Magnetotransport measurements are presented on polycrystalline MgB2 samples. The resistive upper critical magnetic field reveals a temperature dependence with a positive curvature from Tc = 39.3 K down to about 20 K, then changes to a…
A polycrystalline sample of the MgB_2 superconductor was investigated by measurements of the electrical resistivity, the thermopower and the thermal conductivity in the temperature range between 1.8K and 300K in zero magnetic field. The…
$MgB_2$ becomes superconducting just below 40 K. Whereas porous polycrystalline samples of $MgB_2$ can be synthesized from boron powders, in this letter we demonstrate that dense wires of $MgB_2$ can be prepared by exposing boron filaments…
Transport and thermodynamic properties of a sintered pellet of the newly discovered $MgB_2$ superconductor have been measured to determine the characteristic critical magnetic fields and critical current densities. Both resistive transition…
The upper critical field Hc2(T) of sintered pellets of the recently discovered MgB_2 superconductor was investigated in magnetic fields up to 16 T. The upper critical field of the major fraction of the investigated sample was determined…
The upper critical field Hc2(T) of sintered pellets of the recently discovered MgB_2 superconductor was investigated by transport, ac susceptibility and dc magnetization measurements in magnetic fields up to 16 T covering a temperature…
We present electrical transport, magnetization, and specific heat measurements on bulk MgB2 samples (T_{c} = 38.5 K) synthesized under 200 MPa pressure using a process based on hot isostatic pressing with cooling under pressure. The samples…
We report on the synthesis and measurements of the temperature dependence of resistivity, R(T), the penetration depth, l(T), and upper critical magnetic field, Hc2(T), for polycrystalline samples of dodecaboride ZrB12 and diboride MgB2. We…
We report magnetic field dependent magnetization and microwave impedance measurements on a MgB2 superconductor prepared by high pressure synthesis. We find that the upper critical field is linearly dependent on temperature near Tc and the…
High-density bulk materials of a newly discovered 40K intermetallic MgB2 superconductor were prepared by high pressure sintering. Superconducting transition with the onset temperature of 39K was confirmed by both magnetic and resistive…
We have grown the MoAs$_2$ single crystal which crystallizes in a monoclinic structure with C2/m space group. Transport measurements show that MoAs$_2$ displays a metallic behavior at zero field and undergoes a metal-to-semiconductor…
We report synthesis, structure/micro-structure, resistivity under magnetic field [R(T)H], Raman spectra, thermoelectric power S(T), thermal conductivity K(T), and magnetization of ambient pressure argon annealed polycrystalline bulk samples…
MgB2 hollow wires have been produced with a new technique which uses a conventional wire manufacturing process but is applied to composite billets containing the elemental B and Mg precursors in an appropriate shape. The technique has been…
We report on syntheses and electron transport properties of polycrystalline samples of diborides (AB2) with different transition metals atoms (A=Zr,Nb,Ta). The temperature dependence of resistivity, \rho(T), and ac susceptibility of these…
We prepared and characterized monofilamentary MgB2 wires with a mechanically reinforced composite sheath of Ta(Nb)/Cu/steel, which leads to dense filaments and correspondingly high transport currents up to Jc = 10^5 A/cm^2 at 4.2 K, self…
We report here the magneto-transport properties of the newly synthesized Heusler compound Cr2NiGa which crystallizes in a disordered cubic B2 structure belonging to Pm-3m space group. The sample is found to be paramagnetic down to 2 K with…
We report measurements of the transport and the magnetic properties of high-quality, sub-millimeter-sized MgB2 single crystals with clear hexagonal-plate shapes. The low-field magnetization and the magnetic hysteresis curves show the vortex…
Magnetization studies have been carried out on superconducting MgB$_2$ (T$_c$=37K) in the temperature range of 2-50K and in magnetic field up to 5 Tesla. From these measurements, values of the lower critical field H$_c1$(0), upper critical…
We synthesized single crystalline and policrystalline MgB_2 under ambient pressures. The single crystals of MgB_2 were of good quality, where the crystal structure refinements were successfully converged with R = 0.020. The specific heat of…
Electrolysis was carried out on fused mixtures of MgCl2, NaCl, KCl and MgB2O4 under an Ar flow at 600C. Electrical resistivity measurements for the grown deposits show an onset of superconducting transition at 37 K in the absence of applied…