Related papers: Magnetization studies on superconducting MgB$_2$ -…
Extensive measurements of the magnetization of superconducting single crystal samples of Ba0.6K0.4BiO3} have been made using SQUID and cantilever force magnetometry at temperatures ranging between 1.3 and 350 K and in magnetic fields from…
Transport and thermodynamic properties of a sintered pellet of the newly discovered $MgB_2$ superconductor have been measured to determine the characteristic critical magnetic fields and critical current densities. Both resistive transition…
Magnetization in DC magnetic fields and at different temperatures have been measured on the Li2Pd3B compound. This material was recently found to show superconductivity at 7-8K. Critical fields Hc1(0) and Hc2(0) have been determined to be…
Magnetisation and magnetoresistance measurements have been carried out on superconducting Ba1-xKxFe2As2 samples with x=0.40 and 0.50. From low field magnetization data carried out at different temperatures below TC, HC1 has been extracted.…
We present electrical transport, magnetization, and specific heat measurements on bulk MgB2 samples (T_{c} = 38.5 K) synthesized under 200 MPa pressure using a process based on hot isostatic pressing with cooling under pressure. The samples…
We report magnetic field dependent magnetization and microwave impedance measurements on a MgB2 superconductor prepared by high pressure synthesis. We find that the upper critical field is linearly dependent on temperature near Tc and the…
The upper critical field Hc2(T) of sintered pellets of the recently discovered MgB_2 superconductor was investigated by transport, ac susceptibility and dc magnetization measurements in magnetic fields up to 16 T covering a temperature…
The upper critical field Hc2(T) of sintered pellets of the recently discovered MgB_2 superconductor was investigated in magnetic fields up to 16 T. The upper critical field of the major fraction of the investigated sample was determined…
Magnetotransport measurements are presented on polycrystalline MgB2 samples. The resistive upper critical magnetic field reveals a temperature dependence with a positive curvature from Tc = 39.3 K down to about 20 K, then changes to a…
High-density bulk materials of a newly discovered 40K intermetallic MgB2 superconductor were prepared by high pressure sintering. Superconducting transition with the onset temperature of 39K was confirmed by both magnetic and resistive…
We present evidence of type I superconductivity in YbSb2 single crystals, from DC and AC magnetization, heat capacity and resistivity measurements. The critical temperature and critical field are determined to be $T_c\approx$ 1.3 K and…
The high field magnetization and magneto transport measurements are carried out to determine the critical superconducting parameters of MgB2-xCx system. The synthesized samples are pure phase and the lattice parameters evaluation is carried…
We have successfully prepared the MgB2 superconducting bulk and powdered materials by the method of combustion synthesis. The starting materials used in this study were powders of Mg and B. X-ray powder diffraction pattern was well assigned…
The specific heat C of a sintered polycrystalline sample of MgB2 with a bulk superconducting transition temperature Tc=36.7 K is measured as a function of the temperature (2-300 K) and magnetic field (0-16 T), together with magnetic…
Magnetic susceptibility, M-H plot, magnetoresistance and thermoelectric power of the RuSr2Eu1.5Ce0.5Cu2O10 superconductor are measured. Values of the magnetic transition temperature Tmag, superconductivity transition temperature Tc, upper…
We report the magnetic-field dependence of the irreversible magnetization of the recently discovered binary superconductor MgB$_{2}$. For the temperature region of $T< 0.9T_c$, the contribution of the bulk pinning to the magnetization…
We present magnetization measurements for the upper critical field $H_{c2}$ on aligned Na$_{x}$(H$_{3}$O)$_{z}$CoO$_{2}\cdot y$H$_{2}$O superconductors with magnetic field parallel to CoO$_2$ layers. The temperature-dependent part of the…
For a Ba_{0.63}K_{0.37}BiO_3 single crystal with T_c=31 K, H_{c1}=750 Oe at 5 K, and dimensions 3x3x1 mm^3, the temperature and field dependences of magnetic hysteresis loops have been measured within 5-25 K in magnetic fields up to 6…
The superconducting phase diagram of MgB2 was determined from magnetization, magneto-transport and the first single-crystal specific heat measurements. A zero-temperature in-plane coherence length of 8 nm is determined. The superconducting…
We report specific heat measurements at magnetic fields up to 20 T on the recently discovered superconductor SmFeAsO$_{0.85}$F$_{0.15}$. The B-T diagram of a polycrystalline SmFeAsO$_{0.85}$F$_{0.15}$ sample with T$_c$ = 46 K was…