Related papers: Magnetocaloric effect in Gd3Ir compound
We report the magnetocaloric effect in terms of isothermal magnetic entropy change as well as adiabatic temperature change, calculated using the heat capacity data. Using the zero field heat capacity data, the magnetic contribution to the…
We report a large entropy change (DeltaS) below 300 K, peaking near TC= 220 K, due to isothermal change of magnetic field, for Gd4Co3, with a refrigeration capacity higher than that of Gd. Notably, the isothermal magnetization is…
The caloric effect in Gd5Si2Ge2 compound is studied experimentally and theoretically. The first-order phase transition is sensitive to both magnetic field and pressure. It indicates that the influences of magnetic field and pressure on the…
Heat capacity of polycrystalline R2Ti3Ge4 (R = Gd, Tb and Er) compounds (Orthorhombic, Sm5Ge4-type, Space group Pnma) has been studied in the temperature range of 1.8 K to 300 K in various applied magnetic fields. The compounds with…
We have investigated the magnetocaloric effect in single and polycrystalline samples of quantum paraelectric EuTiO3 by magnetization and heat capacity measurements. Single crystalline EuTiO3 shows antiferromagnetic ordering due to Eu2+…
We study structural, magnetic and magneto-thermal properties of GdRhIn compound. The room temperature X-ray diffraction measurements show hexagonal crystal structure. Temperature and field dependence of magnetization suggest two magnetic…
We report the structural, magnetic properties, and magnetocaloric effect of a new polycrystalline compound of $\mathrm{Tb_2Rh_3Ge}$. This present compound crystallizes with $\mathrm{Mg_2Ni_3Si}$-type of rhombohedral Laves phases (space…
The excellent magnetocaloric effect of a dense inorganic framework, orthorhombic Gd(OH)CO3, is evaluated by isothermal magnetization and heat capacity measurements. The large -{\Delta}Sm, both in gravimetric and volumetric units, place it…
The magnetocaloric effect in RE$_{11}$Co$_4$In$_9$ (RE = Tb, Er) has been studied by means of magnetometric measurements in the function of temperature and applied magnetic field. The maximum magnetic entropy change ($-\Delta…
The electrical resistivity, magnetization and heat-capacity behavior of the Gd-based compounds, Gd2Co2Al, Gd2Co2Ga and Gd7Rh3, ordering magnetically at TC= 78 K, TC= 76 K and TN= 140 K have been investigated as a function of temperature and…
This study presents systematic investigations into the growth and physical properties of EuAl$_3$Si single crystals, encompassing magnetic, transport, and thermodynamic analyses. EuAl$_3$Si undergoes a ferromagnetic transition at $T_C$ = 15…
The magnetocaloric effect in the quantum dipolar magnet Yb$_3$Ga$_5$O$_{12}$ is studied both for pure material and with non-magnetic substitution: (Yb$_{1-x}$Y$_x$)$_3$Ga$_5$O$_{12}$. Magnetization measurements have been performed on a…
The effect of Ge substitution on the magnetization, heat capacity, magnetocaloric effect and magnetoresistance of GdMn2Si2-xGex (x=0, 1, and 2) compounds has been studied. The magnetic transition associated with the Gd ordering is found to…
We report on a novel class of nanocrystalline/amorphous Gd$_3$Ni/Gd$_{65}$Ni$_{35}$ composite microwires, which was created directly by melt-extraction through controlled solidification. X-ray diffraction (XRD) and transmission electron…
We report the magnetic and magnetocaloric properties of HoCoSi, which shows second order ferro-para magnetic transition at 14 K. It is found to exhibit a large magnetic entropy change of 13 J/kg K for a field change of 20 kOe, which…
The magnetocaloric properties of three samples of LaFe$_{13-x-y}$Co$_x$Si$_y$ have been measured and compared to measurements of commercial grade Gd. The samples have (x=0.86, y=1.08), (x=0.94, y=1.01) and (x=0.97, y=1.07) yielding Curie…
We report a giant magnetocaloric effect near room temperature in an off-stoichiometric Mn-Co-Ge alloy, across the magnetostructural transition. The isothermal entropy change accompanying this transition has a peak value of nearly 40 J/kg-K…
Magnetocaloric effect and magnetoresistance have been studied in Dy(Co1-xSix)2 [x=0, 0.075 and 0.15] compounds. Magnetocaloric effect has been calculated in terms of adiabatic temperatue change (Delta Tad) as well as isothermal magnetic…
We report the effect of exchange frustration on the magnetocaloric properties of GdCrTiO$_5$ compound. Due to the highly exchange-frustrated nature of magnetic interaction, in GdCrTiO$_5$, the long-range antiferromagnetic ordering occurs at…
Magnetic and heat capacity measurements have been carried out on the polycrystalline sample of DyNi which crystallizes in the orthorhombic FeB structure (space group Pnma). This compound is ferromagnetic with a Curie temperature of 59 K.…