Thin superconducting films of magnesium diboride (MgB2) with Tc \approx 24K were prepared on various oxide substrates by pulsed laser deposition (PLD) followed by an in-situ anneal. A systematic study of the influence of various in-situ…
In the present work, a thin film was deposited on quartz substrate by reactive RF magnetron sputtering of high purity (99.999%) aluminium target using ultra-high pure (Ar + N2) gas mixture. The percentage ratio of Ar and N2 in the gas…
Pure rutile Co-doped TiO$_2$ films were fabricated successfully by the conventional pulsed laser deposition technique on silicon substrates from a ceramic target. Under the right fabrication conditions, Co concentration in the films could…
High quality vanadium sesquioxide V2O3 films (170-1100 {\AA}) were grown using the pulsed laser deposition technique on (0001)-oriented sapphire substrates, and the effects of film thickness on the lattice strain and electronic properties…
Zinc telluride (ZnTe) thin films have special semiconducting characteristics that make them very promising for a broad range of optoelectronic applications. In this work, a novel approach for synthesizing ZnTe thin films by spin coating…
We report in situ characterized TiO2 thin-films deposited on optical fiber, having thicknesses in the 20-100nm range, and having enhanced conductivity values of 700S/cm upon interacting with hydrogen. This conductivity was achieved in pure…
Low-temperature powder neutron diffraction measurements are performed in the ordered magnetic state of the pyrochlore antiferromagnet Gd2Sn2O7. Symmetry analysis of the diffraction data indicates that this compound has the ground state…
We have investigated the structural and magnetic properties of BiFeO$_3$ (BFO) thin films grown over (100)-oriented Si substrates by rf magnetron sputtering in a new route under O$_2$ free low pressure Ar atmosphere. Single-phase BFO films…
We report a detailed study of structural and magnetic properties of the pyrochlore-type (Bi2-xPrx)Ru2O7 series. Eleven compositions with 0 <= x <= 2 were prepared by solid state reaction at 1050 degrees C and found to form a solid solution…
The structural, magnetic and dielectric properties have been investigated in 3$d$-5$d$ based double perovskite Sr$_2$FeIrO$_6$ thin films deposited by pulse laser deposition technique. To understand the effect of strain, epitaxial films are…
50nm thick nanogranular polycrystalline dysprosium thin films have been prepared via ultra-high vacuum DC sputtering on SiO2 and Si wafers. The maximum in-plane spontaneous magnetization at T = 4K was found to be MS4K = 3.28T for samples…
Lead based relaxor ferroelectric thin films have been of technological importance due to excellent properties for several commercial applications. However subtleness and high cost of fabrication have plagued of these materials. In this work…
This work reports on sputter depositions carried out from a compound (Ti,Zr)2AlC target, whereupon Al-containing (Ti,Zr)C thin films (30-40 nm in thickness) were deposited on MgO(111) and Al2O3(0001) substrates at temperatures ranging…
The synthesis of stoichiometric and epitaxial pyrochlore iridate thin films presents significant challenges yet is critical for unlocking experimental access to novel topological and magnetic states. Towards this goal, we unveil an in-situ…
In the present work, a set of ZrO2 thin films have been deposited at 82 degree angle of deposition at several substrate rotation speeds and at 0 degree. The effect of substrate rotation on optical, structural, morphological properties and…
Nanocrystalline n-AlN:Er thin films were deposited on (001) Silicon substrates by r. f. magnetron sputtering at room temperature to study the correlation between 1.54 $\mu$m IR photoluminescence (PL) intensity, AlN crystalline structure and…
5$\mu$m thick NdFeB films have been sputtered onto 100 mm Si substrates using high rate sputtering (18 $\mu$m/h). Films were deposited at ≤ 500 C and then annealed at 750 C for 10 minutes. While films deposited at temperatures up to…
In this work, the results of fabricating ultra thin VO$_2$ films on the technologically relevant amorphous SiO$_2$ surface using reactive DC magnetron sputtering are presented. Results indicate that a post deposition anneal in low partial…
The authors have shown that nanogranular indium tin oxide (ITO) films, deposited by spray pyrolysis on silicon substrate, demonstrate ultralow thermal conductivity ~ 0.84 +/-0.12 Wm-1K-1 at room temperature. This value is approximately by…
Nickel oxide (NiO) is a binary compound with a lot of applications in the present technology. NiO thin films were deposited by reactive sputtering magnetron under several voltage biases applied in the glass substrates (0, 50, 100, 200, 300,…