Related papers: Superconducting MgB(2) films via precursor post-pr…
We report the growth and properties of epitaxial MgB2 thin films on (0001) Al2O3 substrates. The MgB2 thin films were prepared by depositing boron films via RF magnetron sputtering, followed by a post-deposition anneal at 850C in magnesium…
We have successfully prepared the MgB2 superconducting bulk and powdered materials by the method of combustion synthesis. The starting materials used in this study were powders of Mg and B. X-ray powder diffraction pattern was well assigned…
We report the effect of annealing on the superconductivity of MgB2 thin films as functions of the postannealing temperature in the range from 700 C to 950 C and of the postannealing time in the range from 30 min to 120 min. On annealing at…
We have studied the structural and superconducting properties of MgB$_2$ thin films made by pulsed laser deposition followed by in situ annealing. The cross-sectional transmission electron microscopy reveals a nanocrystalline mixture of…
MgB2 thick film was synthesized on the stainless steel substrate by the technique of hybrid physical-chemical vapor deposition (HPCVD), using Mg ingot and B2H6 as the raw materials. The film thickness is about 10 microns. The scanning…
Highly dense MgB2 policrystalline bulk materials, obtained by reactive liquid infiltration, have been characterized in their superconducting transport and magnetic properties in magnetic field and in a temperature range of interest for the…
Superconducting thin films of magnesium diboride (MgB$_2$) were prepared on MgO (001) substrate by a molecular beam epitaxy (MBE) method with the co-evaporation conditions of low deposition rate in ultra-high vacuum. The structural and…
Superconducting thick films (200$\mu$m-300$\mu$m) of YBCO have been fabricated successfully on MgO substrates by a new approach. The precursor powders (YBa2Cu3O7-$\delta$(Y123)+0.1molY2BaCuO5(Y211)) are placed between two MgO (10mm x 10mm)…
High quality MgB2 thin films have been obtained by pulsed laser deposition both on MgO and on Al2O3 substrates using different methods. In the standard two-step procedure, an amorphous precursor layer is deposited at room temperature…
We report the growth of high-quality epitaxial MgB2 thin films on (1102) Al2O3 and (001) SrTiO3 substrates by using a pulsed laser deposition technique. The thin films grown on Al2O3 substrates show a Tc of 39 K with a sharp transition…
The discovery of superconductivity at 39 K in magnesium diboride offers the possibility of a new class of low-cost, high-performance superconducting materials for magnets and electronic applications. With twice the critical temperature of…
Very thick, ~ 40 $\mu$m, clean, and highly textured MgB2 film was effectively grown on an Al2O3 substrate. The fabrication technique is by the hybrid physical-chemical vapor deposition (HPCVD) using B2H6 gas and Mg ingot as the sources. The…
The effect of water exposure on MgB2 is studied by submerging an 800 nm thick MgB2 film into deionized water at room temperature for 1 hour, 4 hours, 10 hours, and 15 hours, and by analyzing the resulting material using scanning electron…
ctical superconducting material for power-electric products such as superconducing tapes because of its high superconducting transition temperature (Tc) of 39 K and its high critical current density (Jc) under magnetic fields.…
The in situ annealing conditions of pulsed laser deposited MgB2 films were studied. The precursor films were deposited at 250 C from a stoichiometric MgB2 target in a 120mTorr Ar atmosphere. The films were then in situ annealed at a…
Superconductivity was discovered in heavily boron-doped diamond thin films deposited by the microwave plasma assisted chemical vapor deposition (MPCVD) method. Advantages of the MPCVD deposited diamond are the controllability of boron…
The electronic anisotropy in MgB2, is still a not completely clear topic; high quality c-oriented films are suitable systems to investigate this property. In this work we present our results on MgB2 superconducting thin films grown on MgO…
Highly smooth and c-axis oriented superconducting MgB2 thin films were prepared by pulsed laser deposition (PLD) with off-axis geometry. The films were deposited on Al2O3-C substrates perpendicularly aligned to a stoichiometric MgB2 target…
The fabrication, characterisation, and superconductivity of MgB2 thick films grown on stainless steel substrate were studied. XRD, SEM, and magnetic measurements were carried out. It was found that the MgB2 thick films can be fast formed by…
The MgB2 bulks were prepared by high energy milling of Mg and B powder. The correlations among milling times, microstructure and superconducting properties were investigated in MgB2 bulks. Samples were characterized by x-ray diffraction…