Transport and thermodynamic properties of a sintered pellet of the newly discovered $MgB_2$ superconductor have been measured to determine the characteristic critical magnetic fields and critical current densities. Both resistive transition…
The powder-in-tube MgB2 wires were prepared by high energy milling of Mg and B powder. The powder was not mechanically alloyed for 2h short milling time. However, the MgB2 grains in wires are very small (20 100nm) and resembled to the…
Spatially resolved characterization of the critical current density Jc in superconductors under high magnetic fields is crucial for both fundamental understanding and practical applications. However, conventional techniques primarily…
The critical current density flowing across low angle grain boundaries in YBa$_2$Cu$_3$O$_{7-\delta}$ thin films has been studied magnetometrically. Films (200 nm thickness) were deposited on SrTiO$_3$ bicrystal substrates containing a…
If the critical current density Jc is very high for a superconductor, then estimating its value from transport measurements is not very easy. In such cases, the value of Jc, called Jcm for magnetic Jc, is usually obtained from the measured…
We present electrical transport, magnetization, and specific heat measurements on bulk MgB2 samples (T_{c} = 38.5 K) synthesized under 200 MPa pressure using a process based on hot isostatic pressing with cooling under pressure. The samples…
In this letter, we report the first successful fabrication of dense, metal-clad MgB2 superconductor wires as well as the first demonstration of high transport Jc of greater than 36,000 A/cm2 in MgB2. The fabrication technique that we…
Magnetic flux distribution across a high-temperature superconductor strip is measured using magneto-optical imaging at 15 K. Both the current-carrying state and the remanent state after transport current are studied up to the currents 0.97…
We prepared and characterized monofilamentary MgB2 wires with a mechanically reinforced composite sheath of Ta(Nb)/Cu/steel, which leads to dense filaments and correspondingly high transport currents up to Jc = 10^5 A/cm^2 at 4.2 K, self…
Magnetoresistance and radio frequency penetration depth techniques are used to study grain connectivity and broadening of superconducting transition. We study and compare these issues in clean polycrytalline samples of three different…
The structural properties of MgB2 superconductors have been analyzed by means of convergent-beam electron diffraction, high-resolution transmission-electron microscopy, and theoretical simulations. The MgB2 crystal has been identified to…
A trapped field of over 3 T has been measured at 17.5 K in a magnetised stack of two disc-shaped bulk MgB2 superconductors of diameter 25 mm and thickness 5.4 mm. The bulk MgB2 samples were fabricated by uniaxial hot pressing, which is a…
The dynamics of magnetic flux distributions across a YBaCuO strip carrying transport current is measured using magneto-optical imaging at 20 K. The current is applied in pulses of 40-5000 ms duration and magnitude close to the critical one,…
Grain boundaries (GBs) have been shown to limit critical current density, Jc, in YBa2Cu3O7 (YBCO) coated conductors. Here we use transport measurements and scanning Hall probe microscopy coupled with current reconstruction to demonstrate…
Magnetotransport measurements are presented on polycrystalline MgB2 samples. The resistive upper critical magnetic field reveals a temperature dependence with a positive curvature from Tc = 39.3 K down to about 20 K, then changes to a…
We have investigated the microstructure, normal-state electrical connectivity, and critical current density of ex-situ MgB2 polycrystalline bulks prepared by systematically varying the sintering conditions under low pressure. Samples heated…
The determination of the critical current density from magnetic hysteresis loops is widely used to characterize and compare superconducting samples. Magnetic hysteresis loops for tapes and single crystals depend on both the critical current…
The current transport in polycrystalline MgB$_2$ is strongly influenced by the intrinsic anisotropy of this superconductor. Untextured bulks and wires are macroscopically isotropic, but the grains retain their anisotropic properties and the…
We review recent measurements of upper (Hc2) and lower (Hc1) critical fields in clean single crystals of MgB2, and their anisotropies between the two principal crystallographic directions. Such crystals are far into the "clean limit" of…
We study the effect of 100 MeV Silicon and 200 MeV Gold ion irradiation on the inter and intra grain properties of superconducting thin films of Magnesium Diboride. Substantial decrease in inter-grain connectivity is observed, depending on…