Related papers: Fully dense MgB_2 superconductor textured by hot d…
In the present paper we report an in-situ high-energy X-ray diffraction analysis of MgB2 tapes during the preparation process. The experiment was performed in a specifically designed furnace working in reducing atmosphere, compatible with…
Based on weakly-coupled anisotropic BCS theory, the dependence of energy gap and specific heat on temperature are evaluated for superconductor MgB$_2$, and the results are compared with experimental data.We show that the weak coupling…
The lattice parameters of MgB2 up to pressures of 8 GPa were determined using high-resolution x-ray powder diffraction in a diamond anvil cell. The bulk modulus, B0, was determined to be 151 +-5 GPa. Both experimental and first-principles…
Transport current values of 7.5 x 104 A/cm2 at 4.2 K and self-field are reported for MbB2-based tapes. MgB2 strands were formed by directly filling commercially available MgB2 powder into Nb-lined, monel tubes and wire drawing. The wires…
High-pressure (HP) synthesis and sintering are promising methods for manufacturing of the bulk MgB2 superconductive material. The available high-pressure apparatuses with 100 cm3 working volume can allow us to use the bulk MgB2 for…
Structural and superconducting properties of magnesium diboride thin films grown by pulsed laser deposition on zirconium diboride buffer layers were studied. We demonstrate that the ZrB2 layer is compatible with the MgB2 two step deposition…
Thin films of the recently discovered magnesium diboride (MgB2) intermetalic superconducting compound have been grown using a magnetron sputtering deposition technique followed by in-situ annealing at 830 C. High quality films were obtained…
We report the fabrication of MgB2 with bulk superconducting properties by conventional solid state methods at temperatures as low as 550 C. Mg deficiencies of the type Mg1-xB2 were tested. Tc was found to decrease by about 1K at large x,…
Nowadays the development of high-field magnets strongly relies on the performance of superconducting materials. Iron-based superconductors exhibit high upper critical fields and low electromagnetic anisotropy, making them particularly…
We report magnetic field dependent magnetization and microwave impedance measurements on a MgB2 superconductor prepared by high pressure synthesis. We find that the upper critical field is linearly dependent on temperature near Tc and the…
Since the discovery of MgB2 with Tc=39K, various metal diborides of MB2 have been intensively studied to find possible conventional high-temperature superconductors. A possible 2D structure of the metal diboride has been shown to be in the…
Carbon-doped magnesium diboride was fabricated from pre-reacted pure MgB2 by mechanical alloying. The sample set had excellent critical current densities Jc(8T,4.2K) ranging from 15-60 kA/cm2, depending on composition. Magneto-optical…
Current transport in polycrystalline magnesium diboride is highly non-uniform (percolative) due to the presence of secondary phases and also due to the intrinsic anisotropy of the material. The influence of secondary phases on the transport…
The effect of high magnetic fields on the current carrying properties of both MgB2 bulks and Fe-sheathed tapes was investigated following different thermal sequences. It is found that application of a large magnetic field during processing…
We have determined the structural properties of the superconducting compound MgB2 as a function of temperature from 11 K to 297 K and as a function of hydrostatic pressure up to 0.62 GPa using neutron powder diffraction. This compound, when…
Magnesium diboride MgB2 has been an extraordinarily hot research topic since the discovery of superconductivity below 40 K, due to the vast amount of unusual properties originating from the involvement in superconductivity of two sets of…
We characterize the superconducting state of phase pure polycrystalline samples of the new layered superconductor MgB$_2$ by specific heat measurements in magnetic fields up to 9 T. The characteristic jump at the superconducting transition…
BaFe2As2 (Ba-122) and (Ba0.6K0.4)Fe2As2 (K-doped Ba-122) powders were successfully synthesized from the elements using a reaction method, which incorporates a mechanochemical reaction using high-impact ball milling. Mechanically-activated,…
We report the effect of annealing on the superconductivity of MgB2 thin films as functions of the postannealing temperature in the range from 700 C to 950 C and of the postannealing time in the range from 30 min to 120 min. On annealing at…
We report the effect of the sintering temperature on the superconductivity of MgB2 pellets prepared under a high pressure of 3 GPa. The superconducting properties of the non-heated MgB2 in this high pressure were poor. However, as the…