The structural, magnetic and resistive properties of (La1-yYy)FeAsO compounds (y = 0.10, 0.20, 0.30) have been investigated by means of X-ray and neutron powder diffraction as well as by resistivity measurements. The temperatures at which…
The crystal structure of SmFeAsO has been investigated by means of Rietveld refinement of high resolution synchrotron powder diffraction data collected at 300 K and 100 K. The compound crystallizes in the tetragonal P4/nmm space group at…
The low-temperature crystal structure of Fe1.13Te, which exhibits an anomalous two-step magnetic transition, was clarified by the systematic x-ray diffraction measurements. It was found that two-step structural phase transition,…
Specific heat, resistivity, magnetic susceptibility, linear thermal expansion (LTE), and high-resolution synchrotron X-ray powder diffraction investigations of single crystals Fe1+yTe (0.06 < y < 0.15) reveal a splitting of a single,…
The tetragonal-to-orthorhombic structural phase transition (SPT) in LaFeAsO (La-1111) and SmFeAsO (Sm-1111) single crystals measured by high resolution x-ray diffraction is found to be sharp while the RFeAsO (R=La, Nd, Pr, Sm)…
The nature of the tetragonal-to-orthorhombic structural transition at $T_s\approx90$ K in single crystalline FeSe is studied using shear-modulus, heat-capacity, magnetization and NMR measurements. The transition is shown to be accompanied…
The structural and microstructural properties of the Sm(Fe1-xRux)As(O0.85F0.15) system were investigated by means of high-resolution synchrotron X-ray powder diffraction between 10 K and 300 K. The tetragonal to orthorhombic structural…
We report the temperature dependent x-ray powder diffraction of the FeAs-based superconductors in the range between 300 K and 95 K. In the case of NdOFeAs we have detected the structural phase transition from the tetragonal phase, with…
Neutron diffraction measurements of a high quality single crystal of CaFe2As2 are reported. A sharp transition was observed between the high temperature tetragonal and low temperature orthorhombic structures at TS = 172.5K (on cooling) and…
The structural properties of the CaFe2As2 have been investigated by x-ray and neutron powder diffraction techniques as a function of temperature. Unambiguous experimental evidence is shown for coexistence of tetragonal and orthorhombic…
SrFe2As2 is the end-member for a series of iron-pnictide superconductors and has a tetragonal-to-orthorhombic phase transition near 200 K. Previous macroscopic measurements to determine the nature of the transition gave seemingly…
Synchrotron x-ray diffraction experiments were performed on BaFe$_2$As$_2$ and Sr(Fe$_{1-x}$Co$_{x}$)$_2$As$_2$ single crystals as a function of temperature and applied magnetic field along the tetragonal $[1 \bar{1} 0]$ direction,…
$^{75}$As and $^{139}$La NMR results of LaFeAs(O$_{1-x}$F$_x$) ($x$=0, 0.025, and 0.04) were reported. Upon F-doping, the tetragonal-to-orthorhombic structural phase transition temperature $T_S$, antiferromagnetic transition temperature…
We report systematic investigation of high pressure crystal structures and structural phase transition upto 46 GPa in CaFeAsF and 40 GPa in SrFeAsF at 40 K using powder synchrotron x-ray diffraction experiments and Rietveld analysis of the…
The magnetic ordering and crystal structure of iron pnictide SrFeAsF was investigated by using neutron powder diffraction method. With decreasing temperature, the tetragonal to orthorhombic phase transition is found at 180 K, while the…
The structural properties of the SrFe2As2 and CaFe2As2 compounds have been extensively analyzed by transmission electron microscopy (TEM) from room temperature down to 20K. The experimental results demonstrate that the SrFe2As2 crystal, in…
We use neutron scattering to study the spin and lattice structures of single crystal and powder samples of Na$_{1-\delta}$FeAs ($T_c = 23$ K). On cooling from room temperature, the system goes through a series of phase transitions: first…
A detailed elastic neutron scattering study of the structural and magnetic phase transitions in single-crystal SrFe$_2$As$_2$ reveals that the orthorhombic (O)-tetragonal (T) and the antiferromagnetic transitions coincide at $T_\texttt{O}$…
A detailed elastic neutron scattering study of the structural and magnetic phase transitions in single-crystal SrFe$_2$As$_2$ reveals that the orthorhombic (O)-tetragonal (T) and the antiferromagnetic transitions coincide at $T_\texttt{O}$…
X-ray and Neutron diffraction as well as muon spin relaxation and M\"ossbauer experiments performed on SrFe$_2$As$_2$ polycrystalls confirm a sharp first order transition at $T_0 = 205$,K corresponding to an orthorhombic phase distortion…