Related papers: Carbon substitution effect in MgB$_2$
We analyze the data for the pressure and boron isotope effect on the temperature dependence of the magnetization near $T_{c}$. Invoking the universal scaling relation for the magnetization at fixed magnetic field it is shown that the…
We report the preparation of Mg1-xLixB2 compounds. Nearly single phased samples were obtained for x<0.3. The in-plane lattice parameter a decreases with Li doping, while the lattice parameter c does not show obvious change. The…
A new method for preparation of single crystals of the superconducting intermetallic MgB2 compound from a Mg-Cu-B melt flux is presented. The high vapour pressure of Mg at elevated temperature is a serious challenge of the preparation…
``Sub-meV'' resolution photoemission spectroscopy was used to study carbon-substitution dependence on the multiple superconducting gap of Mg(B$_{1 - x}$C$_{x})_{2}$. Two features corresponding to $\sigma $ and $\pi $ gaps are clearly…
Carbon-substituted MgB2 single crystals, Mg(B_1-xC_x)_2 of 0.3-1.0 mm size were grown for x=0.02-0.15 by a high-pressure technique. The doping dependence of lattice constants studied in a range of x=0.0-0.2 shows a monotonic decrease in a,…
Superconducting MgB(2) films with Tc = 38.6 K were prepared using a precursor-deposition, ex-situ post-processing approach. Precursor films of boron, ~0.5 micrometer thick, were deposited onto Al(2)O(3) (102) substrates by e-beam…
We studied the influence of sample preparation and defects in the superconducting properties samples using atomic ratios of Mg:B=1:1 and Mg:B=1:2. Samples were characterized by SEM, and XRD, and the magnetization properties were examined in…
We report the preparation of Mg$_{1-x}$B$_{2}$ (0$\le$x$\le$0.5) compounds with the nominal compositions. Single phase MgB$_{2}$ was obtained for x=0 sample. For 0$<$x$\le$0.5, MgB$_{4}$ coexists with "MgB$_{2}$" and the amount of MgB$_{4}$…
The pressure effect on the superconducting transition temperature of MgB2 has been determined using gas pressure up to 1 GPa. The transition temperature Tc was found to decrease linearly at a constant rate over the whole pressure range. The…
MgB2 superconducting wires with critical temperature Tc approaching 40 K were used for preparation of MgB2/Ag and MgB2/In junctions. The differential conductance vs. voltage characteristics of N-S junctions exhibit clear contribution of…
The effect of the 16O-->18O substitution on the superconducting transition temperatures Tc of NaxCoO2.yH2O has been studied for several sets of samples. Each set has two kinds of samples, one with the oxygen sites in the CoO2 layers filled…
We report on measurements of the specific heat of the recently discovered superconductor MgB$_2$ in the temperature range between 3 and 220 K. Based on a modified Debye-Einstein model, we have achieved a rather accurate account of the…
We have constructed MgB2/Pb planar junctions for both temperature and field dependence studies. Our results show that the small gap is a true bulk property of MgB2 superconductor, not due to surface effects. The temperature dependence of…
A recent work has demonstrated that MoB$_2$, transforming to the same structure as MgB$_2$ ($P6/mmm$), superconducts at temperatures above 30 K near 100 GPa [C. Pei $et$ $al$. Natl. Sci. Rev., nwad034 (2023)], and Nb-substitution in MoB$_2$…
The effect of Carbon isotope substitution on T_c in the intermetallic perovskite superconductor MgCNi_3 is reported. Four independent groups of samples were synthesized and characterized. The average T_c for the Carbon-12 samples was found…
With the motivation of searching for new superconductors in the Mg-B system, we performed ab initio evolutionary searches for all the stable compounds in this binary system in the pressure range of 0-200 GPa. We found previously unknown,…
We report resistivity and magnetization of single crystal MgB2, focusing on the broadening of superconducting (SC) transition in magnetic fields. In-plane and out-of-plane resistivity indicate that the broadening of superconducting…
We show that the specific heat of the superconductor MgB_2 (MgB2) in zero field, for which significant non-BCS features have been reported, can be fitted, essentially within experimental error, over the entire range of temperature to T_c by…
Point-contact spectroscopy measurements on magnesium diboride reveal the existence of two superconducting energy gaps closing at the same transition temperature in line with the multiband model of superconductivity. The sizes of the two…
In-plane electrical transport properties of MgB2 single crystals grown under high pressure of 4-6 GPa and temperature of 1400-1700oC in Mg-B-N system have been measured. For all specimens we found sharp superconducting transition around…