"F-free" CeOBiS$_2$ single crystals have successfully grown, thoroughly eliminating a concern about F-contamination by using a high-purity CsCl flux. The obtained crystals have a plate-like shape with a size of 1.0-3.0 mm in the…
Single crystals of Ce-doped (La,Pr)OBiS2 superconductors, multinary rare-earth elements substituted ROBiS2, were successfully grown. The grown crystals typically had a size of 1-2 mm and a plate-like shape with a well-developed c-plane. The…
Sb-substituted CeOBiS2 single crystals with 0.2-1.0 mm size have been successfully grown using CsCl/KCl flux. Sb substitution strongly suppressed the superconductivity in CeOBiS2, and the substitution of more than approximately 4 atomic…
We report the effects of Ce substitution on structural, electronic, and magnetic properties of layered bismuth-chalcogenide La1-xCexOBiSSe (x = 0-0.9), which are newly obtained in this study. Metallic conductivity was observed for x > 0.1…
Through the combination of X-ray diffraction, electrical transport, magnetic susceptibility, and the heat capacity measurements, we studied the effect of Ce doping in the newly discovered SrFBiS${2}$ system. It is found that…
We report the Se substitution effects on the crystal structure, superconducting properties, and valence states of self-doped BiCh2-based compound CeOBiS2-xSex. Polycrystalline CeOBiS2-xSex samples with x = 0-1.0 were synthesized. For x =…
It has been proposed that there are two types of superconductivity in CeCu2Si2, mediated by spin fluctuations at ambient pressure, and by critical valence fluctuations around a charge instability at a pressure P_v \simeq 4.5 GPa. We present…
Polycrystalline samples of F-substituted LnOBiS2 (Ln = La, Ce, Pr, Nd, Yb) compounds were synthesized by solid-state reaction. The samples were characterized by x-ray diffraction measurements and found to have the ZrCuSiAs crystal…
The first heavy fermion superconductor CeCu$_2$Si$_2$ has not revealed all its striking mysteries yet. At high pressures, superconductivity is supposed to be mediated by valence fluctuations, in contrast to ambient pressure, where spin…
Sb- and Se-substituted CeOBiS2 single crystals have been successfully grown using CsCl/KCl flux. Sb and Se substitution dependence of the superconductivity on CeOBiS2 was investigated and the superconducting phase diagram at above 0.3 K was…
We present a combined growth and transport study of superconducting single-crystalline NdO$_{0.5}$F$_{0.5}$BiS$_2$. Evidence of two-dimensional superconductivity with significant phase fluctuations of preformed Cooper pairs preceding the…
A series of layered CeO$_{1-x}$F$_x$FeAs compounds with x=0 to 0.20 are synthesized by solid state reaction method. Similar to the LaOFeAs, the pure CeOFeAs shows a strong resistivity anomaly near 145 K, which was ascribed to the…
F-doped LaOBiSe$_{2}$ superconducting single crystals with typical size of 2$\times$4$\times$0.2 mm$^{3}$ are successfully grown by flux method and the superconducting properties are studied. Both the superconducting transition temperature…
Superconductivity is achieved in Nd1-xCexOBiS2 via electron doping using mixed-valence Ce ions. Single crystals with x = 0.2, 0.3, 0.4, and 0.5 are generated using a CsCl flux method. Plate-like single crystals with dimensions of 0.8 0.8…
Resistive and magnetization properties have been measured in BiS$_2$-based samples CeO$_{1-x}$F$_{x}$BiS$_{2}$ with a systematic substitution of O with F (0 $<$ x $<$ 0.6). In contrast to the band structure calculations, it is found that…
Simultaneous resistivity and a.c.-specific heat measurements have been performed under pressure on single crystalline CeCu2Si2 to over 6 GPa in a hydrostatic helium pressure medium. A series of anomalies were observed around the pressure…
Many cerium-based heavy fermion (HF) compounds have pressure-temperature phase diagrams in which a superconducting region extends far from a magnetic quantum critical point. In at least two compounds, CeCu2Si2 and CeCu2Ge2, an enhancement…
We present the pressure-temperature phase diagram of the antiferromagnet CeAg$_2$Si$_2$ established via resistivity and calorimetry measurements under quasi-hydrostatic conditions up to 22.5~GPa. With increasing pressure, the N\'eel…
The layered compound LaOBiSSe was successfully synthesized by a two-step solid-state reaction method, which is isostructural with the quaternary compound LaOBiS2 indicated by the powder X-ray diffraction characterization, and the crystal…
We measured the electrical resistivity of a BiS2-based compound EuFBiS2 under high pressure. Polycrystalline EuFBiS2 shows insulator-metal transition and pressure-induced superconductivity above 0.7 GPa. The superconducting transition…