Recently, superconductivity at high temperatures has been observed in bulk La$_3$Ni$_2$O$_{7-{\delta}}$ under high pressure. However, the attainment of high-purity La$_3$Ni$_2$O$_{7-{\delta}}$ single crystals, exhibiting controlled and…
Bulk single crystals of SrPt3P have been grown for the first time by a self-flux method at 2 GPa and 1500 {\deg}C using the cubic-anvil, high-pressure and high-temperature technique. The grown black crystals were found to have either a…
Nickelates have attracted enormous attention since the discovery of high-temperature superconductivity in La3Ni2O7 under high pressure. However, whether superconducting nickelate single crystals can be prepared at ambient pressure remains…
The recent discovery of superconductivity in pressurized Ruddlesden-Popper (RP) nickelates has provided new perspectives on the mechanism of high-temperature superconductivity. Up to now, most experiments concentrated on the…
Single crystals of PrNiO3 were grown under an oxygen pressure of 295 bar using a unique high-pressure optical-image floating zone furnace. The crystals, with volume in excess of 1 mm3, were characterized structurally using single crystal…
We report the first single crystal growth of the correlated metal LaNiO3 using a high-pressure optical-image floating zone furnace. The crystals were studied using single crystal/powder x-ray diffraction, resistivity, specific heat, and…
For the first time Lu$_2$S$_3$ (undoped and Pr-doped) single crystals were successfully grown from melt using micro-pulling-down (mPD) technique. Customization of halide mPD apparatus allowed us to grow rod-shaped (\O 2 mm and length around…
Millimeter-sized single crystals of LaFeAsO, LaFeAsO1-xFx, and LaFe1-xCoxAsO were grown in NaAs flux at ambient pressure. The detailed growth procedure and crystal characterizations are reported. The as-grown crystals have typical…
We explore the layered palladium oxides La$_2$PdO$_4$, LaPdO$_2$ and La$_4$Pd$_3$O$_8$ via ab initio calculations. La$_2$PdO$_4$, being low spin $d^8$, is quite different from its high spin nickel analog. Hypothetical LaPdO$_2$, despite its…
The discovery of superconductivity with onset temperature of ~80 K in pressurized bilayer Ruddlesden-Popper La3Ni2O7-d has attracted much attention. Despite intense research, determination of the exact oxygen content and understanding of…
Single crystals of the metallic Ruddlesden-Popper trilayer nickelates R$_4$Ni$_3$O$_{10}$ (R=La, Pr) were successfully grown using an optical-image floating zone furnace under oxygen pressure (pO$_2$) of 20 bar for La$_4$Ni$_3$O$_{10}$ and…
Advancement of technologies relies on discovery of new materials with emerging physical properties that are determined by their crystal structures. Ruddlesden-Popper (R-P) phases with formula of $A_{n+1}$$B_n$$X_{3n+1}$ (n=1,2,3...) are…
Recently, the Ruddlesden-Popper bilayer nickelate $La_3Ni_2O_7$ has emerged as a superconductor with a transition temperature ($T_c$) of approximately 80 K above 14 GPa (Refs. 1-3). Achieving higher $T_c$ in nickelate superconductors, along…
We synthesized polycrystalline La3Ni2O7 samples by using the sol-gel method without post-annealing under high oxygen pressure, and then measured temperature-dependent resistivity under various hydrostatic pressures up to 14.5 GPa in a cubic…
Nickelate superconductors have attracted a great deal of attention over the past few decades due to their similar crystal and electronic structures with high-temperature cuprate superconductors. Here, we report the superconductivity in a…
Single crystals of Ruddlesden-Popper nickelates La$_4$Ni$_3$O$_{10}$ were grown by means of the floating-zone technique at oxygen pressure of 20~bar. Our results reveal the effects of the annealing process under pressure on the crystal…
The discovery of high-temperature superconductivity in La$_3$Ni$_2$O$_7$ at pressures above 14 GPa has spurred extensive research efforts. Yet, fundamental aspects of the superconducting phase, including the possibility of a filamentary…
Solution growth of single crystals of the recently reported new compound Ce2PdIn8 was investigated. When growing from a stoichiometry in a range 2:1:20 - 2:1:35, single crystals of CeIn3 covered by a thin (~50 um) single-crystalline layer…
Recently, the Pr-doped Ruddlesden-Popper phase of bilayer nickelate La3Ni2O7 has been reported to exhibit a superconducting transition temperature (Tc) of 82.5 K and superconducting volume fraction of about 57 % at high pressure. However,…
The recent report of pressure-induced structure transition and signature of superconductivity with Tc = 80 K above 14 GPa in the La3Ni2O7 crystals has garnered considerable attention. To further elaborate this discovery, we carried out…