Related papers: Effect of sintering temperature under high pressur…
Nanocrystalline MgB$_2$ produced by mechanical alloying has been shown to exhibit enhanced superconducting properties such as increased pinning and higher critical currents. However, the effects of the synthesis process on the intrinsic…
We report the temperature- and magnetic-field-dependent resistivity of MgB2 sintered at high temperature and high pressure condition. The superconducting transition width for the resistivity measurement was about 0.4 K, and the low-field…
High-density bulk materials of a newly discovered 40K intermetallic MgB2 superconductor were prepared by high pressure sintering. Superconducting transition with the onset temperature of 39K was confirmed by both magnetic and resistive…
We present electrical transport, magnetization, and specific heat measurements on bulk MgB2 samples (T_{c} = 38.5 K) synthesized under 200 MPa pressure using a process based on hot isostatic pressing with cooling under pressure. The samples…
The review considers bulk MgB2-based materials in terms of their structure, superconducting and mechanical properties. Superconducting transition temperatures of 34.5-39.4 K, critical current densities of 1.8-1.0 x E6 A/sq.cm in self field…
We synthesized single crystalline and policrystalline MgB_2 under ambient pressures. The single crystals of MgB_2 were of good quality, where the crystal structure refinements were successfully converged with R = 0.020. The specific heat of…
Measurements of the superconducting transition temperature Tc have been performed by the inductive method on MgB2 at pressures up to 28 GPa. Tc decreases with applied pressure, exhibiting a cusp at about 9 GPa. We interpret the appearance…
Based on DC magnetization measurements, the temperature dependencies of the trapped magnetic field have been calculated for two MgB2 samples prepared by two different techniques: the high-pressure sintering and the hot pressing.…
High-pressure (HP) synthesis and sintering are promising methods for manufacturing of the bulk MgB2 superconductive material. The available high-pressure apparatuses with 100 cm3 working volume can allow us to use the bulk MgB2 for…
We have successfully prepared the MgB2 superconducting bulk and powdered materials by the method of combustion synthesis. The starting materials used in this study were powders of Mg and B. X-ray powder diffraction pattern was well assigned…
Superconductivity with Tc above 9 K was found in metal-deficient NbB2 prepared under 5 GPa, while no clear superconductivity was observed down to 3 K in stoichiometric NbB2. The superconductivity was observed above x = 0.04 in Nb1-xB2. and…
We study the effects of pressure on the electron-phonon interaction in MgB_2 using density-functional-based methods. Our results show that the superconductivity in MgB_2 vanishes by 100 GPa, and then reappears at higher pressures. In…
The pressure effect on the superconducting transition temperature of MgB2 has been determined using gas pressure up to 1 GPa. The transition temperature Tc was found to decrease linearly at a constant rate over the whole pressure range. The…
In this paper we have investigated the effects of sintering time and temperature on the formation and critical current densities of Fe-clad MgB2 wires. MgB2 wires were fabricated using the powder-in-tube process and sintered for different…
Transport and thermodynamic properties of a sintered pellet of the newly discovered $MgB_2$ superconductor have been measured to determine the characteristic critical magnetic fields and critical current densities. Both resistive transition…
Highly dense MgB2 policrystalline bulk materials, obtained by reactive liquid infiltration, have been characterized in their superconducting transport and magnetic properties in magnetic field and in a temperature range of interest for the…
In-plane electrical transport properties of MgB2 single crystals grown under high pressure of 4-6 GPa and temperature of 1400-1700oC in Mg-B-N system have been measured. For all specimens we found sharp superconducting transition around…
The microstructure of the MgB2 superconductor sintered at high temperature under a high pressure of about 3 GPa was investigated by using a high-resolution transmission electron microscope (HRTEM). The TEM images did not show any pores in…
Dense pure and doped (Mg1-xAx)B2 samples with A = Na, Ca, Cu, Ag, Zn and Al were synthesized at high pressure - high temperature in a multi anvils press (3.5-6 GPa, 900-1000C) for x up to 0.20. They were studied by x-ray diffraction,…
The MgB2 bulks were prepared by high energy milling of Mg and B powder. The correlations among milling times, microstructure and superconducting properties were investigated in MgB2 bulks. Samples were characterized by x-ray diffraction…