We present the crystal structure and low temperature electronic transport properties of the intermetallic commonly known as BeB_2. In contrast to the much simpler AlB_2-type structure of the 39K superconductor MgB_2, BeB_2 forms a complex…
We prepared MgB$_{2-x}$Be$_{x}$ ($x=0$, 0.2, 0.3, 0.4, and 0.6) samples where B is substituted with Be. MgB$_{2}$ structure is maintained up to $x=0.6$. In-plane and inter-plane lattice constants were found to decrease and increase,…
We have performed high-resolution photoemission spectroscopy on MgB2 and observed opening of a superconducting gap with a narrow coherent peak. We found that the superconducting gap is s-like with the gap value of 4.5 meV at 15 K. The…
Considerable excitement has been caused recently by the discovery that the binary boride system with stoichiometry MgB2 is superconducting at the remarkably high temperature of 39 K (1). This potentially opens the way to even higher Tc…
Superconductivity was found for a rhenium boride Re3B at Tc=4.7 K and for ReB2 with Tc in the range from 4.5 to 6.3 K depending on the boron concentrations. Both compounds have the structure different from that of the simple layered…
Magnetic properties of TaB$_{2}$ were studied by means of DC and AC susceptibility measurements. It has been found that the compound becomes superconducting at T$_{c}$ = 9.5 K. From upper critical field measurements the superconducting…
The basic magnetic and electronic properties of most binary compounds have been well known for decades. Therefore the recent announcement of superconductivity at 39 K in the simple binary ceramic compound MgB2 is surprising. This compound,…
Intensive and extensive searches for superconductivity in materials iso-structural, iso-electronic and iso-valent with magnesium diboride, MgB2, have not produced superconductors with Tc close to 39K. Recently, we proposed lithium magnesium…
The search for superconductivity in materials iso-structural and iso-valent with magnesium diboride, MgB2, has not yielded any results close enough to the 39K Tc of MgB2. Lithium magnesium nitride, LiMgN, resembles MgB2 in that they both…
This review paper illustrates the main normal and superconducting state properties of magnesium diboride, a material known since early 1950's, but recently discovered to be superconductive at a remarkably high critical temperature Tc=40K…
The search for materials similar to magnesium diboride, MgB2, based on structure and electronic similarity did not produce close enough superconductors in terms of Tc. Changing the search to iso-electronic and iso-atomic number equivalents…
WBe2, which occurs in space group 194, with hexagonal symmetry P63/mmc, is prepared by arc-melting at temperatures above 2200 C, where Be vapor loss is significant. This study is motivated by recent work on MoB2 and WB2, both…
A bulk diluted magnetic semiconductor was found in the K and Mn co-doped BaCd2As2 system. Different from recently reported tetragonal ThCr2Si2-structured II-II-V based(Ba,K)(Zn,Mn)2As2, the Ba1-yKyCd2-xMnxAs2 system has a hexagonal…
We report the synthesis and electronic properties of polycrystalline samples of Zr6MBi2 (M = Ru and Fe) crystallizing in the hexagonal Zr6CoAl2-type structure. Based on their electrical resistivity, magnetization, and heat capacity data,…
The results of electrical resistance (1.4 - 300 K), magnetization (2-300 K) and heat-capacity (2 - 50 K) measurements in Y$_2$PdGe$_3$, found to crystallize in a AlB$_2$-derived hexagonalstructure, are reported. The results establish that…
We report synthesis, structure/micro-structure, resistivity under magnetic field [R(T)H], Raman spectra, thermoelectric power S(T), thermal conductivity K(T), and magnetization of ambient pressure argon annealed polycrystalline bulk samples…
We report that the ternary MgB2-xCx compounds adopt an isostructural AlB2-type hexagonal structure in a relatively small range of nominal carbon concentration, x<0.1. The lattice parameter a decreases almost linearly with increasing carbon…
The system MgxB2 has been investigated to investigate possible nonstoichiometry in MgB2. When synthesized at 850oC, MgB2 is a line compound with a possible Mg vacancy content of about 1%. Small changes in lattice constants as a function of…
The recent discovery of superconductivity at ~39 K in MgB2, by Nagamatsu et al. establishes this simple binary compound as having the highest bulk superconducting transition temperature, Tc, of any non-copper-oxide material. Much of the…
Superconductivity is observed with critical temperatures near 9K in the tetragonal compound Mo5PB2. This material adopts the Cr5B3 structure type common to supercondcuting Nb5Si3-xBx, Mo5SiB2, and W5SiB2, which have critical temperatures of…