Related papers: Superconductivity in WBe2
Recently it was discovered that, under elevated pressures, MoB$_2$ exhibits superconductivity at a critical temperature, $T_c$, as high as 32 K. The superconductivity appears to develop following a pressure-induced structural transition…
Dense pure and doped (Mg1-xAx)B2 samples with A = Na, Ca, Cu, Ag, Zn and Al were synthesized at high pressure - high temperature in a multi anvils press (3.5-6 GPa, 900-1000C) for x up to 0.20. They were studied by x-ray diffraction,…
$MgB_2$ becomes superconducting just below 40 K. Whereas porous polycrystalline samples of $MgB_2$ can be synthesized from boron powders, in this letter we demonstrate that dense wires of $MgB_2$ can be prepared by exposing boron filaments…
The RuSr2Gd1.5Ce0.5Cu2O10-d (Ru-1222) compounds, with varying oxygen content, crystallize in a tetragonal crystal structure (space group I4/mmm). Resistance (R) versus temperature (T) measurements show that the air-annealed samples exhibit…
We report superconducting properties of PrO1-xFxBiS2 compounds, synthesized by the vacuum encapsulation technique. The synthesized PrO1-xFxBiS2 (x=0.1, 0.3, 0.5, 0.7 and 0.9) samples are crystallized in a tetragonal P4/nmm space group. Both…
The superconducting phase diagram of MgB2 was determined from magnetization, magneto-transport and the first single-crystal specific heat measurements. A zero-temperature in-plane coherence length of 8 nm is determined. The superconducting…
We report a mechanical point-contact spectroscopy study on the single crystalline NbGe$_2$ with a superconducting transition temperature $T\rm_c$ = 2.0 - 2.1 K. The differential conductance curves at 0.3 K can be well fitted by a single gap…
A series of new Cr$_{5+x}$Mo$_{35-x}$W$_{12}$Re$_{35}$Ru$_{13}$C$_{20}$ high-entropy alloys (HEAs) have been synthesized and characterized by x-ray diffraction, scanning electron microscopy, electrical resistivity, magnetic susceptibility…
Following the recent theoretical prediction of superconductivity in hole doped LiBC by Rosner et al [1], we have attempted to synthesise Li deficient LixBC (x = 1, 0.8, 0.6 and 0.4) and look for superconductivity in this system. Our…
We have constructed a pressure$-$temperature ($P-T$) phase diagram of $P$-induced superconductivity in EuFe$_2$As$_2$ single crystals, via resistivity ($\rho$) measurements up to 3.2 GPa. As hydrostatic pressure is applied, an…
In this letter, we present the superconducting property characterization of a phase pure reasonably good quality YBa2Cu3O7-{\delta} sample. Studied compound is crystallized in orthorhombic Pmmm space group with lattice parameters a, b, and…
The electrical resistivity \rho(T) and heat capacity C(T) on single crystals of SrNi2As2 and EuNi2As2 are reported. While there is no evidence for a structural transition in either compound, SrNi2As2 is found to be a bulk superconductor at…
High pressure electrical resistance and x-ray diffraction measurements have been performed on ruthenium-doped Ba(Fe0.9Ru0.1)2As2, up to pressures of 32 GPa and down to temperatures of 10 K, using designer diamond anvils under…
Two single crystalline samples with the same nominal composition of Rb0.8Fe2Se2 prepared via slightly different precursor routes under the same thermal processing conditions were investigated at ambient and high pressures. One sample was…
We report the ac magnetic susceptibility $\chi_{ac}$ and resistivity $\rho$ measurements of EuFe$_2$As$_2$ under high pressure $P$. By observing nearly 100% superconducting shielding and zero resistivity at $P$ = 28 kbar, we establish that…
The single crystal of ThCr2Si2-type BaPd2As2 was successfully prepared by a self-flux method, and the crystal structure was characterized by X-ray diffraction method with the lattice parameters a = 4.489(2) {\AA} and c = 10.322(3) {\AA}.…
The results of electrical resistance (1.4 - 300 K), magnetization (2-300 K) and heat-capacity (2 - 50 K) measurements in Y$_2$PdGe$_3$, found to crystallize in a AlB$_2$-derived hexagonalstructure, are reported. The results establish that…
The electrical resistivity of polycrystalline Bi2Sr2Ca2Cu3O10-x (Bi-2223) was measured vs. applied magnetic fields up to 0.45 T, applied currents up to 1 A, and temperature from liquid nitrogen temperature (LN2) to room temperature. In the…
A series of layered (Sr$_{1-x}$K$_x$)Fe$_2$As$_2$ compounds with nominal x=0 to 0.40 are synthesized by solid state reaction method. Similar to other parent compounds of iron-based pnictide superconductors, the pure SrFe$_2$As$_2$ shows a…
CeRh$_2$As$_2$ is a rare unconventional superconductor ($T_c=0.26$ K) characterized by two adjacent superconducting phases for a magnetic field $H \parallel c$-axis of the tetragonal crystal structure. Antiferromagnetic order,…