Related papers: Magnetic dilution by severe plastic deformation
Initial powder mixtures of Cu, Fe and Co are exposed to severe plastic deformation by high-pressure torsion to prepare solid solutions. A broad range of compositions is investigated, whereas this study aims at the synthesis of soft magnetic…
In this study, severe plastic deformation by high pressure torsion is used as a fabrication method for nanocrystalline magnetic CuCo alloys in bulk quantities. By subsequent isothermal annealing, phase separation of the supersaturated solid…
Severe plastic deformation using high-pressure torsion of ternary Cu-based materials (CuFeCo and CuFeNi) was used to fabricate bulk samples with a nanocrystalline microstructure. The goal was to produce materials featuring the granular…
In this study, a preparation route of Co-Cu alloys with soft magnetic properties by high-pressure torsion deformation is introduced. Nanocrystalline, supersaturated single-phase microstructures are obtained after deformation of Co-Cu…
A filamentary composite elaborated by cold drawing was processed by High Pressure Torsion (HPT). The nanostructure resulting from this severe plastic deformation (SPD) was investigated thanks to scanning electron microscopy, transmission…
Bulk metallic samples were synthesized from different binary powder mixtures consisting of elemental Cu, Co, and Fe using severe plastic deformation. Small particles of the ferromagnetic phase originate in the conductive Cu phase, either by…
High-pressure torsion (HPT), a technique of severe plastic deformation (SPD), is shown as a promising processing method for exchange-spring magnetic materials in bulk form. Powder mixtures of Fe and SmCo$_{5}$ are consolidated and deformed…
Samples consisting of one ferromagnetic and one diamagnetic component which are immiscible at the thermodynamic equilibrium (Co-Cu, Fe-Cu, Fe-Ag) are processed by high-pressure torsion at various compositions. The received microstructures…
Severe plastic deformation of powder blends consisting of SmCo5-Cu results in magnetically hardened nanocomposite bulk materials. The microstructure is continuously refined with increasing torsional deformation, yet, coercivity saturates at…
A FePd alloy was nanostructured by severe plastic deformation following two different routes: ordered and disordered states were processed by high pressure torsion (HPT). A grain size in a range of 50 to 150 nm is obtained in both cases.…
Bulk nanocrystalline materials of small and medium ferromagnetic content were produced using severe plastic deformation by high-pressure torsion at roomtemperature. Giant magnetoresistive behavior was found for as deformed materials, which…
Nanostructured Pd-Fe thin films with varied Fe content were prepared by electrodeposition technique from organic electrolytes on Cu and brass substrates. The structure and the magnetic properties of the films were investigated prior to…
A Cu-Cr composite was processed by severe plastic deformation to investigate the role of interphase boundaries on the grain size reduction mechanisms. The as-deformed material exhibits a grain size of only 20nm. This gives rise to a…
Exchange-coupling between soft- and hard-magnetic phases plays an important role in the engineering of novel magnetic materials. To achieve exchange coupling, a two-phase microstructure is necessary. This interface effect is further…
This work gives insights into processing and characterisation of bulk nanocrystalline FeCr materials. The investigated FeCr alloys, consisting of 30, 50 and 70 at.% ferromagnetic Fe and remaining anti-ferromagnetic Cr, are processed by arc…
The capability of high-pressure torsion on the preparation of supersaturated solid solutions, consisting of Cu-14Fe (wt.%), is studied. From microstructural investigations a steady state is obtained with nanocrystalline grains. The…
The processing of binary alloys consisting of ferromagnetic Fe and antiferromagnetic Cr by severe plastic deformation (SPD) with different chemical compositions has been investigated. Although the phase diagram exhibits a large gap in the…
A Cu-Fe nanocomposite containing 50 nm thick iron filaments dispersed in a copper matrix was processed by torsion under high pressure at various strain rates and temperatures. The resulting nanostructures were characterized by transmission…
Nickel carbon nanotube composites with varying amounts of carbon nanotubes are deformed by high pressure torsion at different deformation temperatures to high strains, where no further refinement of the Nickel matrix microstructure is…
Nanoindentation is a powerful tool capable of providing fundamental insights of material elastic and plastic response at the nanoscale. Alloys at nanoscale are particularly interesting as the local heterogeneity and deformation mechanism…