Segregation to defects, in particular to grain boundaries (GBs), is an unavoidable phenomenon leading to changed material behavior over time. With the increase of available computational power, unbiased quantum-mechanical predictions of…
Nanocrystalline (NC) materials are intrinsically unstable against grain growth. Significant research efforts have been dedicated to suppressing the grain growth by solute segregation, including the pursuit of a special NC structure that…
The accumulation of helium bubbles at grain boundaries (GBs) critically degrades the mechanical integrity of structural materials in nuclear reactors. While GBs act as sinks for radiation-induced defects, their inherent structural…
Previous studies demonstrate that grain-boundary sliding could accelerate creep rate and give rise to large internal stresses that can lead to damage development, e.g. formation of wedge cracks. The present study provides more insight into…
A numerical investigation of grain-boundary (GB) grooving by means of the Level Set (LS) method is carried out. GB grooving is emerging as a key element of electromigration drift in polycrystalline microelectronic interconnects, as…
We show that molecular dynamics (MD) simulations are capable of reproducing the drag of solute segregation atmospheres by moving grain boundaries (GBs). Although lattice diffusion is frozen out on the MD timescale, the accelerated GB…
Radiation-induced segregation (RIS) poses a significant challenge for ferritic Fe-Cr alloys under irradiation, as it can compromise mechanical integrity and increase susceptibility to intergranular corrosion. Yet, the mechanisms governing…
This study investigates the boundary migration mechanisms near the sample surface of recrystallizing grains in high-purity Al subjected to cryogenic rolling. Local strain and stress tensors were characterized during \textit{in situ}…
It was recently reported that segregation of Zr to grain boundaries (GB) in nanocrystalline Cu can lead to the formation of disordered intergranular films [1,2]. In this study we employ atomistic computer simulations to study how the…
The study of defect phases is important for designing nanostructured metals and alloys. Grain boundaries (GBs) form one class of defects that directly influence materials properties, such as deformability and strength. At the same time,…
Interfacial segregation can stabilize grain structures and even lead to grain boundary complexion transitions. However, understanding of the complexity of such phenomena in polycrystalline materials is limited, as most studies focus on…
The macroscopic behavior of polycrystalline materials is influenced by the local variation of properties caused by the presence of impurities and defects. The effect of these impurities at the atomic scale can either embrittle or strengthen…
The grain boundary (GB) microstructure influences and is influenced by the development of residual stresses during synthesis of polycrystalline thin films. Recent studies have shown that the frustration between the preferred growth…
Grain boundaries (GBs) are central defects for describing polycrystalline materials, and playing major role in a wide-range of physical properties of polycrystals. Control over GB kinetics provides effective means to tailor polycrystal…
Grain-boundary (GB) local stress is central to the initiation and evolution of long-term creep damage in polycrystalline superalloys. Owing to the high-dimensional nonlinear relationships between the GB stress response and multiple…
Hydrogen grain boundary (GB) trapping is widely accepted as the main cause for hydrogen induced intergranular failure. Several studies were conducted to unveil the role of GBs on hydrogen transport; however, a clear understanding is yet to…
Grain boundary (GB) segregation models are derived for multi-principal element and high-entropy alloys (MPEAs and HEAs). Differing from classical models where one component is taken as solvent and others are considered solutes, these models…
Amorphous grain-boundary (GB) complexions in thermally stable nanocrystalline alloys are commonly assumed to be structurally homogeneous, yet their disordered nature makes them susceptible to local short-range ordering (SRO). The influence…
Engineering structure of grain boundaries (GBs) by solute segregation is a promising strategy to tailor the properties of polycrystalline materials. Theoretically it has been suggested that solute segregation can trigger phase transitions…
Grain boundary (GB) migration stands as a linchpin process governing microstructural evolution in polycrystalline materials. Over the past decade, the concept of shear coupling, quantified through the shear coupling factor, has transformed…