Related papers: Pressure Induced Metallization of BaMn2As2
We report magnetization, susceptibility, electrical transport, and electron spin resonance (ESR) studies of single crystals of beta-AgNpO2(SeO3). Here the valence of the Np sites is expected to be Np(V). We observe a magnetic transition…
Electrical resistivity measurements have been performed on the iron-based ladder compounds Ba$_{1-x}$Cs$_x$Fe$_2$Se$_3$ ($x$ = 0, 0.25, 0.65, and 1) under high pressure. A cubic anvil press was used up to 8.0 GPa, whereas further higher…
We studied single-crystals of the antiferromagnetic compound UNi0.5Sb2 (TN ~ 161 K) by means of measurements of magnetic susceptibility (chi), specific heat (Cp), and electrical resistivity (rho) at ambient pressure, and resistivity under…
The newly discovered BaPt$_2$As$_2$ shows a structural distortion at around 275~K, followed by the emergence of superconductivity at lower temperatures. Here we identify the presence of charge density wave (CDW) order at room temperature…
We report on an infrared study on the undoped compound BaFe2As2 as a function of both pressure (up to about 10 GPa) at three temperatures (300, 160, and 110 K). The evolution with pressure and temperature of the optical conductivity shows…
We report specific-heat experiments under the influence of high pressure on a strongly underdoped Co-substituted BaFe2As2 single crystal. This allows us to study the phase diagram of this iron pnictide superconductor with a bulk…
Superconductivity in iron pnictides is unconventional and pairing may be mediated by magnetic fluctuations in the Fe-sublattice. Pressure is a clean method to explore superconductivity in iron based superconductors by tuning the ground…
We measured the electrical resistivity and ac magnetic susceptibility of BaFe2As2 and SrFe2As2 single crystals under pressure using a cubic anvil apparatus. For BaFe2As2, the antiferromagnetic (AF) and structural transitions are suppressed…
Neutron diffraction measurements have been performed on a powder sample of BaMn2As2 over the temperature T range from 10 K to 675 K. These measurements demonstrate that this compound exhibits collinear antiferromagnetic ordering below the…
Using X-ray absorption spectroscopy (XAS), we studied the local structure in LaMnO3 under applied pressure across and well above the insulator to metal (IM) transition. A hysteretic behavior points to the coexistence of two phases within a…
Binary ruthenium pnictides, RuP and RuAs, with an orthorhombic MnP structure, were found to show a metal to a non-magnetic insulator transition at TMI = 270 K and 200 K, respectively. In the metallic region above TMI, a structural phase…
Recently the memristive electrical transport properties in NbO$_2$ have attracted much attention for their promising application to the neuromorphic computation. At the center of debates is whether the metal-to-insulator transition (MIT)…
Raman spectra of the MgB2 ceramic samples were measured as a function of pressure up to 32 GPa at room temperature. The spectrum at normal conditions contains a very broad peak at ~590 cm-1 related to the E2g phonon mode. The frequency of…
We report the results of Hall coefficient R_H and magnetoresistance (MR) measurements on single crystalline samples of Sr3Ru2O7 grown by the floating zone method. R_H was found to be positive over the entire temperature range studied (0.3 -…
We have investigated the effect of Cu substitution in Eu2(Ir1-xCux)2O7 with the help of magnetic and transport property measurements. XPS measurement reveals that each Cu2+ converts Ir4+ to double amount of Ir5+ ions. The metal-insulator…
The high-pressure behavior of two Mn-based honeycomb-structured magnetoelectric materials, Mn4Nb2O9 (MNO) and Mn4Ta2O9 (MTO), was investigated using Raman spectroscopy, synchrotron x-ray diffraction, and density functional theory (DFT)…
The metal-insulator (MI) transition in BaVS$_3$ has been studied at ambient pressure and under hydrostatic pressure up to $p=26 $kbar in the frequency range of $20-3000 $cm$^{-1}$. The charge gap determined from the optical reflectivity is…
A new ternary intermetallic compound $\mathrm{Pr_2Rh_2Ga}$ was synthesized by arc-melting and was characterized by powder X-ray diffraction (PXRD), magnetization, heat capacity $\mathrm{C}_p(\textit{T})$, and electrical resistivity…
The magnetotransport in single layer graphene has been experimentally investigated in magnetic fields up to 18 T as a function of temperature. A pronounced T-dependence is observed for T < 50 K, which is either metallic, or insulating,…
We report anomalous physical properties of single-crystalline FeSi over a wide temperature range 1.8-400 K. X-ray diffraction, specific heat, and magnetization measurements indicate that the FeSi crystals synthesized in this study are of…