Related papers: Absence of Superconductivity in BeB2
We report the preparation method of, and boron isotope effect for MgB$_2$, a new binary intermetallic superconductor with a remarkably high superconducting transition temperature $T_c$($^{10}$B) = 40.2 K. Measurements of both temperature…
Superconducting MgB2 was synthesized in a stainless steel tube which compressed by pulsed magnetic field. The temperature dependence of diamagnetic moment m(T) was investigated and the pinning potential was determined
Single crystals of MgB2 and Mg(B1-xCx)2 have been grown using cubic anvil technique. Tc values vary in a wide range (39-9 K) with carbon content varying from 0 up to 16%. Using SiC as the precursor leads to C and not to Si substituted…
Superconductivity was recently observed in the iron-arsenic-based compounds with a superconducting transition temperature (Tc) as high as 56K [1-7], naturally raising comparisons with the high Tc copper oxides. The copper oxides have…
We measured the in-plane optical conductivity of a nearly optimally doped (Ba,K)Fe2As2 single crystal with Tc = 39.1 K. Upon entering the superconducting state the optical conductivity below ~20 meV vanishes, strongly suggesting a fully…
A ternary compound, MgPtSi, was synthesized by solid-state reaction. An examination of the compound by powder X-ray diffraction revealed that it crystallizes in the orthorhombic TiNiSi-type structure with the Pnma space group. The structure…
La2O2Bi2Pb2S6 is a layered Bi-based oxychalcogenide with a thick four-layer-type conducting layer. Although La2O2Bi2Pb2S6 is a structural analogue of La2O2Bi3AgS6, which is a superconductor, insulating behavior has been observed in…
We have determined the structural properties of the superconducting compound MgB2 as a function of temperature from 11 K to 297 K and as a function of hydrostatic pressure up to 0.62 GPa using neutron powder diffraction. This compound, when…
We have synthesized single crystals of K1.00(3)Fe0.85(2)Ag1.15(2)Te2.0(1). The materials crystallizes in the ThCr2Si2 structure with I4/mmm symmetry and without K and Fe/Ag deficiencies, unlike in KxFe2-ySe2 and KxFe2-yS2. In contrast to…
Detailed magneto-transport data on dense wires of $MgB_2$ are reported for applied magnetic fields up to 18 T. The temperature and field dependencies of the electrical resistivity are consistent with $MgB_2$ behaving like a simple metal and…
Measurements of the superconducting transition temperature Tc have been performed by the inductive method on MgB2 at pressures up to 28 GPa. Tc decreases with applied pressure, exhibiting a cusp at about 9 GPa. We interpret the appearance…
Superconducting bulk properties of ternary Nb2 BN are confirmed and are described by means of magnetization, electronic transport and specific-heat measurements. BCS conventional super- conductivity is found with Tc = 4.4 K. Critical fields…
A polycrystalline sample of the MgB_2 superconductor was investigated by measurements of the electrical resistivity, the thermopower and the thermal conductivity in the temperature range between 1.8K and 300K in zero magnetic field. The…
We report on study of the electronic anisotropy of the newly discovered MgB2 superconductor using the in-plane resistivity measurements in magnetic field applied perpendicular and parallel to Mg and B planes of MgB2 single crystals. The…
We successfully synthesized the BaPt$_2$As$_2$ single crystals and studied their structural and physical properties at low temperatures. BaPt$_2$As$_2$ crystallizes in the CaBe$_2$Ge$_2$-type tetragonal structure (P4/nmm) at room…
We report on existence of superconductivity in YIr2Si2 and LaIr2Si2 compounds in relation to crystal structure. The two compounds crystallize in two structural polymorphs, both tetragonal. The high temperature polymorph (HTP) adopts the…
We report the synthesis, magnetic susceptibility and crystal structure analysis for NbB2+x (x = 0.0 to 1.0) samples. The study facilitates in finding a correlation among the lattice parameters, chemical composition and the superconducting…
The MgB2 superconductor synthesized in a flowing argon atmosphere using nanometer magnesium powder as the raw materials, denoted as Nano-MgB2, has been studied by the technique of in-situ high temperature resistance measurement (HT-RT…
We report specific heat measurements in neutron irradiated MgB2 samples, for which the critical temperature has been suppressed down to 8.5 K, but the superconducting transition remains extremely sharp, indicative of a defect structure…
We report on tunneling spectroscopy experiments in small grains of the new binary intermetallic superconductor MgB2. Experiments have been performed at 2.5 K using a low temperature scanning tunneling microscope. Good fit to the BCS model…