We present magnetic susceptibility and electrical transport measurements of the highly anisotropic compound LaSb$_2$ observing a very broad transition into a clean, consistent with type-I, superconducting state with distinct features of 2…
Single crystals of the compound LaFePO were prepared using a flux growth technique at high temperatures. Electrical resistivity measurements reveal metallic behavior and a resistive transition to the superconducting state at a critical…
The recently discovered superconductivity in MgB2 has captured world attention due to its simple crystal structure and relatively high superconducting transition temperature Tc=39K. It appears to be generally accepted that it is…
Hall, resistivity, magnetization, and thermoelectric power measurements were performed on single crystals of the highly anisotropic layered metal LaSb2. A 100-fold linear magnetoresistance (MR) was observed in fields up to 45 T, with no…
The magnetotransport properties of single crystals of the highly anisotropic layered metal LaSb2 are reported in magnetic fields up to 45 T with fields oriented both parallel and perpendicular to the layers. Below 10 K the perpendicular…
LaSb2 is found to be an example of an exceptionally pressure sensitive and tunable, two dimensional compound. In-plane electrical resistivity of LaSb2 under pressure up to 12.9 kbar was measured in zero and applied magnetic field. The…
OsB_2 crystallizes in an orthorhombic structure (Pmmn) which contains alternate boron and osmium layers stacked along the c-axis. The boron layers consist of puckered hexagons as opposed to the flat graphite-like boron layers in MgB_2.…
We report here synthesis, structural, DC magnetization, and transport studies of new BiS2 based layered LaO0.5F0.5BiS2 superconductor [1]. The sample was synthesized by conventional solid state route via vacuum encapsulation technique at…
It has recently been observed that MgB_2 is a superconductor with a high transition temperature. Here we propose a model of anisotropic s-wave superconductivity which consistently describes the observed properties of this compound,…
In-plane electrical transport properties of MgB2 single crystals grown under high pressure of 4-6 GPa and temperature of 1400-1700oC in Mg-B-N system have been measured. For all specimens we found sharp superconducting transition around…
We successfully grew the high-quality single crystal of Rb$_{0.78}$Fe$_2$Se$_{1.78}$, which shows sharp superconducting transition in magnetic susceptibility and electrical resistivity. Resistivity measurements show the onset…
We present measurements of $ab$-plane resistivity $\rho_{ab}(T)$ and superfluid density [$\propto \lambda^{-2}$, $\lambda$ = magnetic penetration depth] in $La_{2-x}Sr_{x}CuO_{4}$ films. As Sr concentration $x$ exceeds about 0.22, the…
We investigated a high-quality MgB$_{2}$ thin film with a thickness of $\sim$1000 nm on an Al$_{2}$O$_{3}$ substrate using optical spectroscopy. We measured the reflectance spectra of the film at various temperatures both below, and above,…
Here we report the discovery of superconductivity in the ternary LaRu2As2 compound. The polycrystalline LaRu2As2 samples were synthesized by the conventional solid state reaction method. Powder X-ray diffraction analysis indicates that…
We synthesized large superconducting single crystal Ca0.77La0.18Fe0.90As2 ('112' type) of 2 millimeter size. Scanning electron microscopy (SEM) measurements revealed that bright and dark stripes alternately spread on the surface of…
The recent discovery of large and non-saturating magnetoresistance (LMR) in WTe2 provides a unique playground to find new phenomena and significant perspective for potential applications. Here we report the first observation of…
The complex conductivity of a MgB2 film has been investigated in the frequency range 4 cm^{-1}< nu < 30 cm^{-1} and for temperatures 2.7 K < T <300 K. The overall temperature dependence of both components of the complex conductivity is…
The temperature and angular dependencies of the resistive upper critical magnetic field $B_{c2}$ reveal a dimensional crossover of the superconducting state in the highly anisotropic misfit-layer single crystal of (LaSe)$_{1.14}$(NbSe$_2$)…
Superlattices of the repeated structure La(1.56)Sr(0.44)CuO(4)/La(2)CuO(4) (LSCO-LCO), where none of the constituents is superconducting, show a superconducting transition of T_c \simeq 25 K. In order to elucidate the nature of the…
We present evidence of type I superconductivity in YbSb2 single crystals, from DC and AC magnetization, heat capacity and resistivity measurements. The critical temperature and critical field are determined to be $T_c\approx$ 1.3 K and…