Melting of rhombohedral boron subnitride B13N2 has been studied in situ at pressures to 8 GPa using synchrotron X-ray diffraction and electrical resistivity measurements. It has been found that above 2.6 GPa B13N2 melts incongruently, and…
Melting of cubic boron phosphide, BP has been studied at pressures to 9 GPa using synchrotron X-ray diffraction and electrical resistivity measurements. It has been found that above 2.6 GPa BP melts congruently, and the melting curve…
The pressure dependence of melting temperatures for boron carbide and B4C-carbon eutectic has been studied up to 8 GPa, and it was found that in both cases the melting curves exhibit negative slope (-13\pm6 K/GPa), that is indicative of…
The melting of silicon carbide has been studied at pressures 5-8 GPa and temperatures up to 3300 K. It has been found that SiC melts congruently, and its melting curve has negative slope of -44 +/- 4 K/GPa.
Melting of boron subphosphide (B12P2) to 26 GPa has been studied by in situ synchrotron X-ray powder diffraction in a laser-heated diamond anvil cell, and by quenching and electrical resistance measurements in a toroid-type high-pressure…
The melting curve of pure silica (SiO$_2$) was determined using {\it ab initio} density functional theory together with the solid-liquid coexisting approach, thermodynamic integration and the Z method. The melting curves are consistent with…
Crystal structure searching and ab initio calculations have been used here to explore low-energy structures of boron carbides under high pressure. Under pressures of 85-110 GPa, a metastable B6C with R-3m symmetry is found to be…
The electrical conductivity of melts of boron and its carbide (B4C), nitride (BN), and phosphide (BP) has been studied at pressures to 7.7 GPa and temperatures to 3500 K. It has been shown that these melts are good conductors with specific…
Recent experiments have obtained the melting line of sodium up to pressures of about 130 GPa, finding that the melting line from the {\em bcc} phase reaches a maximum at a temperature of {\em c.a.} 1000 K and a pressure of 31 GPa, and at…
Rattling-induced superconductivity in the beta-pyrochlore oxide RbOs2O6 is investigated under high pressures up to 6 GPa. Resistivity measurements in a high-quality single crystal show that the superconducting transition temperature Tc…
Recent reports of the melting curve of sodium at high pressure have shown that it has a very steep descent after a maximum of around 1000K at 31 GPa. This is not due to a phase transition. According to the Lindemann criterion, this…
p-V-T equation of state of superhard boron suboxide B6O has been measured up to 6 GPa and 2700 K using multianvil technique and synchrotron X-ray diffraction. To fit the experimental data, the theoretical p-V-T equation of state has been…
The compounds, Gd6Co1.67Si3 and Tb6Co1.67Si3, recently reported to form in a Ce6Ni2Si3-derived hexagonal structure (space group: P6_3 / m) and to order magnetically below 295 and 190 K respectively, have been investigated by detailed…
Different phases of solid boron under high pressure are studied by first principles calculations. The $\alpha$-B$_{12}$ structure is found to be stable up to 270 GPa. Its semiconductor band gap (1.72 eV) decreases continuously to zero…
Molybdenum disilicide (MoSi$_2$) is a very promising material for high temperature structural applications due to its high melting point (2030 {\deg}C), low density, high thermal conductivity and good oxidation resistance. However, MoSi$_2$…
Black phosphorus (bP) is a crystalline material that can be seen as ordered stackings of two-dimensional layers, which lead to outstanding anisotropic physical properties. The knowledge of its pressure-temperature (P-T) phase diagram, and…
Two novel of boron-rich selenides, orthorhombic B$_6$Se and rhombohedral B$_{12}$Se, have been recently synthesized at high pressure - high temperature conditions. Room-temperature compressibilities of these phases were studied in a diamond…
We report the results of the X-ray diffraction study of B2O3 glass in the pressure interval up to 10 GPa in the 300-700 K temperature range, the results of in-situ volumetric measurements of the glass at pressures up to 9 GPa at room…
High-pressure phase of boron oxide, orthorhombic \b{eta}-B2O3, has been studied in situ by synchrotron X-ray diffraction to 22 GPa and Raman scattering to 46 GPa at room temperature. The bulk modulus of \b{eta}-B2O3 has been found to be…
The phase diagram of Zn has been explored up to 140 GPa and 6000 K, by combining optical observations, x-ray diffraction, and ab-initio calculations. In the pressure range covered by this study, Zn is found to retain a hexagonal…