The MgB2 - based material high-pressure synthesized at 2 GPa and 800 C for 1 h from Mg and B (taken in the stoichiometry ratio of MgB2) with addition of 2-10 wt% of Ti demonstrated the critical current density (jc) higher than 100 kA/cm^2…
We investigate nonreciprocal electrical transport in bulk single-crystalline Mo3Al2C, a material known to host crystallographic chirality, a polar charge-density-wave instability, and a superconducting transition near 8 K. Using AC…
The new class of Mg-B superconducting conductors was prepared using the standard in-situ powder-in-tube, PIT, method where Mg+2B mixture was used to fill the copper and silver tubes. Study of the intergranular current, grain connectivity…
If the critical current density Jc is very high for a superconductor, then estimating its value from transport measurements is not very easy. In such cases, the value of Jc, called Jcm for magnetic Jc, is usually obtained from the measured…
The MgB$_2$ superconductor, discovered in 2001, has provided unique compound features of magnesium diboride with much higher critical temperature and critical field compared to NbTi superconductor. Its applications have been expanding owing…
The microstructures of MgB2 wires prepared by the powder-in-tube technique and subsequent hot isostatic pressing were investigated using transmission electron microscopy. Large amount of crystalline defects including small angle twisting,…
The anisotropy gamma of the superconducting state of high quality single-crystals of MgB2 was determined, using torque magnetometry with two different methods. The anisotropy of the upper critical field was found to be temperature…
A c-axis oriented thin film and a high density sintered pellet of MgB2 have been studied by x-ray photoemission spectroscopy, and compared to measurements from MgO and MgF2 single crystals. The as-grown surface has a layer which is Mg-rich…
We have grown MgB2 films in a postannealing process. Precursors were prepared on Al2O3(0001) substrates by codeposition of Mg and MgB2 using pulsed laser deposition technique. Superconducting MgB2 thin films were obtained via an ex situ…
Polarization-dependent x-ray absorption spectroscopy at the B 1s edge of single-crystalline Mg(x)Al(1-x)B(2) reveals a strongly anisotropic electronic structure near the Fermi energy. Comparing spectra for superconducting compounds (x=0.9,…
The electronic anisotropy in MgB2, is still a not completely clear topic; high quality c-oriented films are suitable systems to investigate this property. In this work we present our results on MgB2 superconducting thin films grown on MgO…
The penetration depth lambda of MgB2 was deduced from both the ac susceptibility chi and the magnetization M(H) of sorted powders. The good agreement between the two sets of data without geometric correction for the grain orientation…
Two-band superconductivity has become an important topic over the last ten years. Extensive experimental and theoretical studies started with MgB2 and are now focused on the iron-based and other new superconductors. In this review, I…
We studied the influence of sample preparation and defects in the superconducting properties samples using atomic ratios of Mg:B=1:1 and Mg:B=1:2. Samples were characterized by SEM, and XRD, and the magnetization properties were examined in…
Here we report the growth of sub-millimeter MgB2 single crystals of various shapes under high pressure in Mg-B-N system. Structure refinement using a single-crystal X-ray diffraction analysis gives lattice parameters a=3.0851(5) A and…
Since the discovery of MgB2 with Tc=39K, various metal diborides of MB2 have been intensively studied to find possible conventional high-temperature superconductors. A possible 2D structure of the metal diboride has been shown to be in the…
The transport properties of interacting electrons for which the spin degree of freedom is taken into account are numerically studied for small two dimensional diffusive clusters. On-site electron-electron interactions tend to delocalize the…
Superconducting MgB(2) films with Tc = 38.6 K were prepared using a precursor-deposition, ex-situ post-processing approach. Precursor films of boron, ~0.5 micrometer thick, were deposited onto Al(2)O(3) (102) substrates by e-beam…
For the first time magnetrotransport of the ferromagnetic high-pressure phases of (GaSb)$_2$M (M=Cr,Mn) was measured. It was found that the main component of magnetotransport in these phases is negative and its amplitude is increasing with…
Highly dense nanocrystalline MgB_2 bulk superconductors with distinctly improved pinning were prepared by mechanical alloying of Mg and B powders and hot compaction at ambient temperatures. The nanocrystalline samples reveal high critical…