The magnetic properties of Fe$_3$O$_4$ nanoparticle assemblies have been investigated in detail through a combination of vibrating sample magnetometry and muon spin relaxation ($\mu$SR) techniques. Two samples with average particle sizes of…
The structural and magnetic properties of ZnFe2O4 nanoparticles embedded in a non-magnetic ZnO matrix are presented. X-ray diffractograms and Transmission Electron Microscopy (TEM) images showed that the resulting samples are composed of…
The scope of this article is to report very detailed results of the measurements of magnetic relaxation phenomena in the new Cu$_{0.5}$Fe$_{2.5}$O$_{4}$ nanoparticles and known CuFe$_{2}$O$_{4}$ nanoparticles. The size of synthesized…
Spinel Fe3O4 nanoparticles have been produced through ball milling in methyl-alcohol (CH3OH), aiming to obtain samples with similar average particle sizes <d> and different interparticle interactions. Three samples having Fe3O4/CH3(OH) mass…
Pure ultrafine ZnFe2O4 particles have been obtained from mechanosynthesis of the ZnO and Fe2O3 oxides. The average grain diameter was estimated from x-ray diffraction to be <d> = 36(6) nm. Refinement of neutron diffraction (ND) data showed…
Single-phase Mg-doped ZnFe$_2$O$_4$ nanoparticles with x= 0, 0.3, 0.5, 0.7 have been prepared by the glycol-thermal method without any subsequent calcination. The crystallite size, microstructure and magnetic properties of the prepared…
We report the particle size dependent magnetic behaviour in the antiferromagnetic spinel CoRh2O4. The nanoparticles were obtained by mechanical milling of bulk material, prepared under sintering method. The XRD spectra show that the samples…
We report detailed studies on magnetic properties of Co3O4 nanoparticles of average size 12.5 nm. Temperature and field dependence of magnetization, wait time dependence of magnetic relaxation (aging), memory effects and temperature…
In this paper we report an investigation on the ferromagnetic state and the nature of ferromagnetic transition of nanoparticles of $\mathrm{La_{0.67}Ca_{0.33}MnO_3}$ using magnetic measurements and neutron diffraction. The investigation was…
The saturation magnetization (M_s), antiferromagnetic transition point (T_N), and the off-center displacements of Bi and Fe ions have been measured as a function of particle size in nanoscale BiFeO3. T_N decreases down to ~550 K for…
Nd2Fe14B magnetic nanoparticles have been successfully produced using a surfactant-assisted ball milling technique. The nanoparticles with different size about 6, 20 and 300 nm were obtained by a size-selection process. Spin-reorientation…
We have studied the magnetic behavior of dextran-coated magnetite (Fe$_3$O$_4$) nanoparticles with median particle size $\left<d\right>=8$ $nm$. Magnetization curves and in-field M\"ossbauer spectroscopy measurements showed that the…
Y-type hexaferrite samples Ba2ZnxCo2-xFe12O22 with x = 0, 1 and 2 were prepared from precursors synthesized by the citrate sol-gel auto combustion method. The powders were sintered at 1100{\deg} C for four hours. X-ray diffraction, scanning…
The experimental studies of the paramagnetic-antiferromagnetic phase transition through M\"{o}ssbauer spectroscopy and measurements of temperature and field dependencies of magnetic susceptibility in the layered Cu$_{0.15}$Fe$_{0.85}$PS$_3$…
We report the magnetic properties of mechanically milled Co$_{0.2}$Zn$_{0.8}$Fe$_2$O$_4$ spinel oxide. After 24 hours milling of the bulk sample, the XRD spectra show nanostructure with average particle size $\approx$ 20 nm. The as milled…
We investigated magnetization, muon spin rotation ($\mu$SR), and $^{119}Sn$ M\"{o}ssbauer spectroscopy on Sn substituted $CuCr_{2-x}Sn_xS_4$ (x=0.03 and 0.08) spinel compounds. The magnetization and $\mu$SR results reveal similar additional…
CuMoO4 is a triclinic quantum magnet based on S = 1/2 moments at the Cu2+ site. It has recently attracted interest due to the remarkable changes in its chromic and volumetric properties at high temperatures, and in its magnetic properties…
Iron-titanium sulfides FeTi2S4 and Fe2TiS4 have been structurally and magnetically characterized using powder X Ray Diffraction with Rietveld refinement method and 57Fe M\"ossbauer spectroscopy at variable temperature. Both sulfides have…
We report results of a comprehensive study of the phase transition at T_N (~643 K) as a function of particle size in multiferroic BiFeO3 system. We employed electrical, thermal, and temperature dependent X-ray diffraction (XRD) studies in…
We report nanoscale inter-particle magnetic orderings in self-assemblies of Fe3O4 nanoparticles (NPs), and the emergence of inter-particle antiferromagnetic (AF) (super-antiferromagnetic) correlations near the coercive field at low…