Related papers: Large low-temperature magnetoresistance in SrFe2As…

Growth of BaMn2As2 crystals using both MnAs and Sn fluxes is reported. Room temperature crystallography, anisotropic isothermal magnetization M versus field H and magnetic susceptibility chi versus temperature T, electrical resistivity in…

We report here the magneto-transport properties of the newly synthesized Heusler compound Cr2NiGa which crystallizes in a disordered cubic B2 structure belonging to Pm-3m space group. The sample is found to be paramagnetic down to 2 K with…

We investigated the transport properties of BaFe$_2$As$_2$ single crystals before and after annealing with BaAs powder. The annealing remarkably improves transport properties, in particular the magnitude of residual resistivity which…

The magnetization, resistivity and magnetoresistance (MR) of single crystals of GdBaCo2O5.5 and EuBaCo2O5.5 are measured over a wide range of dc magnetic fields (up to 30 T) and temperature. In LnBaCo2O5.5 (Ln=Gd, Eu), the Co-ions are…

YSb crystals are grown and the transport properties under magnetic field are measured. The resistivity exhibits metallic behavior under zero magnetic field and the low temperature resistivity shows a clear upturn once a moderate magnetic…

We demonstrate the preparation of large, free standing iron pnictide single crystals with a size up to 20 x 10 x 1 mm3 using solvents in zirconia crucibles under argon atmosphere. Transport and magnetic properties are investigated to study…

We report high field magneto transport of Sm/PrFeAsO. Below spin density wave transition (TSDW), the magneto-resistance (MR) of Sm/PrFeAsO is positive and increasing with decreasing temperature. The MR of SmFeAsO, is found 16%, whereas the…

We report on magnetic and electrical transport properties of Sb2-xCrxTe3 single crystals with 0 <= x <= 0.095 over temperatures from 2 K to 300 K. A ferromagnetic state develops in these crystals at low temperatures with Curie temperatures…

Ni$_3$In$_2$S$_2$ is the most recent entrant into the family of topological insulator (TI) materials, the same exhibits very high MR in a low-temperature regime. Here, we report the crystal growth, the structural, micro-structural, and…

Fe$_3$Ga$_4$ possesses a helical spin spiral with a complex competition between ferromagnetic and antiferromagnetic ground states. This competition generates multiple metamagnetic transitions that are governed by both applied magnetic field…

A review of our investigations on single crystals of LnFeAsO1-xFx (Ln=La, Pr, Nd, Sm, Gd) and Ba1-xRbxFe2As2 is presented. A high pressure technique has been applied for the growth of LnFeAsO1-xFx crystals, while Ba1-xRbxFe2As2 crystals…

The extremely large magnetoresistance (XMR) in nonmagnetic semimetals has inspired growing interest owing to both intriguing physics and potential applications. We report results of synchrotron X-ray diffraction (SXRD) and electrical…

We have grown La$_{1.37}$Sr$_{1.63}$Mn$_2$O$_7$ single crystals with a laser-diode-heated floating-zone furnace and studied the crystallinity, structure, and magnetoresistance (MR) effect by in-house X-ray Laue diffraction, X-ray powder…

A bulk diluted magnetic semiconductor (Sr,K)(Zn,Mn)$_{2}$As$_{2}$ was synthesized with decoupled charge and spin doping. It has a hexagonal CaAl$_{2}$Si$_{2}$-type structure with the (Zn,Mn)$_{2}$As$_{2}$ layer forming a honeycomb-like…

Ambipolar transport is a commonly occurring theme in semimetals and semiconductors. Here we present an analytical formulation of the conductivity for a two-band system. Electron and hole carrier densities and their respective conductivities…

e have developed a simple process to obtain large magnetoresistance (MR) in perovskite manganite thin films by a combination of focused ion beam (FIB) milling and 120 keV H$_{2}^{+}$ ion implantation. Metal slits about 70 nm in width were…

NbTe2 crystal is quasi-2D layered semimetal with charge density wave ground state showing a distorted-1T structure at room temperature. Here we report the anisotropic magneto-transport properties of NbTe2. An anomalous linear…

Unusually large low field magetoresistance (LFMR), ~ 10 %, at 300 K has been observed with the sample of mono-dispersed Fe3O4 magnetite nanospheres, ~ 200 nm, compactly cold-pressed and sintered at 800 C. A detailed analysis on the…

We have investigated transport properties of CrO2 thin films deposited on TiO2 and sapphire substrates. The films are good metals down to low temperatures. The residual resistivity is of the order of 6 micro-ohhmcm for films deposited on…

For the first time magnetrotransport of the ferromagnetic high-pressure phases of (GaSb)$_2$M (M=Cr,Mn) was measured. It was found that the main component of magnetotransport in these phases is negative and its amplitude is increasing with…