Chemical doping has recently become a very important strategy to induce superconductivity especially in complex compounds. Distinguished examples include Ba-doped La$_2$CuO$_4$ (the first high temperature superconductor), K-doped BaBiO$_3$,…
By using solid state reaction method, we have synthesized the Pd-doped superconductor SrFe2-xPdxAs2. The systematic evolution of the lattice constants indicated that the Fe ions were successfully replaced by the Pd. By increasing the doping…
In the electron doped compounds SrFe_(2-x)Co_xAs_2 superconductivity with T_c up to 20 K is observed for 0.2 < x < 0.4. Results of structure determination, magnetic susceptibility, electrical resistivity, and specific heat are reported. The…
Here we report the synthesis and basic characterization of LaFe1-xCoxAsO for several values of x. The parent phase LaFeAsO orders antiferromagnetically (TN ~ 145 K). Replacing Fe with Co is expected to both electron dope the system and…
By doping Rh to the Fe sites in SrFe2As2, superconductivity is induced when the antiferromagnetic (AF) order is suppressed. The maximum superconducting transition temperature was found at about 22 K with the doping level of x = 0.25. It is…
K$_x$Fe$_{2-y}$Se$_2$ exhibits an iron-vacancy ordering at $T_{\rm s} {\sim}270{\deg}$C and separates into two phases: a minor superconducting (iron-vacancy-disordered) phase and a major non-superconducting (iron-vacancy-ordered) phase. The…
We report the superconductivity at above 30 K in a new FeSe-layer compound K0.8Fe2Se2 (nominal composition) achieved by metal K intercalating in between FeSe layers. It is isostructural to BaFe2As2 and possesses the highest Tc for…
In this paper we report the synthesis of iron-based superconductors CaFe2-xRhxAs2 using one-step solid state reaction method, which crystallizes in the ThCr2Si2-type structure with a space group I4/mmm. The systematic evolution of the…
We report the effect of 3d metal Cobalt (Co) and Nickel (Ni) doping on the FeTe0.5Se0.5 superconductor with the nominal composition range Fe1-xMxTe0.5Se0.5 (M = Co, Ni and x = 0.00, 0.01 0.02, 0.05, and 0.10). Samples are synthesized…
Here we report the synthesis and basic characterization of SmFe1-xCoxAsO (x=0.10, 0.15). The parent compound SmFeAsO itself is not superconducting but shows an antiferromagnetic order near 150 K, which must be suppressed by doping before…
We elucidate the existing controversies in the newly discovered K-doped iron selenide (KxFe2-ySe2-z) superconductors. The stoichiometric KFe2Se2 with \surd2\times\surd2 charge ordering was identified as the parent compound of KxFe2-ySe2-z…
We synthesized the new Fe-based superconductor K0.8Fe2Se2 single crystals. The obtained single crystal exhibited a sharp superconducting transition, and the onset and zero-resistivity temperature was estimated to be 33 and 31.8 K,…
Platelet-like single crystals of the Ca(Fe1-xCox)2As2 series having lateral dimensions up to 15 mm and thickness up to 0.5 mm were obtained from the high temperature solution growth technique using Sn flux. Upon Co doping, the c-axis of the…
The effect of Co doping on supercoductivity of FeSe$_{0.4}$Te$_{0.6}$ single crystals is investigated. The superconducting transition temperature decreases linearly for Co doping with the rate -0.75 K/(Co %). On the other hand, the residual…
By direct quenching or post-annealing followed by quenching, we have successfully obtained a series of KxFe2-ySe2 samples with different properties. It is found that the samples directly quenched in the cooling process of growth show…
Superconducting single crystals of Rb-intercalated FeSe compounds Rb$_x$Fe$_{2-y}$Se$_2$ were prepared by using a starting material of Rb$_2$Se as a Rb source. The superconducting properties and the surface microstructures were…
We report significantly enhanced magnetic moment in K0.69(2)Fe1.45(1)Se2.00(1) single crystals with sharp Tc and bulk superconductivity obtained by postannealing and quenching process. There are two Fe sites in the…
The recently discovered Fe-based superconductor (FeBS) LaFe2As2 seems to break away from an established pattern that doping FeBS beyond 0.2e/Fe destroys superconductivity. LaFe2As2 has an apparent doping of 0.5e, yet superconducts at 12.1…
We report synthesis, structural details and magnetization of SmFe1-xCoxAsO with x ranging from 0.0 to 0.30. It is found that Co substitutes fully at Fe site in SmFeAsO in an iso-structural lattice with slightly compressed cell. The parent…
By substituting Fe with the 5d-transition metal Pt in BaFe2As2, we have successfully synthesized the superconductors BaFe2-xPtxAs2. The systematic evolution of the lattice constants indicates that the Fe ions were successfully replaced by…