 0.6 and 0.4) and look for superconductivity in this system. Our…