Single crystals of BaFe$_2$As$_2$ and (Ba$_{0.55}$K$_{0.45}$)Fe$_2$As$_2$ have been grown out of excess Sn with 1% or less incorporation of solvent. The crystals are exceptionally micaceous, are easily exfoliated and can have dimensions as…
Anisotropic superconducting properties including the upper critical field Hc2, thermal activation energy U0, and critical current density Jc are systematically studied in a large Ca1-xLaxFeAs2 single crystal (x ~ 0.18). The obtained Hc2…
Superconductivity of Ca1-xLaxFe2As2 single crystals with various doping level were investigated via electromagnetic measurements for out-plane (H//c) and in-plane (H//ab) directions. Obvious double superconducting transitions, which can…
We report low-temperature specific heat measurements for high-quality single crystalline KFe2As2 (T_c about 3.5 K). The investigated zero-field specific heat data yields an unusually large nominal Sommerfeld coefficient gamma_n of 94(3)…
We present heat capacity measurements of the upper critical fields of single-crystal NdFeAsO1-xFx. In zero-magnetic field a clear step in the heat capacity is observed at Tc = 47K . In fields applied perpendicular to the FeAs-layers the…
The transport properties, upper critical fields, superconducting anisotropy, and critical current density in an iso-valent phosphorus-doped BaFe2As2 single crystal close to optimum doping are investigated in this report. Temperature…
The temperature dependent resistivity of Ba$_{1-x}$K$_x$Fe$_2$As$_2$ (x = 0.23, 0.25, 0.28 and 0.4) single crystals and the angle dependent resistivity of superconducting Ba$_{0.6}$K$_{0.4}$Fe$_2$As$_2$ single crystals were measured in…
The temperature dependence of the upper critical magnetic field (Hc2) in a BaFe1.84Co0.16As2 single crystal was determined via resistivity, for the inter-plane (H^ab) and in-plane (H//ab) directions in pulsed and static magnetic fields of…
We report the results of a systematic investigation of the phase diagram of the iron-based superconductor, Ba1-xKxFe2As2, from x = 0 to x = 1.0 using high resolution neutron and x-ray diffraction and magnetization measurements. The…
We report on the specific heat determination of the anisotropic phase diagram of single crystals of optimally doped SmFeAsO1-xFx. In zero-field, the optimally doped compound displays a clear cusp-like anomaly in C/T with {\Delta}C/Tc = 24…
The pairing symmetry in the iron-based superconductor Ba1-xKxFe2As2 may change from nodeless s-wave near x~0.4 and Tc>30 K, to nodal (either d-wave or s-wave) at x=1 and Tc<4 K. Theoretical interest has been focused on this possibility,…
The upper critical field was measured upto 12 T for three BaFe2-xCoxAs2 single crystals with estimated Co concentrations of x = 0.082, x = 0.117 and x = 0.143. HC2 versus temperature was measured from temperature dependent resistivity, for…
We present specific heat measurements on a series of BaFe2(As1-xPx)2 single crystals with phosphorous doping ranging from x = 0.3 to 0.55. Our results reveal that BaFe2(As1-xPx)2 follows the scaling Delta_C/Tc ~ Tc^2 remarkably well. The…
Using a differential technique, we have measured the specific heats of polycrystalline Ba1-xKxFe2As2 samples with x=0, 0.1 and 0.3, between 2K and 380K and in magnetic fields 0 to 13 Tesla. From this data we have determined the electronic…
Heat capacity and anisotropic thermal expansion was measured for Ba(Fe_{1-x}Co_x)_2As_2 (x = 0, 0.038, 0.074) single crystals. Thermal expansion is anisotropic and, in tetragonal phase, is significantly higher along the c-axis. Previously…
The superconducting phase diagram of MgB2 was determined from magnetization, magneto-transport and the first single-crystal specific heat measurements. A zero-temperature in-plane coherence length of 8 nm is determined. The superconducting…
The specific heat $C(T)$ of BaFe$_2$As$_2$ single crystal, electron-doped Ba$_{0.7}$La$_{0.3}$Fe$_2$As$_2$ and hole-doped Ba$_{0.5}$K$_{0.5}$Fe$_2$As$_2$ polycrystals were measured. For undoped BaFe$_2$As$_2$ single crystal, a very sharp…
The crystal structure, anisotropic electrical resistivity and magnetic susceptibility, as well as specific heat results from single crystals of BaFe2As2, BaNi2As2, and BaFeNiAs2 are surveyed. BaFe2As2 properties demonstrate the equivalence…
Single crystals of Ca1-xLaxFe2As2 for x ranging from 0 to 0.25 have been grown and characterized by structural, transport and magnetic measurements. Coexistence of two superconducting phases is observed, in which the low superconducting…
The low temperature specific heat of annealed single crystal samples of Ba(Fe1-xCox)2As2 with compositions spanning the entire superconducting phase diagram was measured. Effort was made to discover the best annealing schedule to maximize…