Thin films of Zn2+ doped cupric oxide (CuO) were synthesized using spin coating technique starting from a solution with Cu and Zn. The speed of spin coating and time duration were varied to fabricate a film with required uniform thickness.…
Sol-gel spin coating technique was employed to synthesize CuO thin films at 1500 rpm, 2200 rpm and 2400 rpm for 30 seconds, and subsequently annealed at 150-550{\deg}C for 1 hour. Multi-layered CuO thin films with 3 and 5 layers were…
Spin coating technique was used to synthesize pure ZnO and Cu doped ZnO films on amorphous and conducting glass substrates. The doped amount of Cu in ZnO was varied up to 5% in atomic percentage. Speed of spin coating system, coating time,…
Copper oxide (CuO) thin films have been deposited on glass substrates by a facile sol-gel dip-coating technique with varying withdrawal speeds from 0.73 to 4.17 mm/s. The variation of film thickness manifested by dip-coating withdrawal…
Cu added CdS films were synthesized using spin coating technique at different spin speeds for different time durations. Films were subsequently annealed at different temperatures for different time periods in air to crystallize the phase of…
Thin films of magnesium doped zinc oxide (MZO) were synthesized using the sol gel method and annealed at different temperatures under ambient condition. The morphological properties of the post annealed MZO films were investigated using X…
A comparative study of the physical properties of undoped Zinc Oxide (ZnO) and Al doped Zinc Oxide (AZO) thin films were performed as a function of annealing temperature. The structural properties were analyzed using X-ray diffraction and…
The Fe-doped CuO thin films were deposited onto glass substrates by Spray pyrolysis technique. The structural, micro-structural, optical and electrical properties of the synthesized samples were investigated in details. The X-Ray…
This investigation deals with the effect of annealing temperature on the structural, topographical and optical properties of Zinc Oxide thin films prepared by sol gel method. The structural properties were studied using X-ray diffraction…
In present study, Tetragonal Mn$_3$O$_4$ thin films of different coating layers of 2, 4, 6, 8, and 10 were prepared on the microscopic glass slides by the spin-coating method. X-ray diffraction, Raman spectroscopy, and ultra-violet visible…
Cu doped transparent ZnO thin films were spin coated on conductive glass substrates. The samples were subsequently annealed in air for 1 hour at 500 0C in order to form the phase of ZnO. ZnO samples were doped with different Cu molar…
The study uses AACVD technology with nitrogen carrier gas to make AZO thin films through which it determines structural, optical, and morphological changes from 0 to 20 percent aluminum doping. The depositions took place at 400 degrees…
CdS thin film samples were fabricated using spin coating technique on normal glass and conductive glass substrates and annealed at different temperatures. According to the XRD patterns of films prepared on normal glass substrates,…
This work reports optical functionality contained in, as well as and produced by, thin film coatings. A sol-gel process, formulated with precursor active ingredients of erbium oxide and tetraethylorthosilicate (TEOS), was used for…
Cu-doped NiO thin films were deposited on ITO substrates via spray pyrolysis at 450 {\deg}C for 1.5 minutes. XRD confirmed a cubic NiO structure, with Cu incorporation reducing crystallite size, increasing interplanar spacing, and expanding…
Thin TiO2 films on quartz substrates were prepared by spin coating of undoped and metal-ion-doped Sol Gel precursors. These films were characterised by Scanning Electron Microscopy, Laser Raman Microspectroscopy, Xray Diffraction and UV Vis…
CdS samples were synthesized on amorphous glass and conductive glass substrates at room temperature using spin coating technique and subsequently annealed at five different temperatures in air for one hour. The speed and time of spin…
We fabricated NiFe$_\textrm{2}$O$_\textrm{x}$ thin films on MgAl$_2$O$_4$(001) substrates by reactive dc magnetron co-sputtering varying the oxygen partial pressure during deposition. The fabrication of a variable material with oxygen…
The temperature dependence of the optical and magnetic properties of CuO were examined by means of hybrid density functional theory calculations. Our work shows that the spin exchange interactions in CuO are neither fully one-dimensional…
This paper reports on the structural and optical properties of Co-doped TiO2 thin films grown onto (0001) Al2O3 substrates by non-reactive pulsed laser deposition (PLD) using argon as buffer gas. It is shown that by keeping constant the…