Related papers: Geometry-Dependent Crack Interaction and Toughenin…
A planar crack generically segments into an array of "daughter cracks" shaped as tilted facets when loaded with both a tensile stress normal to the crack plane (mode I) and a shear stress parallel to the crack front (mode III). We…
The growth dynamics of a single crack in a heterogeneous material under subcritical loading is an intermittent process; and many features of this dynamics have been shown to agree with simple models of thermally activated rupture. In order…
Crack advance from short or long pre-cracks is predicted by the progressive failure of a cohesive zone in a strain gradient, elasto-plastic solid. The presence of strain gradients leads to the existence of an elastic zone at the tip of a…
We present a systematic study of the effect of crack blunting on subsequent crack propagation and dislocation emission. We show that the stress intensity factor required to propagate the crack is increased as the crack is blunted by up to…
The scaling laws describing the roughness development of crack surfaces are incorporated into the Griffith criterion. We show that, in the case of a Family-Vicsek scaling, the energy balance leads to a purely elastic brittle behavior. On…
Various kinds of heterogeneity in solids including atomistic discreteness affect the fracture strength as well as the failure dynamics remarkably. Here we study the effects of an initial crack in a discrete model for fracture in…
We investigate numerically the dynamics of crack propagation along a weak plane using a model consisting of fibers connecting a soft and a hard clamp. This bottom-up model has previously been shown to contain the competition of two crack…
The modeling of crack propagation in a heterogeneous material using a phase field model is studied numerically in a simple test case: the crack meets a wedge of higher fracture energy. It is shown that when the crack cannot enter the wedge,…
The propagation of (planar) cracks in a heterogeneous brittle material characterized by a random field of toughness is considered, taking into account explicitly the effect of the crack front roughness on the local stress intensity factor.…
We investigate fracture toughness of architected interfaces and their ability to maintain structural integrity and provide stable damage propagation conditions beyond the failure load. We propose theoretical and numerical frameworks to…
Per weight graphene is stronger than steel, but because graphene is so thin, it breaks and evidently forms cracks during handling, particularly when supporting polymers are not used for transfer. In this paper, the parameter rupture index…
We investigate crack propagation in a simple two-dimensional visco-elastic model and find a scaling regime in the relation between the propagation velocity and energy release rate or fracture energy, together with lower and upper bounds of…
A theoretical study based on dimensional analysis and fractal geometry of crack profiles is proposed to establish the relation between their fractal dimension D (1<D<2) and the parameters defining the fatigue crack propagation rate. The…
We investigate the fracture behavior of pre-cracked triangular beam-lattices whose elements have failure stresses drawn from a Weibull distribution. Through a statistical analysis and numerical simulations, we identify and verify the…
The interaction of an interfacial crack with small impurities is analysed on the basis of an asymptotic formula derived by the authors. The interaction between the main crack and the defects (e.g. small cracks or inclusions) is described…
Defects in solid commonly limit mechanical performance of the material. However, recent measurements reported that the extraordinarily high strength of graphene is almost retained with the presence of grain boundaries. We clarify in this…
In this work, distortion gradient plasticity is used to gain insight into material deformation ahead of a crack tip. This also constitutes the first fracture mechanics analysis of gradient plasticity theories adopting Nye's tensor as primal…
Through controlled numerical simulations in a one dimensional fiber bundle model with local stress concentration, we established an inverse correlation between the strength of the material and the cracks which grow inside it - both the…
Crack fronts deform due to heterogeneities, and inspecting these deformations can reveal local variations of material properties, and help predict out of plane damage. Current models neglect the influence of a finite dissipation…
As a consequence of shearing, wing cracks can emerge from pre-existing fractures. The process involves the interaction of sliding of the existing fracture surfaces and the tensile material failure that creates wing cracks. This work devises…