Related papers: Carbon substitution effect in MgB$_2$
Dense pure and doped (Mg1-xAx)B2 samples with A = Na, Ca, Cu, Ag, Zn and Al were synthesized at high pressure - high temperature in a multi anvils press (3.5-6 GPa, 900-1000C) for x up to 0.20. They were studied by x-ray diffraction,…
According to the crystal structure of MgB$_{2}$ and band structure calculations quasi-two-dimensional (2D) boron planes are responsible for the superconductivity. We report on critical fields and resistance measurements of 30 nm thick…
A polycrystalline sample of the MgB_2 superconductor was investigated by measurements of the electrical resistivity, the thermopower and the thermal conductivity in the temperature range between 1.8K and 300K in zero magnetic field. The…
We investigate the influence of carbon-ion irradiation on the superconducting critical properties of MgB$_2$ thin films. MgB$_2$ films of two thicknesses viz. 400 nm (MB400nm) and 800 nm (MB800nm) were irradiated by 350 keV C ions having a…
We synthesized single crystalline and policrystalline MgB_2 under ambient pressures. The single crystals of MgB_2 were of good quality, where the crystal structure refinements were successfully converged with R = 0.020. The specific heat of…
We have determined the structural properties of the superconducting compound MgB2 as a function of temperature from 11 K to 297 K and as a function of hydrostatic pressure up to 0.62 GPa using neutron powder diffraction. This compound, when…
The physical property characterization of Al doped Mg1-xAlxB2 system with x = 0.0 to 0.50 is reported. The results related to phase formation, structural transition, resistivity R(T) and magnetization M(T) measurements are discussed in…
Density functional calculations are used to investigate the effects of partial substitutional alloying of the B site in MgB2 with C and Be alone and combined with alloying of the Mg site with Cu. The effect of such substitutions on the…
The effect of high pressure on structural and electronic properties of the novel superconductor \MB has been calculated using the full-potential linearized augmented-plane-wave method. Despite the layered crystal structure of \MB nearly…
We report the effect of the sintering temperature on the superconductivity of MgB2 pellets prepared under a high pressure of 3 GPa. The superconducting properties of the non-heated MgB2 in this high pressure were poor. However, as the…
Measurements of the superconducting transition temperature Tc have been performed by the inductive method on MgB2 at pressures up to 28 GPa. Tc decreases with applied pressure, exhibiting a cusp at about 9 GPa. We interpret the appearance…
Sintered powders and wires of superconducting $MgB_2$ have been fabricated under a variety of conditions in order to determine details of the diffusion of the $Mg$ into $B$ and to study the types of defects that arise during growth. For…
The superconducting phase diagram of MgB2 was determined from magnetization, magneto-transport and the first single-crystal specific heat measurements. A zero-temperature in-plane coherence length of 8 nm is determined. The superconducting…
Successful replacement of B by C in the series MgB2-xCx for values of x upto 0.3 are reported. Resistivity and ac susceptibility measurements have been carried out in the samples. Solubility of carbon, inferred from the observed change in…
Considerable excitement has been caused recently by the discovery that the binary boride system with stoichiometry MgB2 is superconducting at the remarkably high temperature of 39 K (1). This potentially opens the way to even higher Tc…
Magnetic ions (Mn) were substituted in MgB_2 single crystals resulting in a strong pair-breaking effect. The superconducting transition temperature, T_c, in Mg_{1-x}Mn_xB_2 has been found to be rapidly suppressed at an initial rate of 10…
Far-infrared reflectance of a MgB2 film has been measured by Fourier-transform spectroscopy for frequencies 10 cm^{-1}<\nu <4000 cm^{-1} above and below the superconducting transition. The data provide clear experimental evidence for the…
The variation of TC in MgB2 has been systematically investigated for monovalent cation substitution in Mg1-xLixB2 and in Mg1-xCuxB2 and simultaneous cation and Carbon substitution in Mg0.80Li0.20B2-xCx and Mg0.95Cu0.05B2-xCx using dc…
Composites consisting of MgB2 and Al, 11% by volume, undergo a transition to superconductivity onset at TC = 38 K, close to the value reported for pure MgB2. The transition appears to have broadened, as determined by both magnetic and…
Recently it was discovered that, under elevated pressures, MoB$_2$ exhibits superconductivity at a critical temperature, $T_c$, as high as 32 K. The superconductivity appears to develop following a pressure-induced structural transition…